The aim of the study was to prepare and evaluate the potential use of poly(lactic acid)/poly(vinyl alcohol) (PLA/PVA) nanoparticle formulations as a drug delivery system. The nanoparticle formulations were successfully developed by the double emulsification/solvent evaporation method. The developed formulations were optimized using the quality by design approach of the ICH Q8 (Pharmaceutical Development) guideline. In the studies, the effects of emulsifying devices, evaporation technique, centrifugation effect, and polymer concentrations on the physicochemical parameters of the formulations were investigated to obtain the best results. Furthermore, the prepared formulations were evaluated for clarity, particle size, distribution, zeta potential, surface and morphological features, preparation efficiency, and long-term stability. Based on the obtained results, the nanoparticle formulation containing 12.5% PLA, 1% primer, and seconder PVA has a suitable particle size (181.7 ± 2.194 nm) and distribution (0.104 ± 0.049), zeta potential (-0.88 ± 0.45 mV), and high preparation efficiency (65.38%), and nanoparticles were spherical, had a smooth surface, and were stable up to 12 months. In conclusion, this novel formulation can be used as a potential drug delivery system.

Breast cancer is a leading cause of cancer-related mortality among women worldwide, with millions of new cases diagnosed yearly. Addressing the burden of breast cancer mortality requires a comprehensive approach involving early detection, accurate diagnosis, effective treatment, and equitable access to healthcare services. In this direction, nano-radiopharmaceuticals have shown potential for enhancing breast cancer diagnosis by combining the benefits of nanoparticles and radiopharmaceutical agents. These nanoscale formulations can provide improved imaging capabilities, increased targeting specificity, and enhanced sensitivity for detecting breast cancer lesions. In this study, we developed and evaluated a novel nano-radio radiopharmaceutical, technetium-99m ([^99mTc]Tc)-labeled trastuzumab (TRZ)-decorated methotrexate (MTX)-loaded human serum albumin (HSA) nanoparticles ([^99mTc]-TRZ-MTX-HSA), for the diagnosis of breast cancer. In this context, HSA and MTX-HSA nanoparticles were prepared. Conjugation of MTX-HSA nanoparticles with TRZ was performed using adsorption and covalent bonding methods. The prepared formulations were evaluated for particle size, PDI value, zeta (ζ) potential, scanning electron microscopy analysis, encapsulation efficiency, and loading capacity and cytotoxicity on MCF-7, 4T1, and MCF-10A cells. Finally, the nanoparticles were radiolabeled with [^99mTc]Tc using the direct radiolabeling method, and cellular uptake was performed with the nano-radiopharmaceutical. The results showed the formation of spherical nanoparticles, with a particle size of 224.1 ± 2.46 nm, a PDI value of 0.09 ± 0.07, and a ζ potential value of −16.4 ± 0.53 mV. The encapsulation efficiency of MTX was found to be 32.46 ± 1.12%, and the amount of TRZ was 80.26 ± 1.96%. The labeling with [^99mTc]Tc showed a high labeling efficiency (>99%). The cytotoxicity studies showed no effect, and the cellular uptake studies showed 97.54 ± 2.16% uptake in MCF-7 cells at the 120th min and were found to have a 3-fold higher uptake in cancer cells than in healthy cells. In conclusion, [^99mTc]Tc-TRZ-MTX-HSA nanoparticles are promising for diagnosing breast cancer and evaluating the response to treatment in breast cancer patients.

Alendronate sodium (ALD) is used orally but it is poorly absorbed from the gastrointestinal (GI) tract. For this reason, microemulsion system was chosen to evaluate ALD from the GI tract after oral delivery. This study was aimed to prepare water-in-oil (w/o) microemulsion formulation of ALD and evaluate the permeability of ALD microemulsion from Caco-2 cell lines with radioactive and nonradioactive studies. The ALD microemulsion was developed by using pseudo-ternary phase diagram and composed of Soybean oil, Colliphor EL, Tween 80, Transcutol and distilled water. The prepared ALD microemulsion was characterized by physical appearance, droplet size, viscosity, pH, electrical conductivity and refractive index. The stability of the formulation was investigated for 6 months at 25±2°C/60±5% of relative humidity (RH) as well as at 40±2°C/75±5% RH. After that 1 mg of ALD was radiolabeled with 99mTc and added to microemulsion. The permeability studies were performed with both 99mTc-ALD microemulsion and ALD microemulsion. The experimental results suggested that ALD microemulsion presented adequate stability with droplet size varying from 37.8±0.9 to 39.9±1.2 nm during incubation time. In addition, ALD microemulsion was radiolabeled with high labeling efficiency (>95%). In a non-radioactive study, ALD permeability was found to be 45 µg.mL-1 and microemulsion has high permeability percentage when compared to another study. The novel w/o microemulsion formulation has been developed for oral delivery of ALD. Based on the results, permeability of ALD could be significantly improved by the microemulsion formulation. In addition, 99mTc-ALD microemulsion in capsule can be used for bone disease treatment and diagnosis.