The Achilles heel of thermoplastic natural fibre composites is their limited durability. The environmental degradation of the mechanical properties of hemp and hemp/basalt hybrid-reinforced high-density polyethylene (HDPE) composites has been investigated with a special focus on the effects of water ageing and accelerated ageing, including hygrothermal and UV radiation. Modification of the matrix was carried out using a maleic anhydride high-density polyethylene copolymer (MAPE) as a compatibilizer. Hybridization of hemp fibres with basalt fibres and the incorporation of MAPE were found to significantly decrease the water uptake (up to 75%) and increase the retention of mechanical properties after accelerated ageing. Secondary crystallization phenomena occurring in the composites, as confirmed by differential scanning calorimetry (DSC) analysis, were able to counteract the severe combined effects of hygrothermal stress and UV radiation, with the exception of hemp-fibre composites where permanent damage to the fibres occurred, with 2% and 20% reduction in tensile strength and modulus, respectively, for a 30 wt % hemp fibre-reinforced HDPE.

The present work investigates the effects of an environmentally friendly treatment based on supercritical carbon dioxide (scCO₂) on the interfacial adhesion of flax fibers with thermoset matrices. In particular, the influence of this green treatment on the mechanical (by single yarn tensile test), thermal (by TGA), and chemical (by FT-IR) properties of commercially available flax yarns was preliminary addressed. Results showed that scCO₂ can significantly modify the biochemical composition of flax fibers, by selectively removing lignin and hemicellulose, without altering their thermal stability and, most importantly, their mechanical properties. Single yarn fragmentation test results highlighted an increased interfacial adhesion after scCO₂ treatment, especially for the vinylester matrix, in terms of reduced debonding and critical fragment length values compared to the untreated yarns by 18.9% and 15.1%, respectively. The treatment was less effective for epoxy matrix, for which debonding and critical fragment length values were reduced to a lesser extent, by 3.4% and 3.7%, respectively.

Hierarchical functionalization of flax fibers with ZnO nanostructures was achieved by electroless deposition to improve the interfacial adhesion between the natural fibers and synthetic matrix in composite materials. The structural, morphological, thermal and wetting properties of the pristine and ZnO-coated flax fibers were investigated. Thus, the ZnO-coated flax fabric discloses an apparent contact angle of ~140° immediately after the placement of a water droplet on its surface. An assessment of the interfacial adhesion at the yarn scale was also carried out on the flax yarns coated with ZnO nanostructures. Thus, after the ZnO functionalization process, no significant degradation of the tensile properties of the flax yarns occurs. Furthermore, the single yarn fragmentation tests revealed a notable increase in the interfacial adhesion with an epoxy matrix, reductions of 36% and 9% in debonding and critical length values being measured compared to those of the pristine flax yarns, respectively. The analysis of the fracture morphology by scanning electron microscopy and X-ray microtomography highlighted the positive role of ZnO nanostructures in restraining debonding phenomena at the flax fibers/epoxy resin matrix interphase.

The aim of this study was to assess the effects of commercially available and relatively inexpensive enzyme preparations based on endo 1,4-β-xylanase, pectinase and xyloglucanase on the thermal (TGA), morphological (SEM), chemical (FT-IR) and mechanical (single yarn tensile tests) properties of flax yarns. The preparation based on pectinase and xyloglucanase provided the best results, resulting in the effective removal of hydrophilic components such as hemicellulose and pectin, the individualization of yarns and increased thermal stability at the expense of a reduction in mechanical properties, depending on the treatment parameters. Single yarn fragmentation tests pointed out an improved interfacial adhesion after enzymatic treatment, with reduced debonding length values of 18% for an epoxy matrix and up to 36% for a vinylester resin compared to untreated flax yarns.