Failure of osteosynthesis implants is an intricate matter with challenging management that calls for efficient investigation and prevention. Using implant retrieval analysis combined with standard radiological examination, we evaluated the main causes for osteosynthesis implant breakdown and the relations among them for a series of cases. Twenty-one patients diagnosed with implant failure were assessed for this work. For metallurgical analysis, microscopy techniques such as scanning electron microscopy (SEM), stereomicroscopy, and optical microscopy were employed. The results showed that material structural deficiencies (nine patients) and faulty surgical techniques (eight patients) were the main causes for failure. An important number of patients presented with material structural deficiencies superimposed on an imperfect osteosynthesis technique (six patients). Consequently, the importance of failure retrieval analysis should not be overlooked, and in combination with other investigational techniques, must provide information for both implant manufacturing and design improvement, as well as osteosynthesis technique optimization.

In the latter part of the 20th century, remarkable developments in new dental materials and technologies were achieved. However, regarding the impact of dental resin-based materials 3D-printed on cellular responses, there have been a limited number of published studies recently. The biocompatibility of dental restorative materials is a controversial topic, especially when discussing modern manufacturing technologies. Three-dimensional printing generates the release of residual monomers due to incomplete polymerization of materials and involves the use of potentially toxic substances in post-printing processes that cannot be completely eliminated. Considering the issue of biocompatibility, this article aims to establish an overview of this aspect, summarizing the different types of biocompatibility tests performed on materials used in 3D printing in dentistry. In order to create this comprehensive review, articles dealing with the issue of 3D printing in dentistry were analysed by accessing the main specialized search engines using specific keywords. Relevant data referring to types of materials used in 3DP to manufacture various dental devices, polymerization methods, factors affecting monomer release, cytotoxicity of unreacted products or post-curing treatments, and methods for assessing biocompatibility were analysed. Although the introduction of new restorative materials used in dental treatments is subject to national and international regulations and standards, it is necessary to investigate them regarding biocompatibility in order to support or deny the manufacturers’ statements regarding this aspect.

Poor oral hygiene leads to serious damages of theteeth’s surface enamel such as micro-abrasions and acid erosion. These alterations combined with bacterial plaque result in cavity appearance. Prophylactic measures include various techniques for enamel surface restoration. Fluorination is one of the most important treatments for this purpose. Therefore, in the present research, we investigated the classical fluorination treatment compared with laser photodynamic fluorination performed on human enamel samples with poor surface quality. Three sample groups were investigated: veneer (F), inlay (I), and crowns (C). The general morphologic aspect was investigated by scanning electron microscopy (SEM), and the specific details such as the fine microstructure and nanostructure were investigated by atomic force microscopy (AFM) of the surface roughness. The samples were also investigated by Fourier transformed infrared attenuated total reflectance (FTIR-ATR) to evidence the fluorination effect on the enamel surface. Results showed that all initial samples had an altered state with micro-abrasions and erosion with mineral loss, which increase the surface roughness. The F group was the most damaged, having a higher roughness, and the I group was less damaged. Classic fluorination treatment partially restored the enamel by local re-mineralization, but did not obtain the parameters of healthy enamel. However, a significant decrease of the roughness was observed (statistical relevance p = 0.001 with the Breusch–Pagan Test). This fact was supported by the presence of newly formed fluorides in the FTIR-ATR spectra. The photodynamic laser fluorination restores the enamel in an enhanced manner by a strong re-mineralization, which implies a significant roughness value decrease comparable to healthy enamel. The Breusch–Pagan Test confirmed the relevance with p = 0.001. This is due to an extended re-mineralization abundant in fluoride crystals as observed by AFM and FTIR. Statistical p-values regarding laser application were in the range of 0.02–0.06, supporting its relevance in the fluorination effect. The final conclusion is that the photodynamic effect is able to favor the newly formed fluoride deposition onto the affected sites of the enamel surface.

In this study, a CoCrMo-based metallic alloy was manufactured using a 3D-printing method with metallic powder and a laser-based 3D printer. The obtained material was immersed in a simulated body fluid (SBF) similar to blood plasma and kept 2 months at 37 °C and in relative motion against the SBF in order to mimic the real motion of body fluids against an implant. At determined time intervals (24, 72, 168, 336, and 1344 h), both the metallic sample and SBF were characterized from a physical-chemical point of view in order to assess the alloy’s behaviour in the SBF. Firstly, the CoCrMo based metallic sample was characterized by scanning electron microscopy (SEM) for assessing surface corrosion and X-ray diffraction (XRD) for determining if and/or what kind of spontaneous protective layer was formed on the surface; secondly, the SBF was characterized by pH, electrical conductivity (EC), and inductively coupled plasma mass spectroscopy (ICP-MS) for assessing the metal ion release. We determined that a 3D-printed CoCrMo alloy does not represent a potential biological hazard in terms of the concentration of metal ion releases, since it forms, in a relatively short period of time, a protective CoCr layer on its exposed surface.

We are reporting a case of natural evolution and pathological data from a young person that was diagnosed with coronavirus disease 2019 (COVID-19). All data has been collected from the autopsy of a 30-year-old female, which was performed by the Department of Forensic Medicine from Emergency County Hospital, Drobeta Turnu Severin, Mehedinţi County, Romania. The infection with severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) was confirmed by reverse transcription polymerase chain reaction (RT–PCR) on the lung tissue which was obtained during autopsy. This case provides the opportunity to study the natural evolution of COVID-19 pneumonia in a young person with clinical signs of pneumonia but without associated comorbidities. The patient had not received any treatment. The histopathological examination of the lung revealed a process of productive proliferation, proteinaceous and fibrin-macrophagic interalveolar spaces exudate, and lesions consistent with vasculitis. In the heart, we identified a cardiac thrombus. These changes are likely to suggest an advanced natural evolution of SARS-CoV-2 virus infection.