An inhibitor that can effectively inhibit shale hydration is necessary for the safe and efficient development of shale gas. In this study, a novel ionic liquid copolymer shale inhibitor (PIL) was prepared by polymerizing the ionic liquid monomers 1-vinyl-3-aminopropylimidazolium bromide, acrylamide, and methacryloyloxyethyl trimethyl ammonium chloride. The chemical structure was characterized using fourier transform infrared spectroscopy (FT-IR) and hydrogen-nuclear magnetic resonance (H-NMR), and the inhibition performance was evaluated using the inhibition of slurrying test, bentonite flocculation test, linear expansion test, and rolling recovery test. The experimental results showed that bentonite had a linear expansion of 27.9% in 1 wt% PIL solution, 18% lower than that in the polyether amine inhibitor. The recovery rate of shale in 1 wt% PIL was 87.4%. The ionic liquid copolymer could work synergistically with the filtrate reducer, reducing filtration loss to 7.2 mL with the addition of 1%. Mechanism analysis showed that PIL adsorbed negatively charged clay particles through cationic groups, which reduced the electrostatic repulsion between particles. Thus, the stability of the bentonite gel systems was destroyed, and the hydration dispersion and expansion of bentonite were inhibited. PIL formed a hydrophobic film on the surface of clay and prevented water from entering into the interlayer of clay. In addition, PIL lowered the surface tension of water, which prevented the water from intruding into the rock under the action of capillary force. These are also the reasons for the superior suppression performance of PIL.

Ensuring wellbore stability is of utmost importance for safety when drilling in deep formations. However, high temperatures severely disrupt the drilling fluid gel system, leading to severe stability issues within ultra-deep formations containing micropores. This study focused on the development of a polymer-based plugging material capable of withstanding high temperatures up to 200 °C. A kind of microsphere, referred to as SST (styrene–sodium styrene sulfonate copolymer), was synthesized with a particle size of 322 nm. Compared to polystyrene, the thermal stability of SST is greatly improved, with a thermal decomposition temperature of 362 °C. Even after subjecting SST to hot rolling at 200 °C for 16 h, the particle size, elemental composition, and zeta potential remained stable within an aqueous dispersion system. The results of core displacement and NMR tests demonstrate that SST considerably reduces the pore diameter with a remarkable plugging efficiency of 78.9%. Additionally, when drilling fluids reach 200 °C, SST still enhances drilling fluid suspension and dispersion, and reduces fluid loss by over 36% by facilitating the dispersion of clay particles, improving the gel structure of the drilling fluid, resisting clay dehydration, and promoting plugging. The development of SST provides valuable insights into the preparation of high-temperature-resistant microspheres and the formulation of effective plugging agents for deep-well drilling fluids.

The ice sheet and subglacial geological environment in Antarctica have become the focus of scientific exploration. The development of Antarctic drilling technology will serve as a crucial safeguard for scientific exploration. However, the extremely ultra-low temperatures and intricate geological conditions present substantial obstacles for drilling operations in Antarctica, and the existing drilling fluid technology cannot satisfy the requirements of efficient and safe drilling. To ameliorate the wettability and rheology of ultra-low-temperature drilling fluids, a new amide material (HAS) was prepared using dodecylamine polyoxyethylene ether, azelaic acid, and N-ethylethylenediamine as raw materials. Experiments using infrared spectroscopy, nuclear magnetic hydrogen spectroscopy, and contact angle indicated that the target product was successfully synthesized. Performance evaluation showed that 2% HAS could achieve a yield point of 2.5 Pa for drilling fluid at −55 °C, and it also gave the fluid superior shear-thinning characteristics and a large thixotropic loop area. This indicated that HAS significantly enhanced the rheological properties of the drilling fluid, ensuring that it can carry cuttings and ice debris. In addition, 2% HAS could also increase the colloidal rate from 8% to more than 76% at −55 °C in different base oils. Meanwhile, the colloid rate was maintained above 92.4% when the density was 0.92~0.95 g/cm³. Mechanism studies showed that HAS increased the zeta potential and decreased the particle size of organoclay. At the same time, it changed the organoclay state from a clustered state to a uniformly dispersed state, and the particle size decreased. It was found that HAS formed a weak gel grid structure through interactions between polar groups, such as amide and imino groups with organoclays particles, thus improving the rheology and wettability of drilling fluid. In addition, HAS is an environmentally friendly high-performance material.