The biosynthesis of oxide semiconductor nanoparticles (NPs) using materials found in nature opens a wide field of study focused on sustainability and environmental protection. Biosynthesized NPs have the capacity to eliminate organic dyes, which pollute water and cause severe damage to the environment. In the present work, the green synthesis of zinc oxide (ZnO) NPs was carried out using Capsicum annuum var. Anaheim extract. The photocatalytic elimination of methylene blue (MB), methyl orange (MO), and Rhodamine B (RhB) in UV radiation was evaluated. The materials were characterized by scanning and transmission electron microscopy (SEM and TEM) and SEM-coupled energy dispersive spectroscopy (EDS), attenuated total reflectance-infrared (ATR-IR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Photoluminescence (PL), and ultraviolet-visible spectroscopy (UV-Vis). The TEM analysis showed the NPs have an average size of 40 nm and quasi-spherical shape. ATR-IR showed the ZnO NPs contained functional groups from the extract. The analysis through XRD indicated that the NPs have a hexagonal zincite crystal structure with an average crystallite size of approximately 17 nm. The photoluminescence spectrum (PL) presented an emission band at 402 nm. From the UV-Vis spectra and TAUC model, the band-gap value was found to be 2.93 eV. Finally, the photocatalytic assessment proved the ZnO NPs achieved 100% elimination of MB at 60 min exposure, and 85 and 92% degradation of MO and RhB, respectively, at 180 min. This indicates that ZnO NPs, in addition to using a friendly method for their synthesis, manage to have excellent photocatalytic activity in the degradation of various organic pollutants.

Currently, several organic dyes found in wastewater cause severe contamination problems for flora, fauna, and people in direct contact with them. This research proposes an alternative for the degradation of polluting dyes using ZnO nanoparticles (NPs) synthesized by an ecological route using leaf and root extracts of Ambrosia ambrosioides as a reducing agent (with a weight/volume ratio = 4%). Scanning Electron Microscopy (SEM) was used to determine the morphology, showing an agglomeration of cluster-shaped NPs. Using Transmission Electron Microscopy (TEM), different sizes of NPs ranging from 5 to 56 nm were observed for both synthesized NPs. The composition and structure of the nanomaterial were analyzed by infrared spectroscopy (FT-IR) and X-ray diffraction (XRD), showing as a result that the NPs have a wurtzite-like crystalline structure with crystallite sizes around 32–37 nm for both samples. Additionally, the bandgap of the NPs was calculated using Ultraviolet Visible Spectroscopy (UV–Vis), determining values of 2.82 and 2.70 eV for the NPs synthesized with leaf and root, respectively. Finally, thermogravimetric analysis demonstrated that the nanoparticles contained an organic part after the green synthesis process, with high thermal stability for both samples. Photocatalytic analysis showed that these nanomaterials can degrade four dyes under UV irradiation, reaching 90% degradation for methylene blue (MB), methyl orange (MO) and Congo red (CR) at 60, 100 and 60 min, respectively, while for methyl red (MR) almost 90% degradation was achieved at 140 min of UV irradiation. These results demonstrate that it is effective to use Ambrosia ambrosioides root and leaf extracts as a reducing agent for the formation of ZnO NPs, also evidencing their favorable application in the photocatalytic degradation of these four organic dyes.

Symmetry in nanomaterials is essential to know the behavior of their properties. In the present research, the photocatalytic properties of SnO₂ and ZnO nanoparticles were compared for the degradation of the cationic dyes Methylene Blue (MB) and Rhodamine B (RB). The nanoparticles were obtained through a green synthesis process assisted by Randia echinocarpa extracts; they were then analyzed through Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD) to characterize their structure. Transmission electron microscopy (TEM) was used to identify the morphology and disclose nanoparticle size, and the optical properties were studied through Ultraviolet–visible spectroscopy (UV–Vis). The results show that the synthesized SnO₂ and ZnO nanomaterials have quasispherical morphologies with average sizes of 8–12 and 4–6 nm, cassiterite and wurtzite crystal phases, and band gap values of 3.5 and 3.8 eV, respectively. The photocatalytic activity yielded 100% degradation of the MB and RB dyes in 210 and 150 min, respectively. ZnO performed higher photocatalytic degradation of the cationic dyes than SnO₂ due to a higher content of Randia echinocarpa extracts remaining after the green synthesis process.

The high demand for nanomaterials in the field of industry and science has forced researchers to develop new synthesis methods that are more efficient, economical, and environmentally friendly. At present, the application of green synthesis has taken a great advantage over conventional synthesis methods because it helps with the control of the characteristics and properties of the resulting nanomaterials. In this research, ZnO nanoparticles (NPs) were synthesized by biosynthesis using dried boldo (Peumus boldus) leaves. The resulting biosynthesized NPs had a high purity, quasi-spherical shape with average sizes ranging from 15 to 30 nm and a band gap of ~2.8–3.1 eV. These NPs were used in the photocatalytic activity of three organic dyes. The results showed degradation of 100% methylene blue (MB) in 180 min, 92% methyl orange (MO) in 180 min, and 100% Rhodamine B (RhB) in 30 min of exposure. These results show that the Peumus boldus leaf extract is effective in the biosynthesis of ZnO NPs with good photocatalytic properties.