Dental remineralization represents the process of depositing calcium and phosphate ions into crystal voids in demineralized enamel, producing net mineral gain and preventing early enamel lesions progression. The aim of the present study was to qualitatively and quantitatively compare the remineralizing effectiveness of four commercially available agents on enamel artificial lesions using Scanning Electron Microscopy (SEM) combined with Energy Dispersive Spectroscopy (EDS) techniques. Thirty-six extracted third molars were collected and randomly assigned to six groups (n = 6), five of which were suspended in demineralizing solution for 72 h to create enamel artificial lesions, and one serving as control: G1, treated with a mousse of casein phosphopeptide and amorphous calcium–phosphate (CPP-ACP); G2, treated with a gel containing nano-hydroxyapatite; G3, treated with a 5% SF varnish; G4, treated with a toothpaste containing ACP functionalized with fluoride and carbonate-coated with citrate; G5, not-treated artificial enamel lesions; G6, not demineralized and not treated sound enamel. G1–G4 were subjected to pH cycling over a period of seven days. Analyses of the specimens’ enamel surfaces morphology were performed by SEM and EDS. Data were statistically analyzed for multiple group comparison by one-way ANOVA/Tukey’s test (p < 0.05). The results show that the Ca/P ratio of the G5 (2.00 ± 0.07) was statistically different (p < 0.05) from G1 (1.73 ± 0.05), G2 (1.76 ± 0.01), G3 (1.88 ± 0.06) and G6 (1.74 ± 0.04), while there were no differences (p > 0.05) between G1, G2 and G6 and between G4 (2.01 ± 0.06) and G5. We concluded that G1 and G2 showed better surface remineralization than G3 and G4, after 7 days of treatment.

Cellularized scaffold is emerging as the preferred solution for tissue regeneration and restoration of damaged functionalities. However, the high cost of preclinical studies creates a gap between investigation and the device market for the biomedical industry. In this work, bone-tailored scaffolds based on the Ti6Al4V alloy manufactured by electron beam melting (EBM) technology with reused powder were investigated, aiming to overcome issues connected to the high cost of preclinical studies. Two different elementary unit cell scaffold geometries, namely diamond (DO) and rhombic dodecahedron (RD), were adopted, while surface functionalization was performed by coating scaffolds with single layers of polycaprolactone (PCL) or with mixture of polycaprolactone and 20 wt.% hydroxyapatite (PCL/HA). The mechanical and biological performances of the produced scaffolds were investigated, and the results were compared to software simulation and experimental evidence available in literature. Good mechanical properties and a favorable environment for cell growth were obtained for all combinations of scaffold geometry and surface functionalization. In conclusion, powder recycling provides a viable practice for the biomedical industry to strongly reduce preclinical costs without altering biomechanical performance.

This study aimed to compare two different bulk-filling techniques, evaluating the internal and external adaptation of class II resin-composite restorations, by analysing the gap formation using microcomputed tomography (µ-CT) and scanning electronic microscopy (SEM) coupled with energy-dispersive X-ray spectroscopy (EDS). Two standardized mesio/disto-occlusal (MO/DO) cavities were prepared in eight extracted human third molars that were divided, according to the filling technique used, in the following two groups (n = 4): BG (Bulk&Go group) and BT (Bulk Traditional group). After universal bonding application, followed by the light curing, all teeth were restored using a bulk-fill composite. Specimens were scanned with µ-CT to evaluate 3D interfacial gaps. Acquired µ-CT data were analysed to quantify the gap formation. Complementary information to the µ-CT analysis were obtained by SEM. Thereafter, the chemical composition of tooth–restoration interface was analysed using EDS. The µ-CT analysis revealed gaps formation at the tooth–restoration interface for both the BG and BT groups, while within the restoration, only in the BT group there was evidence of microleakage formation. The scanning electron micrographs of both groups showed that the external marginal integrity of the restoration was preserved, while EDS showed the three different structures (tooth surface, adhesive layer and resin composite) of the tooth–restoration interface, highlighting the absence of gap formation. In both BG and BT, the two filling techniques did not show significant differences regarding the internal and external marginal adaptation of the restoration. To achieve a successful restoration, the clinician could be advised to restore a class II cavity using a single increment bulk-filling technique (BG), thus treating it as a class I cavity.

The austenitic stainless steels utilized in the production of osteosynthesis devices are susceptible to crevice corrosion. Several studies have compared the corrosive behavior of austenitic and duplex stainless steels (DSS), both of which are recognized as viable biomaterials for tissue engineering applications. All of the in vitro and in vivo studies on animals and clinical results reported to date indicate that austeno-ferritic duplex stainless steel can be recommended as a suitable alternative to ASTM F138 steel, since it is resistant to crevice corrosion in the human body and presents superior mechanical properties. The use of DSS for biomedical applications is still under discussion, mainly due to the lack of knowledge of its behavior in terms of device heating or induced movement when exposed to magnetic fields, a potentially harmful effect for the human body. As a breakthrough production technology, additive manufacturing (AM) has demonstrated significant benefits for the fabrication of metal devices with patient-specific geometry. Laser powder bed fusion has particularly been used to manufacture DSS-based components. A fine control of the processing conditions allows for an understanding of DSS microstructural evolution, which is essential for selecting processing parameters and estimating performance, including mechanical properties and corrosion resistance. Furthermore, scientific investigation is necessary for determining the relationships among material, process, and magnetic properties, in order to establish the underlying principles and critical responses. The purpose of this review is to highlight the key performances of DSS for biomedical applications and to point out the relevant role of advanced processing technologies such as additive manufacturing.

Graded lattice scaffolds based on rhombic dodecahedral (RD) elementary unit cell geometry were manufactured in 316L stainless steel (SS) by laser powder bed fusion (LPBF). Two different strategies based on varying strut thickness layer-by-layer in the building direction were adopted to obtain the graded scaffolds: a) decreasing strut size from core to edge to produce the dense-in (DI) structure and b) increasing strut size in the same direction to produce the dense-out (DO) structure. Both graded structures (DI and DO) were constructed with specular symmetry with respect to the central horizontal axis. Structural, mechanical, and biological characterizations were carried out to evaluate feasibility of designing appropriate biomechanical performances of graded scaffolds in the perspective of bone tissue regeneration. Results showed that mechanical behavior is governed by graded geometry, while printing parameters influence structural properties of the material such as density, textures, and crystallographic phases. The predominant failure mechanism in graded structures initiates in correspondence of thinner struts, due to high stress concentrations on strut junctions. Biological tests evidenced better proliferation of cells in the DO graded scaffold, which in turn exhibits mechanical properties close to cortical bone. The combined control of grading strategy, printing parameters and elementary unit cell geometry can enable implementing scaffolds with improved biomechanical performances for bone tissue regeneration.