This paper studies the effect of high-strength steel fiber reinforced concrete (SFRC) on the axial compression behavior of rectangular-sectional SFRC-filled steel tube columns. The purpose is to improve the integrated bearing capacity of these composite columns. Nine rectangular-sectional SFRC-filled steel tube columns and one normal concrete-filled steel tube column were designed and tested under axial loading to failure. The compressive strength of concrete, the volume fraction of steel fiber, the type of internal longitudinal stiffener and the spacing of circular holes in perfobond rib were considered as the main parameters. The failure modes, axial load-deformation curves, energy dissipation capacity, axial bearing capacity, and ductility index are presented. The results identified that steel fiber delayed the local buckling of steel tube and increased the ductility and energy dissipation capacity of the columns when the volume fraction of steel fiber was not less than 0.8%. The longitudinal internal stiffening ribs and their type changed the failure modes of the local buckling of steel tube, and perfobond ribs increased the ductility and energy dissipation capacity to some degree. The compressive strength of SFRC failed to change the failure modes, but had a significant impact on the energy dissipation capacity, bearing capacity, and ductility. The predictive formulas for the bearing capacity and ductility index of rectangular-sectional SFRC-filled steel tube columns are proposed to be used in engineering practice.

A scientific and concise mix design method is an impending problem in the engineering application of self-compacting steel-fiber-reinforced concrete (SFRC). This paper focuses on the mix proportion of self-compacting SFRC, which is influenced by the steel fibers, along with its effects on the packing properties of the steel fiber aggregate skeleton. In total, 252 groups of packing tests were carried out for several main factors, including with various maximum particle sizes for the coarse aggregates, manufactured sand ratios ranging from 50% to 62%, and with different types of hooked-end steel fibers and crimped steel fibers, with volume fractions ranging from 0% to 2.0%. The results indicated that the void content and rational sand ratio of the steel fiber aggregate skeleton increased linearly with the fiber factor. These results provided a basis for the calculation of the binder content and rational sand ratio of the self-compacting SFRC. Combined with the absolute volume design method and the calculation formula for the water-to-binder ratio, a systematical procedure was proposed for the mix proportion design of the self-compacting SFRC. Based on the design method, eight groups of mixtures were cast and tested to verify the adaptability and practicability of the workability, air content, density, cubic compressive strength, and splitting tensile strength of the self-compacting SFRC. Meanwhile, the outcomes of this study confirmed the applicability of using manufactured sand as a complete replacement for natural sand for the self-compacting SFRC.

The optimization of mix proportions based on the targeted fresh and hardened performances of self-compacting concrete (SCC) is a foundation for its transition from laboratory research to industrial production. In this paper, the mix proportions of various SCC mixtures were designed by the absolute volume method with changes in the content of river sand and manufactured sand, the content of fly ash and granulated ground blast furnace slag (GGBS) and the maximum particle sizes of coarse aggregates. This experimental study was carried out to verify the workability, density and cubic compressive strength of SCC. The results show that SCC demonstrated good performance with appropriate mix proportions of manufactured sand and river sand. A hybrid effect of fly ash and GGBS appeared on the fresh performance of SCC with a constant strength, and the coarse aggregate with a smaller maximum particle size was beneficial to the workability but detrimental to the compressive strength of SCC. Finally, the optimization of the mix proportion of SCC was evaluated by grey relational analysis, in which the weight of the indicators was determined by the entropy method to improve the evaluation credibility. As a result, the optimal mix proportions of SCC were selected.

Durability of concrete is of great significance to prolong the service life of concrete structures in corrosive environments. Aiming at the economical and environment-friendly production of concrete by comprehensive utilization of the supplementary cementitious materials made of industrial byproducts, the resistances to chloride penetration, sulfate attack, and frost of high-performance concrete were studied in this paper. Fifteen concretes were designed at different water–binder ratio with the changes of contents of fly ash (FA), silica fume (SF), ground granulated blast-furnace slag (GGBS), and admixture of sulfate corrosion-resistance (AS). The compressive strength, the total electric flux of chloride penetrability, the sulfate resistance coefficient, and the indices of freezing and thawing were measured. Results indicate that, depending on the chemical composition, fineness, and pozzolanic activity, the supplementary cementitious admixtures had different effects on the compressive strength and the durability of concrete; despite having a higher fineness and pozzolanic activity, the GGBS gave out a negative effect on concrete due to a similar chemical composition with cement; the SF and FA presented beneficial effects on concrete whether they were used singly with GGBS or jointly with GGBS; the AS improved the compressive strength and the sulfate corrosion resistance of concrete. In general, the grade of durability was positively related to the compressive strength of concrete. Except for the concretes admixed only with GGBS or with GGBS and FA, others had super durability with the compressive strength varying from 70 MPa to 113 MPa. The concretes with water to binder ratio of 0.29 and total binders of 500 kg/m³ admixed with 7% FA + 8% SF + 8% GGBS or 7% FA + 8% SF + 8% GGBS + (10~12)% AS presented the highest grades of resistances specified in China codes to chloride penetration, sulfate corrosion, and frost, while the compressive strength was about 100 MPa.