In high entropy alloys (HEAs), the addition of large-size atoms results in lattice distortion and further leads to solid solution strengthening or precipitation strengthening. However, the relationship between atomic radius, solid solution strengthening and precipitation strengthening has not been discerned yet. In this work, CoCrFeNiX_0.4 (X = Al, Nb, Ta, with an equi-atomic radius) HEAs were prepared by powder plasma arc additive manufacturing (PPA-AM) and evaluated for their mechanical properties. Compression and nano-indentation hardness tests showed that the HEA with Ta showed the best properties. The influence of atomic radius and solid solubility on solid solution strengthening was investigated and the main strengthening mechanism that determines the mechanical properties of the developed HEAs was analyzed. The results showed that (i) the CoCrFeNiAl_0.4 alloy did not show any solid solution strengthening effect and that a clear relation between solid solution strengthening and atomic size was not observed; (ii) in both CoCrFeNiTa_0.4 and CoCrFeNiNb_0.4 HEAs, precipitation strengthening and grain boundary strengthening effects are observed, wherein the difference in mechanical properties between both the alloys can be mainly attributed to the formation of fine eutectic structure in CoCrFeNiTa_0.4; and (iii) from the microstructural analyses, it was identified that, in the CoCrFeNiTa_0.4 HEA, the location containing a fine eutectic structure is accompanied by the formation of low-angle grain boundaries (LAGBs), which is also the region where deformed grains gather, giving rise to improved mechanical strengthening.

The current study focusses on the phase composition, solidification path, and microstructure evaluation of gravity cast Al-4Mg-0.5Si-xLa aluminum alloy, where x = 0, 0.1, 0.25, 0.5, 0.75, and 1 wt.% La. A computational CalPhaD approach implemented in Thermo-Calc software and scanning electron microscopy technique equipped with electron microprobe analysis (EMPA) was employed to assess its above-mentioned characteristics. The thermodynamic analysis showed that the equilibrium solidification path of La-containing Al-Mg-Si alloys consists of only binary phases LaSi₂ and Mg₂Si precipitation along with α-Al from the liquid and further solid-state transformation of this mixture into α-Al + Al₁₁La₃ + Mg₂Si + Al₃Mg₂ composition. Scheil–Gulliver simulation showed a similar solidification pathway but was accompanied by an increase in the solidification range (from ~55 °C to 210 °C). Furthermore, microstructural observations were congruent with the calculated fraction of phases at 560 °C and related to α-Al + LaSi₂ + Mg₂Si three-phase region in terms of formation of La-rich phase having both eliminating effect on the eutectic Mg₂Si phase. Quantitative EMPA analysis and elemental mapping revealed that the La-rich phase included Al, La, and Si and may be described as Al₂LaSi₂ phase. This phase shows a visible modifying effect on the eutectic Mg₂Si phase, likely due to absorbing on the liquid/solid interface.

The paper discusses the complex effect of melt overheating with subsequent fast cooling down to the pouring temperature on the crystallization process, microstructure and mechanical properties of Al-Mg-Si aluminum alloy. The results obtained facilitated the establishment of rational modes of melt overheating, leading to a significant change in the dispersion and morphology of structural components. In particular, with an increase in the melt overheating temperature to 900 °C with holding and subsequent rapid cooling to the casting temperature, a decrease in the average size of dendritic cells of the aluminum solid solution from 39 μm to 13 μm was observed. We also noticed the refinement of eutectic inclusions of the Mg₂Si phase with compact morphology. An increased level of mechanical properties was noted; the maximum values of tensile strength and elongation reached 228 MPa and 5.24%, respectively, which exceeded the initial values by 22.5% and 52.3%, correspondingly. The microhardness of the aluminum solid solution sequentially increased from 38.21 to 56.5 HV with an increase in the temperature during melt overheating. According to the EDS linear scanning, an increase in the superheat temperature of the melt is accompanied by an increase in the degree of saturation of the solid solution with magnesium.