Micro/nano-precision glass molding (MNPGM) is an efficient approach for manufacturing micro/nanostructured glass components with intricate geometry and a high-quality optical finish. In MNPGM, the mold, which directly imprints the desired pattern on the glass substrate, is a key component. To date, a wide variety of mold inserts have been utilized in MNPGM. The aim of this article is to review the latest advances in molds for MNPGM and their fabrication methods. Surface finishing is specifically addressed because molded glass is usually intended for optical applications in which the surface roughness should be lower than the wavelength of incident light to avoid scattering loss. The use of molds for a wide range of molding temperatures is also discussed in detail. Finally, a series of tables summarizing the mold fabrication methods, mold patterns and their dimensions, anti-adhesion coatings, molding conditions, molding methods, surface roughness values, glass substrates and their glass transition temperatures, and associated applications are presented. This review is intended as a roadmap for those interested in the glass molding field.

An all glass Fresnel lens (AGFL) was fabricated by glass molding with a vitreous carbon (VC) micro mold. In the glass molding process, a glass plate was heated up to its softening temperature and pressed against to the VC mold to replicate the Fresnel pattern. The VC molds having negative shape Fresnel profile were fabricated by carbonization of replicated Furan precursor using a diamond turning machined nickel master. During the carbonization process, the Furan precursor shrank due to the thermal decomposition, and this shrinkage must be compensated to obtain a precise AGFL. In this study, we examined the shrinkage ratio during the carbonization process using a preliminary experiment using the commercially available PMMA Fresnel lens as the master, and fabricated a nickel master with an enlarged Fresnel profile for shrinkage compensation. To verify the compensation method, the surface profiles of the fabricated VC mold and molded AGFL were measured and compared with the designed profile. The deviations between measured and designed profiles were less than 4 μm. In addition, the tip radii of the grooves and draft angle of the molded AGFL were within the acceptable tolerance for CPV applications.

A glass microfluidic device with superior chemical and mechanical resistance was fabricated using a cost-effective glass molding process with a vitreous carbon (VC) mold, which was prepared by the carbonization of a replicated polymer precursor. For the development of microfluidic chips with dense microchannels on a large footprint, a defect-free VC mold is essential. In this study, a furan imprinting process, in which a patterned furan layer was imprinted (cured) on a polished furan plate, was established to minimize warpage and gas bubble defects. In addition, the proposed imprinting process markedly reduced the fabrication time of the furan precursor. For feasibility testing, a glass micromixer with a total channel length of 30.6 cm and footprint of 20 × 20 mm ² was developed by glass molding with the VC mold and thermal fusion bonding. The fabricated glass-molded micromixer was durable at an internal pressure of ~24 MPa, and there was no swelling when used with toluene for an extended time.

An all-glass bifurcation microfluidic chip for blood plasma separation was fabricated by a cost-effective glass molding process using an amorphous carbon (AC) mold, which in turn was fabricated by the carbonization of a replicated furan precursor. To compensate for the shrinkage during AC mold fabrication, an enlarged photoresist pattern master was designed, and an AC mold with a dimensional error of 2.9% was achieved; the dimensional error of the master pattern was 1.6%. In the glass molding process, a glass microchannel plate with negligible shape errors (~1.5%) compared to AC mold was replicated. Finally, an all-glass bifurcation microfluidic chip was realized by micro drilling and thermal fusion bonding processes. A separation efficiency of 74% was obtained using the fabricated all-glass bifurcation microfluidic chip.

Although polymer nanoimprinting on glass substrates has been widely employed for the fabrication of functional anti-reflective (AR) nanostructures, several drawbacks exist with respect to durability and delamination. The direct patterning of glass material is a potential solution for outdoor applications that require AR functional nanostructured glass plates. In this study, a glass imprinting technique was employed for the fabrication of an AR nanostructure on a soda-lime glass substrate using a vitreous carbon (VC) stamp. The VC stamp, which had a high aspect ratio nanopost array with a pitch of 325 nm, diameter of 110 nm, and height of ~220 nm, was fabricated by the carbonization of a replicated Furan precursor from an Si master. During the glass imprinting process using the nanopost array VC stamp, the softened glass material gradually protruded into the spaces between the nanopins owing to viscoelastic behavior, and one can achieve a cross-sinusoidal surface relief under specific imprinting condition, which can be used as an AR nanostructure with a gradually increasing refractive index. The effects of the processing temperature on the surface profile of the glass imprinted parts and the measured transmission spectra were analyzed, and a glass imprinting temperature of 700 °C and pressure of 1 MPa were found to be the optimum condition. The height of the fabricated cross-sinusoidal nanostructure was 80 nm, and the light transmission was increased by ~2% over the entire visible-light range. Furthermore, the measured transmission spectrum observed to be in good agreement with the simulation results.

This study reports a cost-effective method of replicating glass microfluidic chips using a vitreous carbon (VC) stamp. A glass replica with the required microfluidic microstructures was synthesized without etching. The replication method uses a VC stamp fabricated by combining thermal replication using a furan-based, thermally-curable polymer with carbonization. To test the feasibility of this method, a flow focusing droplet generator with flow-focusing and channel widths of 50 µm and 100 µm, respectively, was successfully fabricated in a soda-lime glass substrate. Deviation between the geometries of the initial shape and the vitreous carbon mold occurred because of shrinkage during the carbonization process, however this effect could be predicted and compensated for. Finally, the monodispersity of the droplets generated by the fabricated microfluidic device was evaluated.