Long-term exposure to ultraviolet (UV) light can degrade and discolor bamboo; thus, coatings to protect it from UV exposure are required, especially for outdoor use. Benzotriazole (BTZ) and zinc oxide nanoparticles (NZnO) are organic and inorganic UV absorbers commonly used in UV shielding coatings. This study investigated the photostabilizing efficiency of acrylic-based bamboo exterior coatings using a combination of BTZ and NZnO. Different film formulations covering bamboo substrates were irradiated with artificial UV light for 500 h to accelerate aging. The UV-shielding effect on bamboo beneath various films was determined by CIELAB color space and Fourier transform infrared (FTIR) analysis. The film effectiveness was analyzed by scanning electron microscopy, wettability, UV-vis spectroscopy, and FTIR-attenuated total reflection (ATR) spectroscopy. Films containing BTZ provided higher resistance to photodegradation and more effectively inhibited photodiscoloration of the bamboo substrates than those prepared solely with NZnO. After 500 h of UV irradiation, the BTZ–NZnO film containing 2 wt % BTZ and 1 wt % NZnO showed the best coating performance. Strong synergistic effects were detected in the BTZ–NZnO coatings, particularly for the 2:1 ratio formulation. This study also demonstrated the potential of combining BTZ and NZnO as additives for developing stable, effective UV-shielding bamboo exterior coatings for outdoor applications.

Bamboo scrimber refers to a lignocellulosic structural material, which is usually attacked by water, ultraviolet radiation and fungus. Surface coating is an effective way to protect it, and its coating properties depend on surface wettability. In this study, the surface wettability of bamboo scrimbers with varying resin content was investigated via the comprehensive analysis of surface roughness, surface contact angle, surface free energy, surface chemical composition and coating properties. The resultant scrimbers had a similar profile with low roughness. Their surface was hydrophilic, but the hydrophilicity decreased with the increase in resin content. High resin content gave rise to low total free energy, in which the Lifshitz–van der Waals component was dominant and it decreased with the increasing resin content. Meanwhile, the ratio of the electron-accepting component to the electron-donating component becomes higher. This was due to the decreasing hydrophilic groups (e.g., -OH and -COOH groups) and the increasing oxygen-free groups (e.g., C-H and -CH₂ groups) on the scrimber surface. The resin content affected the adhesion by decreasing the surface wettability, but the coating adhesion still reached the level of 2 for all bamboo scrimbers. The results will provide a theoretical reference for the surface coating of bamboo scrimbers in the structural application for good coating durability.

With natural texture and high performance, bamboo scrimber is one of the artificial lignocellulosic composites widely used in construction, furniture and other structural applications. However, it is vulnerable to the actions of water, ultraviolet radiation and fungus, which affect its durability, especially in the open. Here, bamboo was treated with superheated steam in an attempt to improve the durability of bamboo scrimbers. The chemical composition, mechanical properties, dimensional stability, aging resistance, decay resistance and anti-mildew properties were investigated at different temperatures (160~200 °C). After superheated steam treatment, the relative contents of holocellulose and α-cellulose in bamboo decreased. The bending strength and short-beam shearing strength slightly decreased as the temperature was raised while the modulus was essentially retained. The aging resistance in terms of thickness swelling rate (≤9.38%) was substantially improved. The decay resistance reached to the level of Grade I and can be dramatically enhanced by elevating temperature. The anti-mildew properties were also improved. To take together, superheated steam treatment remarkably improves the resistance of bamboo scrimbers to water, ultraviolet radiation, rot fungi and mildew with some concomitant reduction in mechanical properties. The results will permit outdoor construction using bamboo scrimbers more resistant to environmental damage.

Wood-fiber-mat-reinforced composites (WFMRCs) possess excellent physical and mechanical properties and provide high structural performance, making them a suitable engineering structural material. However, WFMRCs are susceptible to biological attack by fungi and insects when they are used in outdoor environments. In this study, the efficacy of copper triazole (CuAz) preservative treatment in protecting WFMRC against decay by white- and brown-rot fungi (Trametes versicolor and Gloeophyllum trabeum, respectively) was evaluated. Both fungi caused a mass loss in the untreated scrimber of more than 15%, while the CuAz preservative treatment reduced the mass loss to 5%. The measurement results show that CuAz treatment could effectively reduce the degradation rate of three major components of wood; inhibit fungal colonization and degradation; and improve the decay resistance of WFMRC. The atmospheric impregnation of CuAz preservative is more suitable for the material features of WFMRC than vacuum impregnation and can be considered for practical industrial applications. This study provides technical support for the protection and outdoor application of WFMRCs.