The microstructural development of 316L stainless steel (SS) was investigated over a wide range of systematically varied laser powder bed fusion (LPBF) parameters, such as laser power, scan speed, hatch spacing and volumetric energy density. Relative density, melt pool width and depth, and the size of sub-grain cellular structure were quantified and related to the temperature field estimated by Rosenthal solution. Use of volumetric energy density between 46 and 127 J/mm³ produced nearly fully dense (≥99.8%) samples, and this included the best parameter set: power = 200 W; scan speed = 800 mm/s; hatch spacing = 0.12 mm; slice thickness = 0.03; energy density = 69 J/mm³). Cooling rate of 10⁵ to 10⁷ K/s was estimated base on the size of cellular structure within melt pools. Using the optimized LPBF parameters, the as-built 316L SS had, on average, yield strength of 563 MPa, Young’s modulus of 179 GPa, tensile strength of 710 MPa, and 48% strain at failure.

The present work correlates the quasi-static, tensile mechanical properties of additively manufactured Ti-6Al-4V extra low interstitial (ELI, Grade 23) alloy to the phase constituents, microstructure, and fracture surface characteristics that changed with post-heat treatment of stress relief (670 °C for 5 h) and hot isostatic pressing (HIP with 100 MPa at 920 °C for 2 h under an Ar atmosphere). Ti-6Al-4V ELI alloy tensile specimens in both the horizontal (i.e., X and Y) and vertical (Z) directions were produced by the laser powder bed fusion (LPBF) technique. Higher yield strength (1141 MPa), higher tensile strength (1190 MPa), but lower elongation at fracture (6.9%), along with mechanical anisotropy were observed for as-stress-relieved (ASR) samples. However, after HIP, consistent and isotropic mechanical behaviors were observed with a slight reduction in yield strength (928 MPa) and tensile strength (1003 MPa), but with a significant improvement in elongation at fracture (16.1%). Phase constituents of acicular α′ phase in ASR and lamellar α + β phases in HIP samples were observed and quantified to corroborate the reduction in strength and increase in ductility. The anisotropic variation in elongation at fracture observed for the ASR samples, particularly built in the build (Z) direction, was related to the presence of “keyhole” porosity.