Fiber glass waste (FGW) was subjected to alkali activation in an aqueous solution with different concentrations of sodium/potassium hydroxide. The activated materials were fed into a methane–oxygen flame with a temperature of around 1600 °C. X-ray diffraction analysis confirmed the formation of several hydrated compounds, which decomposed upon flame synthesis, leading to porous glass microspheres (PGMs). Pore formation was favored by using highly concentrated activating alkali solutions. The highest homogeneity and yield of PGMs corresponded to the activation with 9 M KOH aqueous solution.

Additive manufacturing (AM) technologies enable the fabrication of objects with complex geometries in much simpler ways than conventional shaping methods. With the fabrication of recyclable filters for contaminated waters, the present work aims at exploiting such features as an opportunity to reuse glass from discarded pharmaceutical containers. Masked stereolithography-printed scaffolds were first heat-treated at relatively low temperatures (680 and 730 °C for 1 h) and then functionalized by alkali activation, with the formation of zeolite and sodium carbonate phases, which worked as additional adsorbing centers. As-sintered and activated scaffolds were characterized in terms of the efficiency of filtration and removal of methylene blue, used as a reference dye. The adsorption efficiency of activated printed glass was 81%. The 3D-printed adsorbent can be easily separated from the solution for reuse.

Novel and eco-friendly solutions are extensively needed for wastewater treatment. This work capitalizes on the combination of waste vitrification and additive manufacturing to produce an efficient photocatalyst for the specific purpose. Fine powders of waste-derived glass, containing Fe3O4 inclusions, by simple suspension (for a solid loading of 65 wt %) in alkaline solution (5 M NaOH), were transformed into pastes for direct ink writing. 3D-printed reticulated scaffolds were stabilized by the progressive hardening of a zeolite-like gel, formed by glass/solution interaction, at nearly room temperature. The printed scaffolds were successfully tested for the removal of methylene blue, realized by combining the high sorption capacity of the gel with the catalytic activity of magnetite inclusions, under UV light. A complete degradation of methylene blue is achieved by 90 min exposure, comparing favorably with other reported photocatalytic materials, requiring from 60 to 360 min. The photocatalytic activity was tested for several cycles, with no significant degradation. In other words, a waste-derived material can be reused for multiple times, to remediate wastewaters, with evident benefits on waste minimization.