The paper presents the issue of low-temperature transverse cracks which have developed in newly constructed base courses made of high-modulus asphalt concrete mix (HMAC). Numerous transverse cracks developed in the analysed HMAC base during the winter season before the pavement was actually completed, both at the transverse joint locations and in the areas between them. This had not happened so far on such a scale during road construction projects in Poland. The research included both field examination and laboratory testing of high-modulus asphalt concrete used for construction of the base course of the A1 motorway pavement, followed by computational analysis to investigate the causes and mechanism of the analysed pavement distress. The first part of this paper describes the pavement structure, gives the main requirements applicable to HMAC, and presents the results of the cracking survey, visual assessment and laboratory tests carried out on cores cut from the analysed pavement. Later in the article, the causes of cracking are analysed, taking into account the temperature of air and pavement, performance grade assessment of the bitumen used in the works, homogeneity of the constructed layer and calculated thermal stresses induced in HMAC layers. The examinations and analyses allowed to conclude that the main causes of cracking included too stiff mix, taking into account the climate of Poland, deviations from the pre-defined installation practice during the construction of the base course and leaving the HMAC surface unprotected by the overlying layers: binder and wearing courses during winter. Finally, compliance with the best construction practice during placement of HMAC mixes and use of softer or polymer-modified bitumens are indicated as being critical to avoiding distress of HMAC pavement courses.

Warm mix asphalt (WMA) has been widely accepted as a future asphalt paving technology. Besides clear advantages, there are still some concerns regarding durability and long-term performance of pavements made with this type of asphalt mixtures. One of the most important issues is low temperature behaviour of WMA because certain additives used for temperature reduction can affect bitumen properties. This paper presents the evaluation of low-temperature properties of laboratory-produced asphalt concrete for wearing course with selected WMA additives. One type of bitumen with paving grade 50/70 and five WMA additives of different nature (organic, surface tension reducer and combination of both) were used in this study. The production and compaction temperature of mixtures containing WMA additives was 25 °C lower in comparison with the temperature of the reference mix. To assess the susceptibility of WMA to low-temperature cracking, Semi-Circular Bending (SCB) and Thermal Stress Restrained Specimen Test (TSRST) were used. Supplementary rating was made by analysing Bending Beam Rheometer (BBR) test results of asphalt binders.

Tire/road noise in most driving conditions dominates other sources of traffic noise. One of the most efficient ways of reducing tire/road noise is to use the so-called “low noise pavement”. According to numerous studies, at present, poroelastic road pavement that is composed of rubber and mineral aggregate and polyurethane or bituminous binder gives the best noise reduction up to 12 dB. Unfortunately, there are many problems with making durable poroelastic pavements. This article presents the first results of a project that is executed in Poland and aims at the development of a durable, low noise poroelastic pavement based on polymer-modified asphalt binder called Safe, Eco-friendly POroelastic Road Surface (SEPOR). Two test sections were built in 2019 to test the production technology and performance of the SEPOR pavement. It is observed that some of the problems with previous poroelastic materials were mainly eliminated (especially delamination from the base layer and raveling) but noise reduction is a little less than expected (up to 9 dB). Rolling resistance for car tires is acceptable and fire properties (damping of spill fuel fires, toxic gas emission) are very good.

MATEC Web of Conferences, open access proceedings in Materials science, Engineering and Chemistry

Measures for the improvement of acoustic conditions in the vicinity of roads include the construction of pavement structures with low-noise surfaces with optimal macrotexture and the highest possible sound absorption coefficient. Laboratory evaluation of acoustic properties of a designed asphalt mixture before its placement in the pavement is a good solution. Currently, the most popular method for the determination of the sound absorption coefficient of various construction materials under laboratory conditions is the Kundt’s tube test. Sound absorption coefficient can also be assessed based on field and laboratory measurements performed using a Spectronics ACUPAVE System. Other parameters characterising the acoustic properties of road pavement courses include air void content and water drainability or permeability. The article presents an analysis of results of sound absorption coefficient obtained using a Spectronics ACUPAVE System and water drainability and permeability of poroelastic mixtures obtained both in laboratory and on test sections, in relation to air void content and grading of the mixtures. It was established that poroelastic mixtures containing an aggregate of maximum particle size of 5 mm are characterised by better acoustic properties than mixtures with a maximum aggregate particle size of 8 mm. Changes of crumb rubber aggregate grading and bitumen type (within the tested range of values) as well as the addition of lime have shown no evident influence on the sound absorption coefficient. Noise level values at the speed of 30 km/h according to the CPX method were measured as well. Relationships between sound absorption coefficient, water drainability/permeability, and air void content were determined. The performed analyses confirmed that Spectronics ACUPAVE System may be applied for evaluation of acoustic properties of asphalt mixtures in laboratory conditions, but further research is needed to reduce the uncertainty of the results.