Ultrasonic shot peening (USP) is a surface treatment technology used in the mechanical properties strengthening of the engineering material and components during manufacturing. TC4 titanium alloy is a commonly used engineering material in the aerospace industry. In this study, a gradient nanostructured surface layer was successfully fabricated on the TC4 titanium alloy via USP technology at room temperature. The microstructure evolution of TC4 titanium alloy during USP was investigated. The surface microhardness was elevated from 330 HV to 438 HV with a penetrating depth of around 900 μm after USP with the duration of 8 min. EBSD characterization results confirmed the presence of high-density grain boundaries within the gradient structure in the region of 0–200 μm, accompanied by proliferation of dislocation density. TEM characterization indicated a substantial amount of nanograin with an average size of 74.58 nm. Furthermore, the USP process was also investigated by the finite element method to evaluate the surface-strengthening effect. The calculated maximum residual stress reached 973 MPa after multi-ball impact. The impact behavior of the shots during the USP process was studied. The effect of the parameters on the USP strengthening intensity was explored based on the validated model. This work provided a clearer understanding of the USP strengthening process of TC4 titanium alloy through an effective method of evaluating the process parameters.

Surface nanocrystallization of metals and alloys via high-frequency ultrasonic shot peening (USP) can significantly increase the mechanical properties of the materials. However, the relationship between the external process parameters and the internal microstructure of the materials is still unclear and an accurate numerical model to simulate the USP process is urgently required for better control of the grain refinement process. In this study, we successfully realized surface nanocrystallization of 316L stainless steel using USP with an ultrasonic frequency and amplitude of 20 kHz and 50 μm, respectively. The microstructure evaluation of 316L stainless steel during USP was revealed. We established a finite element numerical model to simulate the high-frequency USP process and calculated the plastic strain and stress distribution of 316L stainless steel during the grain refinement process. We investigated the effects of the ultrasonic frequency, working distance, and ultrasonic amplitude on the plastic strain and stress distribution on the materials using the finite element simulation method. The dynamic behavior of the shot during the USP process was studied using a high-speed camera, and the FE simulation results agreed well with the experimental results. We also investigated the impact of multiple shots during the USP process by the high-speed camera observation and FE simulation. Research results indicate that high-frequency USP is an effective method to obtain large-scale bulk nanocrystalline materials and the finite element simulation can help materials scientists and engineers to better understand the relationship between the process parameters and microstructure evaluation of 316L stainless steel.

High forming force is often needed when high-strength and low-plasticity materials are processed by fine blanking. Too high forming force increases the load of the die and greatly increases the risk of die failure. If the forming force is reduced, the material will fracture prematurely, which will lead to poor quality parts. Aiming at this problem, a new force variation load fine-blanking technology is proposed in this paper. During the loading process, the forming force does not remain constant but changes with the blanking stroke. A 2D finite element fine-blanking model was established for the TC4 material. The mechanism of force variation fine blanking is also revealed. This paper proposes a method to design the loading route of the forming force with variable load. This method combines finite element simulation with neural network and a multi-objective genetic algorithm. Finally, the application of variable load fine blanking production and the application of traditional fine blanking production parts are verified by the experimental method. The same results are obtained from both simulation and experiment. It is found that the variable load fine blanking process can greatly reduce the load of the die on the premise of ensuring the quality of fine-blanking parts.