In tendon rupture repair, improvements such as higher primary repair strength, anti-adhesion and accelerated healing are needed. We developed a potential carrier system of an electrospun DegraPol® tube, which was tightly implanted around a transected and conventionally sutured rabbit Achilles tendon. Histomorphometric analysis of the tendon tissue 12 weeks postoperation showed that the tenocyte density, tenocyte morphology and number of inflammation zones were statistically equivalent, whether or not DegraPol tube was implanted; only the collagen fibres were slightly less parallelly orientated in the tube-treated case. Comparison of rabbits that were operated on both hind legs with ones that were operated on only one hind leg showed that there were significantly more inflammation zones in the two-leg cases compared to the one-leg cases, while the implantation of a DegraPol tube had no such adverse effects. These findings are a prerequisite for using DegraPol tube as a carrier system for growth factors, cytokines or stem cells in order to accelerate the healing process of tendon tissue. Copyright © 2012 John Wiley & Sons, Ltd.

Tendon injuries can result in two major drawbacks. Adhesions to the surrounding tissue may limit the range of motion, while fibrovascular scar formation can lead to poor biomechanical outcomes. Prosthetic devices may help to mitigate those problems. Emulsion electrospinning was used to develop a novel three-layer tube based on the polymer DegraPol (DP), with incorporated insulin-like growth factor-1 (IGF-1) in the middle layer. Scanning electron microscopy was utilized to assess the fiber diameter in IGF-1 containing pure DP meshes. Further characterization was performed with Fourier Transformed Infrared Spectroscopy, Differential Scanning Calorimetry, and water contact angle, as well as through the assessment of mechanical properties and release kinetics from ELISA, and the bioactivity of IGF-1 by qPCR of collagen I, ki67, and tenomodulin in rabbit Achilles tenocytes. The IGF-1-containing tubes exhibited a sustained release of the growth factor up to 4 days and showed bioactivity by significantly upregulated ki67 and tenomodulin gene expression. Moreover, they proved to be mechanically superior to pure DP tubes (significantly higher fracture strain, failure stress, and elastic modulus). The novel three-layer tubes intended to be applied over conventionally sutured tendons after a rupture may help accelerate the healing process. The release of IGF-1 stimulates proliferation and matrix synthesis of cells at the repair site. In addition, adhesion formation to surrounding tissue can be reduced due to the physical barrier.

Large bone defects after trauma demand for adequate bone substitutes. Bone void fillers should be antibacterial and pro-angiogenic. One viable option is the use of composite materials like the combination of PLGA and amorphous calcium phosphate (aCaP).

Human lung cancer ranks among the most frequently treated cancers worldwide. As copper appears critical to angiogenesis and tumor growth, selective removal of copper represents a promising strategy to restrict tumor growth. To this end, we explored the activity of the novel high-affinity membrane-permeant Cu(I) chelator PSP-2 featuring a low-zeptomolar dissociation constant. Using H460 human lung cancer cells, we generated small tumors on the chorioallantoic membrane of the chicken embryo (CAM assay) and studied the effects of topical PSP-2 application on their weight and vessel density after one week. We observed a significant angiosuppression along with a marked decrease in tumor weight under PSP-2 application compared to controls. Moreover, PSP-2 exposure resulted in lower ki67⁺ cell numbers at a low dose but increased cell count under a high dose. Moreover, HIF-1α⁺ cells were significantly reduced with low-dose PSP-2 exposure compared to high-dose and control. The total copper content was considerably lower in PSP-2 treated tumors, although statistically not significant. Altogether, PSP-2 shows promising potential as an anti-cancer drug. Nevertheless, further animal experiments and application to different tumor types are mandatory to support these initial findings, paving the way toward clinical trials.

Tendon ruptures are common musculoskeletal injuries associated with prolonged healing and complications such as adhesion formation and rerupture. Despite advancements in treatment strategies, full functional recovery remains a challenge. Growth factors (GFs) like insulin-like growth factor-1 (IGF-1) and platelet-derived growth factor-BB (PDGF-BB) play key roles in tendon repair and may have synergistic effects when applied together. To support tendon healing, a bioactive electrospun polymer scaffold made of Degrapol^® (DP) was developed, incorporating IGF-1, PDGF-BB, or both. A range of in vitro and in vivo analyses were performed to assess scaffold structure, cell behavior, gene expression, metabolism, and biomechanical and adhesion outcomes three weeks post-surgery. Interestingly, the combined application of IGF-1 and PDGF-BB did not simply amplify individual effects but showed a complex interaction. Depending on the parameter and time point, the combination led to either enhanced or reduced responses compared to single-factor treatments, indicating a synergistic modulation rather than a purely additive effect. These findings suggest that the combination of IGF-1 and PDGF-BB can modulate key cellular and molecular processes in tendon regeneration, making this approach a promising strategy to improve tendon healing.

A major problem after tendon injury is adhesion formation to the surrounding tissue leading to a limited range of motion. A viable strategy to reduce adhesion extent is the use of physical barriers that limit the contact between the tendon and the adjacent tissue. The purpose of this study was to fabricate an electrospun bilayered tube of hyaluronic acid/polyethylene oxide (HA/PEO) and biodegradable DegraPol® (DP) to improve the anti-adhesive effect of the implant in a rabbit Achilles tendon full laceration model compared to a pure DP tube. Additionally, the attachment of rabbit tenocytes on pure DP and HA/PEO containing scaffolds was tested and Scanning Electron Microscopy, Fourier-transform Infrared Spectroscopy, Differential Scanning Calorimetry, Water Contact Angle measurements, and testing of mechanical properties were used to characterize the scaffolds. In vivo assessment after three weeks showed that the implant containing a second HA/PEO layer significantly reduced adhesion extent reaching levels comparable to native tendons, compared with a pure DP implant that reduced adhesion formation only by 20 %. Tenocytes were able to attach to and migrate into every scaffold, but cell number was reduced over two weeks. Implants containing HA/PEO showed better mechanical properties than pure DP tubes and with the ability to entirely reduce adhesion extent makes this implant a promising candidate for clinical application in tendon repair.