Nanocellulose, being a material with nanodimensions, is characterized by high tensile strength, high modulus of elasticity, low thermal expansion, and relatively low density, as well as exhibiting very good electrical conductivity properties. The paper presents the results of research on cement mortars with the addition of nanocrystals cellulose, applied in three different amounts (0.5%, 1.0%, and 1.5%) by weight of cement, including: physical and mechanical properties, frost resistance and resistance against the detrimental effect of salt, and microstructure examination (SEM). Along with an increase in amount of admixture, the weight loss following frost resistance and salt crystallization tests is reduced. Studies have shown that the addition of nanocrystalline cellulose improves the compressive and flexural strength by 27.6% and 10.9%, respectively. After 50 freezing and thawing (F–T) cycles for the mortars with 1.5% nanocellulose admixture, an improvement in frost resistance by 98% was observed. In turn, the sulfate crystallization tests indicated a 35-fold decrease in weight loss following 1.5% nanopolymer addition to the mortar.

The paper explores the possibility of covering the mortar with the lightweight aggregate by the nanopolymer silane and siloxane as surface hydrophobisation. The investigation involved the mortars with two types of hydrophobic agents diluted with water in a ratio of 1:4 and 1:8. Mortar wetting properties were determined by measuring the absorbability, water vapor diffusion, contact angle (CA) and surface free energy (SFE) of their structure. Surface micro-roughness and 2D topography were evaluated. Scanning electron microscopy (SEM) has shown the microstructure and distribution of pores in mortars. The reduction in absorbency after the first day of testing by 87% was shown. An improvement in frost resistance after 25 cycles by 97% and an 18-fold decrease in weight loss after the sulphate crystallization test were observed. The hydrophobic coating reduces the SFE of mortars and increases the CA. In the case of using silanes, a 9-fold increase CA was observed.

The application of recycled coarse aggregates (RCA) in high-performance concrete (HPC) was analyzed in the article. In the paper, the behavior of HPC with coarse recycled aggregate and natural coarse aggregate (NCA) was compared. Short-term experiments were conducted, including concrete deformation, deflection, load bearing capacity, and cracking of beams. The analysis involved reinforced concrete T-beams made in 100% of RCA or NCA. The studies indicated that the beams with recycled aggregate are characterized by greater deflection and 7.6% lower load bearing capacity in comparison to the beams with NCA. Substitution of coarse natural aggregate with RCA reduced the compressive and tensile strengths by 20 and 26 (%), whereas and the modulus of elasticity was decreased by 15%.

The paper presents the experimental studies on the effect of the water containing micro-nano bubbles of various gases on the physico-mechanical properties of lime-cement mortars. In total, 7 types of mortars were prepared: with water containing the micro-nano bubbles of O₂, O₃ or CO₂ as 50% or 100% substitute of ordinary mixing water (tap water) and the reference mortar prepared using tap water. In order to determine the influence of water with micro-nano bubbles of gases, the consistency of fresh mortar and the physical properties of hardened mortar, i.e., specific and apparent density, total porosity, water absorption by weight and capillary absorption, were established. The mechanical strength of the considered mortars was studied as well by conducting the tests for flexural and compressive strengths following 14, 28 and 56 days. Reduced workability and capillary absorption were observed in the modified mortars within the range of 0.9–8.5%. The mortars indicated an increase in the flexural strength after 28 days ranging from 3.4% to 23.5% and improved compressive strength in 1.2–31%, in comparison to the reference mortar. The conducted studies indicated increased flexural and compressive strengths along with the share of micro-nano bubbles of gases in the mixing water.

In this study, the possibility of using mixing water containing O₂ and O₃ micro-nano bubbles (M-NBs) in concrete technology was investigated. In particular, the effect of micro-nano bubbles on the durability and frost resistance of concrete was analyzed. Concretes with two types of micro-nano bubbles were studied. The physical properties of both the modified concretes and the reference concrete were determined, i.e., specific and apparent density, porosity, weight absorption and coefficient of water absorption. Mechanical parameters based on compressive and flexural strength were tested after 14 and 28 days of curing. Concrete durability was determined on the basis of frost resistance and resistance to salt crystallization. The pore distribution in the cement matrix was determined based on porosimetry studies. The use of water with micro-nano bubbles of O₂ and O₃, among others, contributed to a reduction in the water absorption coefficient from 42.7% to 52.3%, in comparison to the reference concrete. The strength characterizing the concrete with O₃ increased by 61% after 28 days, and the frost resistance after 150 F-T cycles increased by 2.4 times. Resistance to salt crystallization improved by 11% when water with O₃ was used.