Friction stir spot welding is an emerging spot-welding technology that offers opportunities for joining a wide range of materials with minimum energy consumption. To increase productivity, the present work addresses production challenges and aims to find solutions for the lap-welding of multiple ultrathin sheets with maximum productivity. Two convex tools with different edge radii were used to weld four ultrathin sheets of AA5754-H111 alloy each with 0.3 mm thickness. To understand the influence of tool geometries and process parameters, coefficient of friction (CoF), microstructure and mechanical properties obtained with the Vickers microhardness test and the small punch test were analysed. A scanning acoustic microscope was used to assess weld quality. It was found that the increase of tool radius from 15 to 22.5 mm reduced the dwell time by a factor of three. Samples welded with a specific tool were seen to have no delamination and improved mechanical properties due to longer stirring time. The rotational speed was found to be the most influential parameter in governing the weld shape, CoF, microstructure, microhardness and weld efficiency. Low rotational speeds caused a 14.4% and 12.8% improvement in joint efficiency compared to high rotational speeds for both tools used in this investigation.

Bobbin tool friction stir welding (BTFSW) is a variant of the FSW process which uses the special two-shoulder tool that forms the top and bottom of a weld surface. As such, a significant simplification of the welding setup is achieved. One of the dominant parameters of the BTFSW process is the interference between the tool shoulder pinch gap and the weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact, and bend performance were studied, and appropriate correlations were devised. The base metal was an aluminum–magnesium alloy in which the interference varied in the range of 0.1 to 0.5 mm. Wormhole defects and irregularities were found in all specimens except in the specimen welded with 0.4 mm interference. An optimal interference of 0.4 mm resulted in the best mechanical properties, which, in terms of tensile strength and reduction of area, were similar to the base metal. Furthermore, the impact strength was significantly higher, which was attributed to the grain refinement effect in the nugget zone.

Hardfacing is a welding-related technique aimed at depositing a harder and tougher layer onto a softer, less wear-resistant substrate or base metal. This process enhances the abrasion resistance of the component, increasing its durability under working conditions. A key feature of hardfacing is dilution, which refers to the mixing of the hardfacing layer and the base metal. In this study, shielded metal arc welding (SMAW) was employed to hardface structural steel using chromium carbide vanadium consumables, with results compared to AISI D2 cold-work tool steel. Four different SMAW parameters were tested, and the abrasive test was conducted against SiC discs. Wear rate, represented by the wear loss rate, was correlated to microstructure, scanning electron microscopy, energy-dispersive X-ray spectroscopy, hardness, microhardness, and surface roughness. The results showed that key SMAW parameters, such as welding speed and current, significantly influence wear resistance. Specifically, slower welding speeds and higher currents, which result in greater heat input, led to the increased wear resistance of the deposited layer through the mechanism of the inoculation of larger and harder carbides.

Bobbin tool friction stir welding (BTFSW) utilizes a special tool that possesses two shoulders interconnected by a pin instead of one: the top shoulder and the pin in the conventional FSW tool. This greatly simplifies the kinematics in the otherwise complicated setup of FSW since the bottom shoulder forms the bottom surface of the weld, without the need for a backing plate. Moreover, the tool enters the base metal sideways and travels, forming the joint in a straight line while rotating, without the need for downward and upward motion at the beginning and end of the process. This paper presents a study on the BTFSW tool geometry and parameters on the risk of wormhole defect formation in the AA5005 aluminum–magnesium alloy and the wormhole effect on mechanical properties. It was shown that higher stress imposed by the tool geometry on the joint has a significant influence on heating, an effect similar to the increased rotational speed. Optimal kinematic and geometrical tool properties are required to avoid wormhole defects. Although weld tensile strengths were lower (between ~111 and 115 MPa) compared with a base metal (137 MPa), the ductile fracture was obtained. Furthermore, all welds had a higher impact strength (between ~20.7 and 27.8 J) compared with the base material (~18.5 J); it was found that the wormhole defect only marginally influences the mechanical properties of welds.

Bobbin Tool Friction Stir Welding (BTFSW) is a variant of FSW process using the special two shoulder tool that forms the top and bottom weld surface. As such, a significant simplification of welding setup is achieved. One of the dominant parameters of BTFSW process is the interference between tool shoulder pinch gap and weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact and bend performance were studied, and appropriate correlations were devised. The base metal was aluminum-magnesium alloy, with the interference varied in the range of 0.1 to 0.5 mm. The worm defects and irregularities were found in all specimens except in specimen welded with 0.4 mm interference. Optimal interference of 0.4 mm resulted in the highest mechanical properties, which, in terms of tensile strength and reduction of area were similar to the base metal. Furthermore, impact strength was significantly higher, which was attributed to grain refinement effect in the nugget zone.