Due to the increasing use of polypropylene-based nonwoven dust masks and air filters, environmental problems that occur due to the plastic pollution resulting from the disposal of these materials have also increased. Hence, an eco-friendly air filter based on PVA nanofibers (NFs) was fabricated by electrospinning on a nonwoven fabric, and its performance was evaluated as a filter capable of blocking or capturing particulate matter. The quality factor of the optimized PVA NF-based air filter was found to be 0.010606 Pa⁻¹, which is lower than that of a HEPA filter (0.015394 Pa⁻¹), but higher than that of a cabin air filter (0.010517 Pa⁻¹) and a dust mask (0.009102 Pa⁻¹). The contamination level of the PVA NF-based filter was analyzed by optical and structural analyses of the filter surface. Finally, the filter was soaked in water to selectively remove the contaminated PVA NF layer, and the remaining nonwoven fabric was able to be reused to make the filter.

To develop high-performance de- or anti-frosting/icing devices based on transparent heaters, it is necessary to study the evaporation-rate control of droplets on heater surfaces. However, almost no research has been done on the evaporation-rate control of liquid droplets on transparent heaters. In this study, we investigate the evaporation characteristics of water droplets on transparent heater surfaces and determine that they depend upon the surface wettability, by modifying which, the complete evaporation time can be controlled. In addition, we study the defrosting and deicing performances through the surface wettability, by placing the flexible transparent heater on a webcam. The obtained results can be used as fundamental data for the transparent defrosting and deicing systems of closed-circuit television (CCTV) camera lenses, smart windows, vehicle backup cameras, aircraft windows, and sensor applications.

Modern energy needs and the pressing issue of environmental sustainability have driven many research groups to focus on energy-generation devices made from novel nanomaterials. We have prepared platinum nanoparticle-decorated silicon nanowire/carbon core–shell nanomaterials (SiNW/C@Pt). The processing steps are relatively simple, including wet chemical etching to form the silicon nanowires (SiNWs), chemical vapor deposition to form the carbon shell, and drop-casting and thermal treatment to embed platinum nanoparticles (Pt NPs). This nanomaterial was then tested as the counter electrode (CE) in dye-sensitized solar cells (DSSCs). SiNW/C@Pt shows potential as a good electrocatalyst based on material characterization data from Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). Raman spectroscopy shows that the surface reactivity of the SiNW/C is increased by the decoration of Pt NPs. These data also show that the carbon shell included both graphitic (sp ${}^2$ hybridization) and defective (sp ${}^3$ hybridization) phases of carbon. We achieved the minimum charge-transfer resistance of 0.025 $\Omega$ · cm ${}^2$ and the maximum efficiency of 9.46% with a symmetric dummy cell and DSSC device fabricated from the SiNW/C@Pt CEs, respectively.

Digital printing technologies—including inkjet printing, aerosol jet printing, and electrohydrodynamic jet printing—have emerged as promising strategies for next-generation electronic devices. However, the weak adhesion between printed electrodes and substrates can lead to electrode delamination, thereby compromising device reliability and lifetime. In this study, a dielectric interlayer was introduced to improve the adhesion of silver (Ag) mesh electrodes on glass, polyethersulfone film, and polyimide film substrates. The optimized electrode on PES film achieved an optical transmittance of 83% at 550 nm and line resistance of 0.3 Ω, confirming its suitability as a transparent electrode. The incorporation of the interlayer also enhanced the adhesion and mechanical flexibility across all substrates. Moreover, the printed electrodes exhibited uniform surface heating under an applied bias (≤DC 3 V), and their feasibility as low-power flexible transparent heaters was experimentally demonstrated. These findings present a simple and effective printing strategy for fabricating robust and multifunctional electrodes, offering enormous potential for the realization of future flexible and transparent electronic systems.

We used capacitance–voltage (C–V), conductance–voltage (G–V), and noise measurements to examine the carrier trap mechanisms at the surface/core of an AlGaN/GaN nanowire wrap-gate transistor (WGT). When the frequency is increased, the predicted surface trap density promptly drops, with values ranging from 9.1 × 10¹³ eV⁻¹∙cm⁻² at 1 kHz to 1.2 × 10¹¹ eV⁻¹∙cm⁻² at 1 MHz. The power spectral density exhibits 1/f-noise behavior in the barrier accumulation area and rises with gate bias, according to the 1/f-noise features. At lower frequencies, the device exhibits 1/f-noise behavior, while beyond 1 kHz, it exhibits 1/f²-noise behavior. Additionally, when the fabricated device governs in the deep-subthreshold regime, the cutoff frequency for the 1/f²-noise features moves to the subordinated frequency (~10² Hz) side.

Graphene oxide (GO) is one of the interesting ink materials owing to its fascinating properties, such as high dissolubility in water and high controllable electric properties. For versatile printing application, the viscosity of GO colloids should be controlled in order to meet the specific process requirements. Here, we report on the relatively rapid fabrication of viscosity-increased GO (VIGO) colloids mixed with electrophoretically deposited GO sheets (EPD-GO). As the GO colloid concentration, applied voltage, and deposition time increase, the viscosity of the GO colloids becomes high. The reason for the improved viscosity of GO colloids is because EPD-GO has parallel stacked GO sheets. The GO and VIGO colloids are compared and characterized using various chemical and structural analyzers. Consequently, our simple and fast method for the fabrication of GO colloids with enhanced viscosity can be used for producing inks for flexible and printed electronics.