Cu–Cr-based alloys exhibit excellent electrical conductivity and strength, but their poor thermal stability limits their application in industry. In this paper, Cu–0.2Cr (at. %) and Cu–0.2Cr–0.12Ag (at. %) alloys were prepared to study the effect of Ag on the properties, microstructure, and thermal stability of the Cu–Cr alloy. Microstructure and precipitation were observed by an optical microscope (OM) and a transmission–electron microscope (TEM). After cold-drawing by 99.9% and aging at 450 °C for 2 h, the peak hardness and electric conductivity of the Cu–Cr alloy were 120.3 HV and 99.5% IACS, respectively, and those of the Cu–Cr–Ag alloy were 135.8 HV and 98.3% IACS, respectively. The softening temperature of the Cu–Cr alloy was 500~525 °C, and that of the Cu–Cr–Ag alloy was about 550 °C. The creep strains of the Cu–Cr and Cu–Cr–Ag alloys at 40 MPa and 400 ℃ for 50 h were 0.18% and 0.05%, respectively. Ag elements improved the thermal stability of the Cu–Cr alloy. Recovery and recrystallization occurred before the coarsening of precipitates during the softening process. Ag atoms mainly improved the softening resistance of the alloy by delaying recrystallization, and mainly increased creep resistance by preventing the increase in mobile-dislocation density.

To study the effect of aluminum and nickel elements on the microstructures and properties of the nickel–aluminum bronze (NAB) alloy, four kinds of alloys with different compositions, ZCuAl7–7–4–2, ZCuAl8-6-4-2, ZCuAl9-5-4-2, and ZCuAl10-4-4-2, are prepared by vacuum-melting technology. The effects of different Al/Ni ratios on the microstructures of NAB are investigated using a metalloscope, scanning electron microscopy, transmission electron microscopy, and XPS analysis. The mechanical property is evaluated with microhardness testing and tensile mechanical testing. The corrosion resistance is evaluated using mass-loss testing, electrochemical testing, and corrosion-product characterization. The results show that with the increase of the Al/Ni ratio, the content of precipitated phases increases, while β′ and hard κ, which have a different morphology, appear. As the Al/Ni ratio rises from 1 to 2.5, the hardness increases from 104 HV to 202 HV, and the tensile strength increases by 394 MPa from 356 MPa to 751 MPa, but the elongation decreases substantially from 50.50% to 11.00%. The best corrosion resistance is shown on ZCuAl7-7-4-2, with a corrosion rate of 0.00267 mm/a after 30 d of static immersion corrosion in 3.5 wt.% NaCl solution. Through electrochemical testing and corrosion-product characterization, it is found that ZCuAl7-7-4-2 has the largest polarization resistance R_p, and the selective corrosion of the surface is mild.