Due to the increasing use of polypropylene-based nonwoven dust masks and air filters, environmental problems that occur due to the plastic pollution resulting from the disposal of these materials have also increased. Hence, an eco-friendly air filter based on PVA nanofibers (NFs) was fabricated by electrospinning on a nonwoven fabric, and its performance was evaluated as a filter capable of blocking or capturing particulate matter. The quality factor of the optimized PVA NF-based air filter was found to be 0.010606 Pa⁻¹, which is lower than that of a HEPA filter (0.015394 Pa⁻¹), but higher than that of a cabin air filter (0.010517 Pa⁻¹) and a dust mask (0.009102 Pa⁻¹). The contamination level of the PVA NF-based filter was analyzed by optical and structural analyses of the filter surface. Finally, the filter was soaked in water to selectively remove the contaminated PVA NF layer, and the remaining nonwoven fabric was able to be reused to make the filter.

In this study, cobalt diselenide (CoSe2) and the composites (CoSe2@RGO) of CoSe2 and reduced graphene oxide (RGO) were synthesized by a facile hydrothermal reaction using cobalt ions and selenide source with or without graphene oxide (GO). The formation of CoSe2@RGO composites was identified by analysis with X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and scanning electron microscopy (SEM). Electrochemical analyses demonstrated that the CoSe2@RGO composites have excellent catalytic activity for the reduction of I3−, possibly indicating a synergetic effect of CoSe2 and RGO. As a consequence, the CoSe2@RGO composites were applied as a counter electrode in DSSC for the reduction of redox couple electrolyte, and exhibiting the comparable power conversion efficiency (7.01%) to the rare metal platinum (Pt) based photovoltaic device (6.77%).

In the photovoltaic industry, there is great interest in increasing the power output of solar cells to achieve grid parity and to promote the widespread use of solar cells. However, despite many developments, a phenomenon called light-induced degradation causes the efficiency of solar cells to deteriorate over time. This study proposes a treatment that can be applied to cells within solar modules. It uses a half-bridge resonance circuit to induce a magnetic field and selectively heat Al electrodes in the solar cells. The electrical state of a solar module was measured in real time as it was being heated, and the results were combined with a kinetics simulation using a cyclic reaction. As the temperature of the solar module increased, the time taken to reach the saturation point and the recovery time decreased. Moreover, the value of the saturation point increased. The light-induced degradation activation energy was similar to results in the existing literature, suggesting that the kinetic model was valid and applicable even when 72 cells were connected in series. This demonstrates that an entire solar module can be treated when the cells are connected in series, and in future multiple modules, could be connected in series during treatment.

Modern energy needs and the pressing issue of environmental sustainability have driven many research groups to focus on energy-generation devices made from novel nanomaterials. We have prepared platinum nanoparticle-decorated silicon nanowire/carbon core–shell nanomaterials (SiNW/C@Pt). The processing steps are relatively simple, including wet chemical etching to form the silicon nanowires (SiNWs), chemical vapor deposition to form the carbon shell, and drop-casting and thermal treatment to embed platinum nanoparticles (Pt NPs). This nanomaterial was then tested as the counter electrode (CE) in dye-sensitized solar cells (DSSCs). SiNW/C@Pt shows potential as a good electrocatalyst based on material characterization data from Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). Raman spectroscopy shows that the surface reactivity of the SiNW/C is increased by the decoration of Pt NPs. These data also show that the carbon shell included both graphitic (sp ${}^2$ hybridization) and defective (sp ${}^3$ hybridization) phases of carbon. We achieved the minimum charge-transfer resistance of 0.025 $\Omega$ · cm ${}^2$ and the maximum efficiency of 9.46% with a symmetric dummy cell and DSSC device fabricated from the SiNW/C@Pt CEs, respectively.

This study presents an inkjet-printed, single-step double layer electrode with an acrylate adhesion layer on PES to enhance Ag adhesion. The electrode offers strong mechanical stability and a simplified solution for flexible device applications.

As the importance of the levelized cost of electricity (LCOE) increases in the solar cell industry, the demand for high-efficiency solar cells is rapidly increasing. Typically, p-type passivated emitter rear contact (PERC) solar cells are the most commonly used in the industry, and their efficiency is approximately 22–23%. P-type solar cells are reported to exhibit a light-induced degradation (LID) phenomenon, in which their output constantly decreases during power generation under solar radiation, and the output significantly reduces as their reference efficiency increases. Ultra-high-efficiency solar cells, which are on high demand, have a considerable output reduction due to the LID phenomenon; hence, technologies to prevent the LID phenomenon are required. However, research on this phenomenon has not been conducted because there is no method to transfer heat to solar cells inside the encapsulant when the modules are produced. In this study, a regeneration state was formed by remotely heating solar cells without damaging the encapsulant of the solar cell module. This was accomplished by using a heating method based on an induction magnetic field. A half-bridge resonance circuit was used to apply the induction magnetic field, and the temperature of the solar cell was controlled by adjusting the magnitude of the current flowing through the coil. To determine whether only the solar cell was heated, the temperature distribution inside the module was analyzed using an IR camera. The minority carrier lifetime was examined by real-time observation of the open-circuit voltage pattern of the solar cell. Finally, the observed real-time open-circuit voltage data were used, and dynamic simulation of the regeneration process was applied to analyze the LID activation energy generated in the regeneration process of the solar cell module. In conclusion, research was conducted on applying the regeneration state to prevent the LID phenomenon in the solar-cell-module stage, and the LID activation energy of the solar cell module was extracted. Based on this, a nondestructive degradation prevention technology for the solar cell module was developed.