The building industry, which emits a significant quantity of greenhouse gases, is under tremendous pressure due to global climate change and its consequences for communities. Given the environmental issues associated with cement production, geopolymer concrete has emerged as a sustainable construction material. Geopolymer concrete is an eco-friendly construction material that uses industrial or agricultural by-product ashes as the principal binder instead of Portland cement. Fly ash, ground granulated blast furnace slag, rice husk ash, metakaolin, and palm oil fuel ash were all employed as binders in geopolymer concrete, with fly ash being the most frequent. The most important engineering property for all types of concrete composites, including geopolymer concrete, is the compressive strength. It is influenced by different parameters such as the chemical composition of the binder materials, alkaline liquid to binder ratio, extra water content, superplasticizers dosages, binder content, fine and coarse aggregate content, sodium hydroxide and sodium silicate content, the ratio of sodium silicate to sodium hydroxide, the concentration of sodium hydroxide (molarity), curing temperature, curing durations inside oven, and specimen ages. In order to demonstrate the effects of these varied parameters on the compressive strength of the fly ash-based geopolymer concrete, a comprehensive dataset of 800 samples was gathered and analyzed. According to the findings, the curing temperature, sodium silicate content, and alkaline solution to binder ratio are the most significant independent parameters influencing the compressive strength of the fly ash-based geopolymer concrete (FA-BGPC) composites.

Geopolymer (GP) concrete is a novel construction material that can be used in place of traditional Portland cement (PC) concrete to reduce greenhouse gas emissions and effectively manage industrial waste. Fly ash (FA) has long been utilized as a key constituent in GPs, and GP technology provides an environmentally benign alternative to FA utilization. As a result, a thorough examination of GP concrete manufactured using FA as a precursor (FA-GP concrete) and employed as a replacement for conventional concrete has become crucial. According to the findings of current investigations, FA-GP concrete has equal or superior mechanical and physical characteristics compared to PC concrete. This article reviews the clean production, mix design, compressive strength (CS), and microstructure (Ms) analyses of the FA-GP concrete to collect and publish the most recent information and data on FA-GP concrete. In addition, this paper shall attempt to develop a comprehensive database based on the previous research study that expounds on the impact of substantial aspects such as physio-chemical characteristics of precursors, mixes, curing, additives, and chemical activation on the CS of FA-GP concrete. The purpose of this work is to give viewers a greater knowledge of the consequences and uses of using FA as a precursor to making effective GP concrete.