High- (and medium-) entropy alloys have emerged as potentially suitable structural materials for nuclear applications, particularly as they appear to show promising irradiation resistance. Recent studies have provided evidence of the presence of local chemical order (LCO) as a salient feature of these complex concentrated solid-solution alloys. However, the influence of such LCO on their irradiation response has remained uncertain thus far. In this work, we combine ion irradiation experiments with large-scale atomistic simulations to reveal that the presence of chemical short-range order, developed as an early stage of LCO, slows down the formation and evolution of point defects in the equiatomic medium-entropy alloy CrCoNi during irradiation. In particular, the irradiation-induced vacancies and interstitials exhibit a smaller difference in their mobility, arising from a stronger effect of LCO in localizing interstitial diffusion. This effect promotes their recombination as the LCO serves to tune the migration energy barriers of these point defects, thereby delaying the initiation of damage. These findings imply that local chemical ordering may provide a variable in the design space to enhance the resistance of multi-principal element alloys to irradiation damage.

Short-range order can be developed in multi-principal element alloys and influences the point defect behavior due to the large variation of the local chemical environment. The effect of short-range order on vacancy and interstitial formation energy and migration behavior was studied in body-centered cubic multi-principal element alloy NbZrTi by first-principles calculations. Two short-range order structures created by density functional theory and Monte Carlo method at 500 and 800 K were compared with the structure of random solid solution. Both vacancy and interstitial formation energies increase with the degree of short-range order. Point defect formation energies tend to be higher in regions enriched in Nb and lower in regions enriched in Zr and Ti. Both vacancies and interstitials prefer to migrate toward Zr,Ti-rich regions and away from Nb-rich regions, suggesting that Zr,Ti-rich regions can potentially act as recombination centers for point defect annihilation. Compared to an ideal random solid solution, the short-range order increases the spatial inhomogeneity of point defect energy landscape. Tuning the degree of short-range order by different processing techniques can be a viable strategy to optimize the point defect behavior to achieve enhanced radiation resistance in multi-principal element alloys.