A simple and green chemical method has been developed to synthesize stable bare and capped silver nanoparticles based on the reduction of silver ions by glucose and capping by poly(α,γ,l-glutamic acid) (PGA). The use of ammonia during synthesis was avoided. PGA has had a dual role in the synthesis and was used as a capping agent to make the silver nanoparticle more biocompatible and to protect the nanoparticles from agglomerating in the liquid medium. The synthesized PGA-capped silver nanoparticles in the size range 5–45 nm were stable over long periods of time, without signs of precipitation. Morphological examination has shown that the silver nanoparticles had a nearly spherical, multiply twinned structure. The effects of the reaction temperature and the reaction time during the synthesis were investigated too. The biocompatibility of the PGA-capped silver nanoparticles is discussed in terms of in vitro toxicity with human intestinal Caco-2 cells. The samples were characterized by UV–Visible spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, and zeta potential measurements.

Modified activated carbon cloth is prepared by mechanochemical modification of viscose rayon carbon cloth. The effects of different milling atmospheres, in the air and inert conditions, were investigated. Changes in kind and number of acidic and basic surface groups on the surface of activated carbon cloth, upon modification, as well as before and after the sorption of arsenic were determined. Higher number of basic groups responsible for the removal of arsenic ions was achieved by modification under inert conditions. Breakage and collapse of cylindrical fibers, decrease of particle sizes, change in the shape and consistency of the particles, as well as increase of microstructural disorder i.e. the loss of turbostratic structure occurred upon milling. pHPZC values increased from 4.46 to 5.04 and 5.77 after the air and inert milling, respectively. Adsorption followed pseudo second order kinetics with chemisorption as rate-controlling step. Langmuir isotherm best fit the equilibrium data and maximum adsorption capacity is 5.5mgg−1 at a pH value close to 7.0, typical for groundwater. The mechanism of arsenic adsorption onto activated carbon cloth milled in inert atmosphere involved electrostatic and dispersive interactions between arsenic ions and carbon particles in wide pH range (from 2 to 10)

The removal of Cs (I) ions from aqueous solution was studied using natural diatomite as adsorption materials originated from Rudovci, Serbia. The microstructure of natural diatomite has been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) while the degree of Cs adsorption was evaluated by atomic emission spectroscopy. The cation exchange capacity (CEC) values for natural diatomite was 50 meq/100g. Depending on whether the Cs adsorption occurred in the acidic and alkaline media at a temperature of 298.15 K in acidic media ?G0 values was -12.674 kJ/mol, while in alkaline media ?G0 was - 13.142 kJ/mol and a change of ?S0 to 42.51 J/molK in acidic media and 44.08 J/molK in alkaline medium.