With the premise of investigating mechanical properties, the thermal conductivity of autoclaved aerated concrete (AAC) is a key index of self-insulation block walls for building energy conservation. This study focused on the effect of pore structures on the mechanical performance and thermal conductivity of AAC with the comparison of AAC base materials. Different kinds of AAC and their base materials were prepared and experimentally investigated. While maintaining a consistent mix proportion of the AAC base material, the pore structure of AAC was changed by the dosage of aluminum power/paste, foam stabilizer, and varying the stirring time of aluminum paste. The steam curing systems of AAC and the base material were determined based on SEM (Scanning Electronic Microscopy) and XRD (X-ray Diffraction) tests. With almost the same apparent density, the pore size decreased with the increasing content of foam stabilizer, and the mixing time of aluminum paste and foam stabilizer has a great influence on pore size. The thermal conductivity test and compressive test results indicated that that pore size had an effect on the thermal conductivity, but it had little effect on the compressive strength, and the thermal conductivity of sand aeration AAC was 8.3% higher than that of fly ash aeration AAC; the compressive strength was 10.4% higher, too. With almost the same apparent density, the regression mathematical model indicates that the thermal conductivity of AAC increased gradually with the increase of pore size, but it had little effect on the compressive strength. From the test results of basic mechanical properties, the mechanical model of cubic compressive strength, elastic modulus, axial compressive strength, and splitting tensile strength was obtained. The proposed stress–strain relationship model could well describe the relationship of AAC and the base material at the rising section of the curve.

With the premise of ensuring workability on a fresh mixture, the volume stability of hardened self-compacting steel fiber reinforced concrete (SFRC) becomes an issue due to the content of cementitious materials increased with the volume fraction of steel fiber. By using the expansive agent to reduce the shrinkage deformation of self-compacting SFRC, the strength reduction of hardened self-compacting SFRC is another issue. To solve these issues, this paper performed an experimental investigation on the workability, shrinkage, and mechanical properties of self-compacting SFRC compared to the self-compacting concrete (SCC) with or without an expansive agent. The calcium-sulfoaluminate expansive agent with content optimized to be 10% mass of binders and the steel fiber with a varying volume fraction from 0.4% to 1.2% were selected as the main parameters. The mix proportion of self-compacting SFRC with expansive agent was designed by the direct absolute volume method, of which the steel fibers are considered to be the distributed coarse aggregates. Results showed that rational high filling and passing ability of fresh self-compacting SFRC was ensured by increasing the binder to coarse-aggregate ratio and the sand ratio in the mix proportions; the autogenous and drying shrinkages of hardened self-compacting SFRC reduced by 22.2% to 3.2% and by 18.5% to 7.3% compared to those of the SCC without expansive agent at a curing age of 180 d, although the expansion effect of expansive agent decreased with the increasing volume fraction of steel fiber; the mechanical properties, including the compressive strength, the splitting tensile strength, and the modulus of elasticity increased with the incorporation of an expansive agent and steel fibers, which met the design requirements.

This paper performed a detailed study on the fundamental properties and thermal conductivity of autoclaved aerated concrete (AAC) self-insulation block, and the mechanical properties and heat transfer resistance of the AAC self-insulation block masonry. Different kinds of joints and the plastering surface were used to build the masonry specimens. The distinctive feature of the blocks and mortars is the lower thermal conductivity with expected strength. Compared to those with larger thickness of insulation mortar joints, the masonry with thin-layer mortar joints had better compressive performance and lower shear strength. The compressive strength of masonry was related with the block and mortar strengths, the shear strength of masonry along mortar joints was related with the mortar strength. The stress–strain relationship of masonry in compression could be predicted by the similar expression of conventional block masonry. The tested heat transfer coefficient of AAC self-insulation block masonry with thickness of 250 mm without plastering surfaces was (0.558 ± 0.003) W/(m²·K). With the plastering surfaces, the heat transfer coefficient reduced by 4.4% to 8.9%. Good agreements in values of heat transfer coefficient existed by using the test, theoretical computation and ANSYS (ANSYS Inc. Canonsburg, PA, USA) analytical methods. Based on the extensibility analyses, the heat transfer coefficients of AAC self-insultation block masonry with different thickness are proposed. The best thickness is proposed for the outer walls of residential buildings in different cold zone to meet the design requirement of energy conservation.

Producing concrete with large content of fly ash attracts increasing attention in low carbon building materials. In this paper, the fly-ash concrete (FAC) with a content of fly ash no less than 50% total weight of binders was developed. The adaptability of fly ash used for concrete was firstly examined by testing the water requirement of normal consistency and the setting time for cement fly-ash paste, and the strengths of cement fly-ash mortar at the curing age of 7 and 28 days. The factors of water-to-binder ratio from 0.3 to 0.5, the content of fly-ash from 40% to 80%, and the excitation measures with additional Ca(OH)₂ and steam curing at initial were considered. After that, the FAC was designed by adding an excessive content of fly ash to reduce the water-to-binder ratio from 0.50 to 0.26, and the content of fly-ash varied from 52% to 60%. Results show that the cement fly-ash paste presented a reduction of water requirement and an elongation of setting time with the increased content of fly ash. This provides a foundation of maintaining the workability of fresh FAC with a decreased water-to-binder ratio by adding the excessive content of fly ash. The cement fly-ash mortar had a lower early strength due to the slow reaction of fly-ash with Ca(OH)₂, which could be improved by steam curing at the initial 24 h due to the excitation of fly-ash activity. At curing age of 28 days, the FAC had the expected axial compressive strength and modulus of elasticity, but the tensile strength was lower than predicted. At the curing age of 56 days, all the basic mechanical properties of FAC reached the prediction. The resistances of FAC to chloride ion penetration and carbonization were realized at a very high level as specified in codes.