A 58S bioglass with a composition in the ternary system 58SiO2-33CaO-9P2O5 (wt.%) was prepared by an innovation sol-gel process in which a small amount of ammonia was used to facilitate the condensation reactions within an acidic solution prepared by tetraethyl orthosilicate, triethyl phosphate and calcium nitrate tetrahydrate. The properties of synthetic glass were investigated by several techniques. The amorphous nature and high specific surface area (99.1m2/g) of the obtained glass were confirmed by using X-ray diffraction and low-temperature nitrogen adsorption techniques, respectively. In vitro experiments were performed by soaking glass samples in the simulated body fluid (SBF). The XRD patterns and SEM images confirmed the bioactivity of the synthesized bioglass by formation of a dense and visible hydroxyapatite layer on its surface after 2 days of in vitro assays. The ICP-OES data illustrated the ion exchange behaviours between the bioglass 58S and the SBF solution.

In this study, a nanostructured NdFeO₃ material was synthesized via a simple process of the hydrolysis of Nd (III) and Fe (III) cations in hot water with 5% NaOH as a precipitating agent. According to the results of the thermal behaviors of each hydroxide, either containing Fe (III) or Nd (III), the perovskite type of neodymium orthoferrite NdFeO₃ was simply synthesized by annealing a mixture of Fe (III) and Nd (III) hydroxides at 750 °C. The nanostructured NdFeO₃ was obtained in spherical granules with diameters of around 30 nm. The magnetic properties of the material were a coercive force (H_c) of 136.76 Oe, a remanent magnetization (M_r) of 0.68 emu·g^–1, and a saturation magnetization (M_s) of 0.79 emu·g^–1.

In this work, single-phase nanostructured NdFe_1−xCo_xO₃ (x = 0, 0.1, 0.2, and 0.3) perovskite materials were obtained by annealing stoichiochemistry mixtures of their component hydroxides at 750 °C for 60 min. The partial substitution of Fe by Co in the NdFeO₃ crystal lattice leads to significant changes in the structural characteristics, and as a consequence, also alters both the magnetic and optical properties of the resulting perovskites. The low optical band gap (E_g = 2.06 ÷ 1.46 eV) and high coercivity (H_c = 136.76 ÷ 416.06 Oe) give Co-doped NdFeO₃ nanoparticles a huge advantage for application in both photocatalysis and hard magnetic devices.

Bioactive glass 70SiO₂-30CaO (mol.%) was successfully synthesized by modified sol–gel in hot water without using an acid catalyst. TG-DSC analysis showed that the amorphous glass could be synthesized by sintering the sample at 700 °C for three hours. The N₂ adsorption/desorption and TEM investigations highlighted that the synthetic glass had a mesoporous structure, consisting of spherical particles with sizes in the range of 11–20 nm. The specific surface area, pore volume, and average pore diameter of synthetic glass were 150.13 m²/g, 0.37 cm³/g, and 11.84 nm, respectively. Moreover, synthetic bioactive glass presented interesting bioactivity and good biocompatibility after in vitro experiments in simulated body fluid (SBF) and in cellular medium.