Polydimethylsiloxane (PDMS), a silicone-based elastomeric polymer, is generally cured by applying heat to a mixture of a PDMS base and crosslinking agent, and its material properties differ according to the mixing ratio and heating conditions. In this study, we analyzed the effects of different curing processes on the various properties of PDMS thin films prepared by mixing a PDMS solution comprising a PDMS base and a crosslinking agent in a ratio of 10:1. The PDMS thin films were cured using three heat transfer methods: convection heat transfer using an oven, conduction heat transfer using a hotplate, and conduction heat transfer using an ultrasonic device that generates heat internally from ultrasonic vibrations. The physical, chemical, mechanical, and tribological properties of the PDMS thin films were assessed after curing. The polymer chains in the PDMS thin films varied according to the heat transfer method, which resulted in changes in the mechanical and tribological properties. The ultrasonicated PDMS thin film exhibited the highest crystallinity, and hence, the best mechanical, friction, and wear properties.

The purpose of this study was to improve the tribological properties of polydimethylsiloxane (PDMS) by mixing lubricants into it.

In this study, we have developed a self-cleaning transparent coating on a glass substrate by dip coating a TiO₂ ̶ KH550 ̶ PEG mixed solution with super-hydrophilicity and good antifogging properties. The fabrication of the thin-film-coated glass is a one-step solution blending method that is performed by depositing only one layer of modified TiO₂ nanoparticles at room temperature. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to determine the structure and morphology of the nanoparticles and the thin-film-coated glass. The surface functional groups were investigated using Fourier-transform infrared spectroscopy (FT-IR), and the optical properties of the glass coating were measured using a UV/Vis spectrometer. The results revealed that the KH-500-modified TiO₂ film coating was in an anatase crystalline form. The hydrophilicity of the coated and uncoated glass substrates was observed by measuring their water contact angle (WCA) using a contact angle instrument. The maximum transparency of the coated glass measured in the visible region (380–780 nm) was approximately 70%, and it possessed excellent super-hydrophilic properties (WCA ~0°) at an annealing temperature of 350 °C without further need of UV or plasma treatment. These results demonstrate the super-hydrophilic coated glass surface has potential for use in self-cleaning and anti-fogging applications.

In this study, the friction and wear characteristics of polydimethylsiloxane (PDMS) were evaluated when using lubricants created by adding surfactants at various ratios to deionized (DI) water. When pure DI water is used as a lubricant, the repulsion of water from the hydrophobic PDMS surface is large and the interfacial affinity is low; thus, the lubrication properties cannot be significantly improved. However, when a lubricant with a surfactant is added to DI water, the interfacial affinity with the PDMS surface increases to form a lubricating film, and the friction coefficient is greatly reduced. In this study, under dry and pure DI water conditions, severe wear tracks were formed on the PDMS surface after 10,000 cycles of reciprocating sliding motion under a vertical load of 100 mN, whereas in the case of the surfactant-based and water-based lubricant, no severe wear tracks occurred. The friction and wear characteristics of the PDMS were evaluated by increasing the normal loads and sliding cycles with a water-based lubricant containing 1 wt % surfactant. Under normal loads of 300 mN and 500 mN, only minor scratches occurred on the PDMS surface up to 10,000 and 100,000 cycles, respectively, but after 300,000 cycles, very severe pit wear tracks occurred.