This paper focuses on the dissociation of carbon dioxide (CO₂) following the absorption processes of microwave radiation by noncontact metal wire (tungsten). Using a microwave plasma generator (MPG) with a single-mode cavity, we conducted an interaction of microwaves with a noncontact electrode in a CO₂ atmosphere. High energy levels of electromagnetic radiation are generated in the focal point of the MPG’s cylindrical cavity. The metal wires are vaporized and ionized from this area, subsequently affecting the dissociation of CO_2. The CO₂ dissociation is highlighted through plasma characterization and carbon monoxide (CO) quantity determination. For plasma characterization, we used an optical emission spectroscopy method (OES), and for CO quantity determination, we used a gas analyzer instrument. Using an MPG in the CO₂ atmosphere, we obtained a high electron temperature of the plasma and a strong dissociation of CO₂. After 20 s of the interaction between microwaves and noncontact electrodes, the quantity of CO increased from 3 ppm to 1377 ppm (0.13% CO). This method can be used in space applications to dissociate CO₂ and refresh the atmosphere of closed spaces.

The effects induced by microwave field upon tungsten wires of different diameters were investigated. Tungsten wires with 0.5 and 1.0 mm diameters were placed in the focal point of a single-mode cylindrical cavity linked to a microwave generator and exposed to microwave field in ambient air. The experimental results showed that the 0.5 mm diameter wire was completely vaporized due to microwaves strong absorption, while the wire with 1 mm diameter was not ignited. During the interaction between microwaves and tungsten wire with 0.5 mm diameter, a plasma with a high electronic excitation temperature was obtained. The theoretical analysis of the experiment showed that the voltage generated by metallic wires in interaction with microwaves depended on their electric resistance in AC and the power of the microwave field. The physical parameters and dimension of the metallic wire play a crucial role in the ignition process of the plasma by the microwave field. This new and simple method to generate a high-temperature plasma from a metallic wire could have many applications, especially in metal oxides synthesis, metal coatings, or thin film deposition.

The aim of this research is to understand the plasma initiation process generated by metallic wires when interacting with high energy density microwaves. Lead (Pb) and molybdenum (Mo) wires of 0.5 mm diameter were investigated in this experiment. The tip of the metallic wire was placed into the nodal point of a waveguide cavity attached to a microwave generator, where it was exposed to the high energy density of the microwave field. Following the interaction between microwaves and the metallic wire, a plasma was initiated having as effect the wire vaporization. The experiments were conducted in atmospheric air at ∼1 bar pressure. From optical emission spectroscopy investigations it was observed that electronic excitation of the plasma has high values and it is in a local thermal equilibrium. The theoretical calculation of the voltages induced in the metallic wires when exposed to high energy density microwave field are similar to those measured in air breakdown experiments. The scanning electron microscopy analysis of the tips of the metallic wires showed that the field emission process is responsible for the ignition of the metallic wires and plasma generation.

This research highlights the different behaviors of titanium (Ti) wires under the action of 500 W and 800 W microwave power levels. Following the interaction between microwaves and a titanium wire placed in the node of the (TM₀₁₁—transverse magnetic mode) waveguide in air at atmospheric pressure, plasma was generated. Using optical emission spectroscopy technique it was observed that during plasma generation at 500 W and 800 W microwaves powers, metallic ions, and gas ions were created, and the plasmas fulfilled the local thermodynamic equilibrium (LTE) conditions. The XRD analysis showed that on the surface of the Ti wire exposed to 500 W microwave power a mixture of titanium dioxide (TiO₂) and titanium oxide (TiO) grew, while the Ti wire exposed to 800 W microwave power was completely vaporized and a mixture of TiO₂ and TiO nanoparticles was synthesized. The SEM analysis showed that the dimensions of the titanium oxide (TiO_x) nanoparticles generated by both microwave discharges ranged from 5 nm to 200 nm. The results of EDS analysis showed that the power of microwaves plays an important role in quantitative conversion from Ti wire into a TiO_x mixture. The TEM analysis indicates that most of the nanoparticles are either amorphous or nanocrystalline. Using this simple and inexpensive technique one can grow a TiO_x layer on the surface of titanium electrodes or can synthetize nanocrystalline TiO_x particles.

A new method for the synthesis and deposition of tungsten oxide nanopowders directly on the surface of a carbon-fiber-reinforced polymer composite (CFRP) is presented. The CFRP was chosen because this material has very good thermal and mechanical properties and chemical resistance. Also, CFRPs have low melting points and are transparent under ionized radiation. The synthesis is based on the direct interaction between high-power-density microwaves and metallic wires to generate a high-temperature plasma in an oxygen-containing atmosphere, which afterward condenses as metallic oxide nanoparticles on the CFRP. During microwave discharge, the value of the electronic temperature of the plasma, estimated from Boltzmann plots, reached up to 4 eV, and tungsten oxide crystals with a size between 5 nm and 100 nm were obtained. Transmission electron microscopy (TEM) analysis of the tungsten oxide nanoparticles showed they were single crystals without any extended defects. Scanning electron microscopy (SEM) analysis showed that the surface of the CFRP sample does not degrade during microwave plasma deposition. The X-ray attenuation of CFRP samples covered with tungsten oxide nanopowder layers of 2 µm and 21 µm thickness was measured. The X-ray attenuation analysis indicated that the thin film with 2 µm thickness attenuated 10% of the photon flux with 20 to 29 KeV of energy, while the sample with 21 µm thickness attenuated 60% of the photon flux.

We present a novel approach for the synthesis of crystalline zinc oxide (ZnO) nanopowders based on the direct interaction of high-power microwave radiation with a zinc wire in atmospheric air. The process utilizes a localized microwave-induced plasma to rapidly vaporize the metal, followed by oxidation and condensation, resulting in the deposition of ZnO nanostructures on glass substrates. Plasma diagnostics confirmed the generation of a plasma in local thermodynamic equilibrium (LTE), characterized by high electron temperatures. Optical emission spectroscopy highlighted atomic species such as ZnI, ZnII, OI, OII, and NI, as well as molecular species including OH, N₂ and O₂. The spectral fingerprint of N₂ molecules reveals the presence of high energy electrons, while the persistent occurrence of OI and OII emission lines throughout the plasma spectrum reveals that ZnO formation is mainly driven by the continuous dissociation of molecular oxygen. High crystallinity and chemical purity of the synthesized ZnO nanoparticles were confirmed through SEM, TEM, XRD, FTIR, and EDX characterization. The resulting nanorods exhibit a rod-like morphology, with diameters ranging from 12 nm to 63 nm and lengths between 58 nm and 354 nm. This low-cost, high-yield method offers a scalable and efficient route for metal oxide nanomaterial fabrication via direct metal–microwave coupling, providing a promising alternative to conventional physical and chemical synthesis techniques.