Biocoke has the potential to reduce the fossil-based materials in metallurgical processes, along with mitigating anthropogenic CO₂- and greenhouse gas (GHG) emissions. Reducing those emissions is possible by using bio-based carbon, which is CO₂-neutral, as a partial replacement of fossil carbon. In this paper, the effect of adding 5, 10, 15, 30, and 45 wt.% biomass pellets on the reactivity, the physicomechanical, and electrical properties of biocoke was established to assess the possibility of using it as a fuel and reducing agent for a blast furnace (BF) or as a carbon source in a submerged arc furnace (SAF). Biocoke was obtained under laboratory conditions at final coking temperatures of 950 or 1100 °C. Research results indicate that for BF purposes, 5 wt.% biomass additives are the maximum as the reactivity increases and the strength after reaction with CO₂ decreases. On the other hand, biocoke’s physicomechanical and electrical properties, obtained at a carbonization temperature of 950 °C, can be considered a promising option for the SAF.

Since the European Union defined ambitious CO₂ emission targets, low-carbon-emission alternatives to the widespread integrated blast furnace (BF)—basic oxygen furnace (BOF) steelmaking strategy—are demanded. Direct reduction (DR) with natural gas as the reducing agent, already an industrially applied technology, is such an alternative. Consequently, the melting behavior of its intermediate product, i.e., direct reduced iron (DRI), in either an electric arc furnace (EAF) or a submerged arc furnace (SAF), is of great interest. Based on the conditions in these aggregates, a test series to experimentally simulate the first few seconds after charging DRI was defined. DRI samples with different carbon contents and hot briquetted iron (HBI) were immersed in high- and low-carbon melts as well as high- and low-iron oxide slags. The reacted samples were quenched in liquid nitrogen. The specimens were qualitatively evaluated by investigating their surfaces and cross sections. The dissolution of carbon-free DRI progressed relatively slowly and was driven by heat transfer. However, carbon, present either in the DRI sample or in the melt, not only accelerated the dissolution process, but also reacted with residual iron oxide in the pellet or the slag.

Hydrogen-based direct reduction is a promising technology for CO₂ lean steelmaking. The electric arc furnace is the most relevant aggregate for processing direct reduced iron (DRI). As DRI is usually added into the arc, the behavior in this area is of great interest. A laboratory-scale hydrogen plasma smelting reduction (HPSR) reactor was used to analyze that under inert conditions. Four cases were compared: carbon-free and carbon-containing DRI from DR-grade pellets as well as fines from a fluidized bed reactor were melted batch-wise. A slag layer’s influence was investigated using DRI from the BF-grade pellets and the continuous addition of slag-forming oxides. While carbon-free materials show a porous structure with gangue entrapments, the carburized DRI forms a dense regulus with the oxides collected on top. The test with slag-forming oxides demonstrates the mixing effect of the arc’s electromagnetic forces. The cross-section shows a steel melt framed by a slag layer. These experiments match the past work in that carburized DRI is preferable, and material feed to the hotspot is critical for the EAF operation.