This work presents a computational model to study the degradation behavior of polyester-based three-dimensional (3D) functionalized scaffolds for bone regeneration. As a case study, we investigated the behavior of a 3D-printed scaffold presenting a functionalized surface with ICOS-Fc, a bioactive protein able to stimulate bone regeneration and healing, inhibiting osteoclast activity. The aim of the model was to optimize the scaffold design to control its degradation and thus the release of grafted protein over time and space. Two different scenarios were considered: (i) a scaffold without macroporosity presenting a functionalized external surface; and (ii) a scaffold presenting an internal functionalized macroporous architecture with open channels to locally deliver the degradation products.

The application of mechanical stimulation on bone tissue engineering constructs aims to mimic the native dynamic nature of bone. Although many attempts have been made to evaluate the effect of applied mechanical stimuli on osteogenic differentiation, the conditions that govern this process have not yet been fully explored. In this study, pre-osteoblastic cells were seeded on PLLA/PCL/PHBV (90/5/5 wt.%) polymeric blend scaffolds. The constructs were subjected every day to cyclic uniaxial compression for 40 min at a displacement of 400 μm, using three frequency values, 0.5, 1, and 1.5 Hz, for up to 21 days, and their osteogenic response was compared to that of static cultures. Finite element simulation was performed to validate the scaffold design and the loading direction, and to assure that cells inside the scaffolds would be subjected to significant levels of strain during stimulation. None of the applied loading conditions negatively affected the cell viability. The alkaline phosphatase activity data indicated significantly higher values at all dynamic conditions compared to the static ones at day 7, with the highest response being observed at 0.5 Hz. Collagen and calcium production were significantly increased compared to static controls. These results indicate that all of the examined frequencies substantially promoted the osteogenic capacity.

Background: Recently, magnetic composite biomaterials have raised attention in bone tissue engineering as the application of dynamic magnetic fields proved to modulate the proliferation and differentiation of several cell types. Methods: This study presents a novel method to fabricate biofunctional magnetic scaffolds by the deposition of superparamagnetic iron oxide nanoparticles (SPIONs) through thermal Drop-On-Demand inkjet printing on three-dimensional (3D) printed scaffolds. Firstly, 3D scaffolds based on thermoplastic polymeric composed by poly-L-lactic acid/poly-caprolactone/poly(3-hydroxybutyrate-co-3-hydroxyvalerate) were fabricated by Fused Deposition Modelling. Then, in a second step, SPIONs were incorporated onto the surface of the scaffolds by inkjet printing following a designed 2D pattern. Results: A complete characterization of the resulting magnetic scaffolds was carried out attending to the surface SPIONs deposits, demonstrating the accuracy and versatility of the production technique, as well as the stability under physiological conditions and the magnetic properties. Biological evaluation with human bone marrow mesenchymal stems cells demonstrated biocompatibility of the scaffolds and increased osteogenic capability under the application of a magnetic field, due to the activation of mechanotransduction processes. Conclusion: These results show that the developed 3D magnetic biofunctional scaffolds can be a very promising tool for advanced and personalised bone regeneration treatments. Graphical