Timber structures in marine applications are often exposed to severe degradation conditions caused by mechanical loads and wood-degrading organisms. This paper presents the use of timber in marine environments in Europe from a wood protection perspective. It discusses the use of wood in coastline protection and archeological marine wood, reviews the marine borer taxa in European waters, and gives an overview of potential solutions for protection of timber in marine environments. Information was compiled from the most relevant literature sources with an emphasis on new wood protection methods; the need for research and potential solutions are discussed. Traditionally, timber has been extensively utilized in a variety of marine applications. Although there is a strong need for developing new protection systems for timber in marine applications, the research in this field has been scarce for many years. New attempts to protect timber used in marine environments in Europe have mainly focused on wood modification and the use of mechanical barriers to prevent colonization of marine wood borers. The importance of understanding the mechanisms of settlement, migration, boring, and digestion of the degrading organisms is key for developing effective systems for protecting timber in marine environments.

The furfurylation process is an extensively investigated wood modification process. Furfuryl alcohol molecules penetrate into the wood cell wall and polymerize in situ. This results in a permanent swelling of the wood cell walls. It is unclear whether or not chemical bonds exist between the furfuryl alcohol polymer and the wood. In the present study, five different wood species were used, both hardwoods and softwoods. They were treated with three different furfurylation procedures and leached according to three different leaching methods. The present study shows that, in general, the leachates from furfurylated wood have low toxicity. It also shows that the choice of leaching method is decisive for the outcome of the toxicity results. Earlier studies have shown that leachates from wood treated with furfuryl alcohol prepolymers have higher toxicity to Vibrio fischeri than leachates from wood treated with furfuryl alcohol monomers. This is probably attributable to differences in leaching of chemical compounds. The present study shows that this difference in the toxicity most likely cannot be attributed to maleic acid, furan, furfural, furfuryl alcohol, or 2-furoic acid. However, the difference might be caused by the two substances 5-hydroxymethylfurfural and 2,5-furandimethanol. The present study found no difference in the amount of leached furfuryl alcohol between leachates from furfurylated softwood and furfurylated hardwood species. Earlier studies have indicated differences in grafting of furfuryl alcohol to lignin. However, nothing was found in the present study that could support this. The leachates of furfurylated wood still need to be investigated further to identify the chemical differences between wood furfurylated with furfuryl alcohol monomers and furfuryl alcohol prepolymers. Environ. Toxicol. Chem. 2010;29:1918–1924. © 2010 SETAC

The aim of cell wall modification is to keep wood moisture content (MC) below favorable conditions for decay organisms. However, thermally modified, furfurylated, and acetylated woods partly show higher MCs than untreated wood in outdoor exposure. The open question is to which extent decay is influenced by the presence of liquid water in cell lumens. The present paper contributes to this topic and reports on physiological threshold values for wood decay fungi with respect to modified wood. In total, 4200 specimens made from acetylated, furfurylated, and thermally modified beech wood (Fagus sylvatica L.) and Scots pine sapwood (sW) (Pinus sylvestris L.) were exposed to Coniophora puteana and Trametes versicolor. Piles consisting of 50 small specimens were incubated above malt agar in Erlenmeyer flasks for 16 weeks. In general, pile upward mass loss (ML) and MC decreased. Threshold values for fungal growth and decay (ML≥2%) were determined. In summary, the minimum MC for fungal decay was slightly below fiber saturation point of the majority of the untreated and differently modified materials. Surprisingly, T. versicolor was able to degrade untreated beech wood at a minimum of 15% MC, and growth was possible at 13% MC. By contrast, untreated pine sW was not decayed by C. puteana at less than 29% MC.

There is a need for new solutions in wood protection against marine wood borers and termites in Europe. A new solution could be the esterification of wood with sorbitol and citric acid (SCA) since these are inexpensive and readily available feedstock chemicals and have shown protective properties against fungal wood degradation in earlier studies and prevented macrobiological degradation, as shown in this study. Protection of wood products in the marine environment lacks available wood preservatives that are approved for marine applications. Termite infestation is opposed mainly by biocide treatments of wood. Several wood modification systems show high resistance against both marine borers and subterranean termites. However, the existing commercialized wood modification products are costly. Both macrobiological forms of degradation represent a great threat for most European wood species, which are rapidly and severely degraded if not properly treated. This study investigated esterified wood in standard field trials against marine wood borers, and against subterranean termites in laboratory trials in a no-choice and choice test. The treatment showed good resistance against wood borers in the marine environment after one season and against subterranean termites in the laboratory after eight weeks. The low termite survival rate (SR) in the no-choice test during the first week of testing indicates a mode of action that is incomparable to other wood modification treatments.

When exposed to moisture, wood undergoes swelling and is susceptible to fungal degradation. Chemical modification via oligomeric lactic acid (OLA) treatment has been found to be a promising environmentally friendly solution to this disadvantage. In this study, wood was impregnated with OLA and then variously heat treated to polymerize the OLA in situ. The effect of curing temperature and time on OLA polymerization has been determined chemically. Dimensional stability was examined by water immersion and hygroscopicity measurements and biological decay resistance also evaluated. OLA impregnation followed by heat treatment enhanced wood properties. OLA cure at 160 °C for 48 h resulted in treated wood with greater dimensional stability and biological resistance.