The European steel industry produces about 70 million tons/year of steel by the electric arc furnace (EAF). The slag consists of about 15% by weight of the produced steel, thus from the perspective of the circular economy, it has a high potential as a co-product. This research aims to assess an innovative reuse of EAF slag as filler in different polymer matrixes: thermoplastic (polypropylene), thermosetting (epoxy resin), elastomeric (nitrile butadiene rubber), and recycled end of life rubber tire. A comparison between neat polymer and polymer filled with a certain amount of EAF slag has been carried out by tensile (or flexural), compression, and hardness tests. Experimental results show that slag as a filler increases the composites’ hardness and elastic modulus at the expense of toughness. For a safe reuse of the slag, the leaching of hazardous elements must comply with current legislation. It was found that, although the used EAF slag releases small amounts of Cr, Mo, and V, incorporating it into a polymer matrix reduces the leaching. The EAF slag particles distribution has been observed by scanning electron microscopy (SEM) images. The obtained results show good technical feasibility of this innovative slag application so that it could pave the way to a new industrial symbiosis between dissimilar sectors, bringing economic and environmental benefits.

This work shows an innovative application for electric arc furnace (EAF) slag: its use as a filler for nitrile butadiene rubber (NBR). Composites with various EAF slag contents were tested. It was found that the polymer matrix significantly reduces the leaching of slag (determined according to the standard CEN-EN 12457-2) incorporated in the NBR. The processability characteristics determined by the rheometric curves highlight that the EAF slag accelerates the crosslinking kinetics, reducing the production cycle time. Mechanical characterization demonstrated that EAF slag increases hardness and compression modulus. The ability to recover an imposed deformation quantified by the compression set is reduced as the EAF slag amount increases but remains below an acceptable value. It can be stated that in sealing systems, the EAF slag as a filler for NBR positively affects the compound properties. Moreover, NBR filled with EAF slag also has magnetic properties compared with standard rubber.

This work reports and analyzes the mechanical properties of some composites obtained using stabilized waste with epoxy resins E-227. For comparison, correspondent composite samples were realized using calcite as a filler. The recovered stabilized waste was obtained by means of a new method to stabilize municipal solid waste incineration (MSWI) fly ash (FA), based on the use of bottom ash (BA). The aim of this paper is to show that the stabilization process, which can be considered a zero—waste treatment, produces inert materials, that can be reused as a filler. The production of new filler was made on a pilot plant, designed to verify the transferability of the proposed stabilization technology. Mechanical analysis revealed that flexural modulus raises by increasing the filler content around 30% wt, independently of filler type, stabilized sample or calcium carbonate. Mechanical properties are lower in the samples with the high amount of filler due to the crowding effect. The morphology of composite materials showed a non-homogeneous dispersion of particles in stabilized sample filler, characterized by large particle agglomerates. Finally, according to the ESCAPE simplified method, the obtained composites result more sustainable in comparison with the corresponding ones produced by using natural resources (like calcite). These findings open new possibilities for the reuse of the stabilized material, in frame of circular economy principles, with environmental and economic advantages.

Environmental stress cracking is a serious problem for polyethylene because it can cause failure without any visible warning due to the slow crack growth accelerated by aggressive agents. Tie molecules and entanglements are the main macromolecular characteristic increasing environmental stress cracking resistance, thus in this work mechanical and thermal properties governed by those macromolecular characteristics are determined by performing simple tests executable in the industrial laboratories for quality control on recycled high-density polyethylene. The mutual relation between the determined properties confirms their dependence on the investigated macromolecular characteristics and allows to predict in a comparative way the expected environmental stress cracking. The mechanical properties related to the environmental stress cracking resistance are the strain hardening modulus and the natural draw ratio. The strain hardening modulus is an intrinsic property that measure the disentanglement capability of the inter-lamellar links and the natural draw ratio is a highly sensitive parameter to the macromolecular network strength via the intercrystalline tie molecules. Since the measurement of these properties according to the standard ISO 18,488 requires a temperature chamber not often available in the industrial laboratories, the tensile test was performed also at room temperature and displacement rate 0.5 mm/min; a proportionality between the data obtained at different test condition emerged. The thermal property related to the environmental stress cracking resistance is the stepwise isothermal segregation ratio that state the chain fraction that generates a high rate of tie molecules responsible of environmental stress cracking resistance.