The study presents an investigation of thermal energy consumption for heating in an educational building located in the north-eastern part of Poland in 2017–2020, after deep thermomodernization. An evaluation of the actual energy effects was made based on measurements carried out over a 4-year operational period. They were compared with the results of theoretical calculations included in the energy audit and an attempt was made to describe the reasons for the discrepancies. The planned and achieved economic efficiency indicators were assessed and the amount of reduction of pollutant emissions was determined. The performed analysis allowed for an assessment of the impact of deep thermomodernization in terms of reducing heat energy consumption for central heating purposes, as well as reducing greenhouse gas emissions such as CO₂, SO_x, NO_x and benzo(a)pyrene to the atmosphere. The implementation of thermomodernization in buildings led to savings of about 43% in terms of heat energy consumption for heating and a reduction in pollutant emissions. The theoretical savings based on the audit were 50.4%. The obtained results show that deep thermomodernization contributes to the improvement of energy and ecological efficiency in educational buildings, however, without the possibility of using subsidies, the investment is unprofitable. All the obtained results were discussed with the available literature sources and have been summarized with appropriate conclusions.

The aim of the article was to test new types of rubber-containing particleboards created from waste materials, which positively contributes to environmental protection, saving primary resources and reducing production costs. This article focuses on the study of three-layer particleboards made from wood particles (spruce non-treated beams) and waste rubber granulates (tires, mixture of seals and carpets, internal flammable cables, external non-flammable cables). Urea–formaldehyde glue, melamine–formaldehyde glue, paraffin emulsion, and ammonium nitrate were used as a binders and excipients in the manufacturing of particleboards. In the core layer of each particleboard, 10% of the weight was made up of rubber granulate. Physical properties (density, water absorption, thickness swelling) and mechanical properties (internal bonding strength, modulus of rupture, modulus of elasticity, screw driving torque) were assessed from this perspective using current EN technical standards. According to the findings, the average densities of all particleboards were comparable to each other in a range from 0.692 to 0.704 g·cm⁻³. The lowest average water absorption and thickness swelling reached particleboards containing 10% of waste internal flammable cables, namely 32.79% for water absorption and 13.21% for thickness swelling. The highest average internal bonding strength reached particleboards without rubber filler and particleboards containing 10% of waste external non-flammable cables, namely 0.52 MPa for both types. The highest average modulus of rupture reached particleboards without rubber filler, namely 12.44 MPa. The highest average modulus of elasticity reached particleboards containing 10% of waste internal flammable cables, namely 2206.29 MPa, and the highest screw driving torque reached particleboards without rubber filler, namely 0.46 N·m for seating torque and 1.44 N·m for stripping torque. The results show that particleboards containing waste external non-flammable cables and particleboards containing waste internal flammable cables achieved comparable results to particleboards without rubber filler, which provides a good basis for a new way of utilizing this type of waste in the form of producing new wood–rubber composites.