The objective of this study was to review the scientific evidence currently available on 3D printable materials and 3D printing technologies used for the fabrication of permanent restorations, focusing on material properties that are clinically relevant. A literature search was performed on four databases (MEDLINE/PubMed, Scopus, Cochrane Library, Web of Science) for articles published from January 2013 until November 2023, using a combination of free words: (restorative dentistry OR prosthetic dentistry) AND (3D printing OR additive manufacturing OR rapid prototyping) AND materials. Two reviewers screened titles and/or abstracts of 2.468 unique studies. In total, 83 studies were selected for full-text reading, from which 36 were included in the review. The assessed variables were mechanical properties, reporting in most of the cases positive results, dimensional accuracy and fit, reporting conflicting results with a predominance of positive, aesthetic properties, with positive reports but scarcely addressed, and biological properties, almost unexplored in independent studies. Despite numerous studies with positive results in favor, papers with negative outcomes were also retrieved. Aesthetic and biological properties are conversely still mostly unexplored. There remains a lack of conclusive evidence for viable 3D printable restorative and prosthodontic materials for permanent restorations. Research should be strengthened by defining international standards for laboratory testing and, where pre-clinical data are promising, conducting clinical trials.

The aim of the study was to compare the translucency of CAD/CAM and printable composite materials for fixed dental prostheses (FDP). Eight A3 composite materials (7 CAD/CAM and 1 printable) for FPD were used to prepare a total of 150 specimens. CAD/CAM materials, all characterized by two different opacity levels, were: Tetric CAD (TEC) HT/MT; Shofu Block HC (SB) HT/LT; Cerasmart (CS) HT/LT; Brilliant Crios (BC) HT/LT; Grandio Bloc (GB) HT/LT; Lava Ultimate (LU) HT/LT, Katana Avencia (KAT) LT/OP. The printable system was Permanent Crown Resin. 1.0 mm-thick specimens were cut from commercial CAD/CAM blocks using a water-cooled diamond saw, or 3D printed. Measurements were performed using a benchtop spectrophotometer with an integrating sphere. Contrast Ratio (CR), Translucency Parameter (TP), and Translucency Parameter 00 (TP₀₀) were calculated. One Way ANOVA followed by Tukey test for post hoc were performed for each of the translucency system. The tested materials exhibited a wide range of translucency values. CR ranged from 59 to 84, TP from 15.75 to 8.96, TP₀₀ from 12.47 to 6.31. KAT(OP) and CS(HT) showed, respectively, the lowest and highest translucency for CR, TP and TP₀₀. Due to the significant range of reported translucency values, clinicians should exercise caution when choosing the most appropriate material, especially considering factors such as substrate masking, and the necessary clinical thickness.