Clay-based nanostructures were prepared from kaolinites of varying structural order by two different methods. In the first method the kaolinite-urea precursor, obtained by dry grinding, was intercalated further with triethanolamine and the tetraalkylammonium salt was synthesized in the interlamellar space. Exfoliation was achieved by the use of sodium polyacrylate (PAS). In the second method, the kaolinite-potassium acetate (kaolinite-KAc) precursor, obtained via two different methods, was intercalated further with ethylene glycol (EG) and then n-hexylamine (HA). Intercalation with EG was also achieved by heating either directly or with microwaves. The morphology that results depends on the method of precursor preparation, the method of heat treatment and the degree of structural order of the original clay. Higher structural order facilitates the formation of a tubular morphology, while mechanical treatment and microwave agitation may result in broken tubes. Molecular mechanical (MM) calculations showed that organo-complexes may be exfoliated to a d value of 10–11 Å.

The purpose of this work was to develop, characterize and test new low-cost materials suitable for removing methylene blue dye from water and wastewater by adsorption. The solid materials consisted of silica gel powder (SG), silica gel mixed with eggshell powder (SG-ES) and a mixture of silica gel with sand from the western Iraqi desert (SG-SI). The samples were milled by using an electrical mixer and a ball mill, followed by a drying step. In addition, desert sand was acid-treated in order to remove impurities. The structure and chemical composition of the samples were investigated by X-ray diffraction (XRD), a scanning electron microscopy technique equipped with an energy-dispersive X-ray spectrometer (SEM-EDX), a low-temperature nitrogen adsorption (BET) technique, thermo-analytical (TG/TGA) measurements and Fourier-transformed infrared spectroscopy (FTIR). The previously mentioned materials were tested to remove methylene blue from an aqueous solution. The adsorption experiments were monitored by ultraviolet–visible (UV-Vis) spectrophotometry and showed that SG and SG-ES gave promising results for the methylene blue removal from water. After 40 min of treatment of the aqueous solution containing 10 mg/L of MB at room temperature, the tested SG, SG-ES and SG-SI materials were found to have 86%, 80% and 57% dye adsorption efficiency, respectively. Taking into consideration not only the adsorption activity of the studied material but their availability, cost and concepts of cleaner production and waste minimization, the developed silica gel with eggshell can be considered as a good, cost-effective alternative to commercially available activated-carbon-based adsorbents. Different kinetic and isotherm models were fitted to the experimental results. A pseudo-second-kinetics-order model revealed high correlation fitting, while the Freundlich model was found to appropriately describe the adsorption isotherm. The thermal stability during the possible regeneration process of the SG-ES adsorbent mixture and its interaction mechanism with cationic dye was discussed.

In this paper, the application of multiwalled carbon nanotubes (MWCNTs) based on metal oxide nanocomposites as adsorbents for the removal of hydrocarbons such as kerosene from water was investigated. Functionalized MWCNTs were obtained by chemical oxidation using concentrated sulfuric and nitric acids. V₂O₅, CeO_2, and V₂O₅:CeO₂ nanocomposites were prepared using the hydrothermal method followed by deposition of these oxides over MWCNTs. Individual and mixed metal oxides, fresh MWCNTs, and metal oxide nanoparticle-doped MWCNTs using different analysis techniques were characterized. XRD, TEM, SEM, EDX, AFM, Raman, TG/DTA, and BET techniques were used to determine the structure as well as chemical and morphological properties of the newly prepared adsorbents. Fresh MWCNTs, Ce/MWCNTs, V/MWCNTs, and V:Ce/MWCNTs were applied for the removal of kerosene from a model solution of water. GC analysis indicated that high kerosene removal efficiency (85%) and adsorption capacity (4270 mg/g) after 60 min of treatment were obtained over V:Ce/MWCNTs in comparison with fresh MWCNTs, Ce/MWCNTs and V/MWCNTs. The kinetic data were analyzed using the pseudo-first order, pseudo-second order, and intra-particle diffusion rate equations.