The safe disposal of an enormous amount of waste glass (WG) in several countries has become a severe environmental issue. In contrast, concrete production consumes a large amount of natural resources and contributes to environmental greenhouse gas emissions. It is widely known that many kinds of waste may be utilized rather than raw materials in the field of construction materials. However, for the wide use of waste in building construction, it is necessary to ensure that the characteristics of the resulting building materials are appropriate. Recycled glass waste is one of the most attractive waste materials that can be used to create sustainable concrete compounds. Therefore, researchers focus on the production of concrete and cement mortar by utilizing waste glass as an aggregate or as a pozzolanic material. In this article, the literature discussing the use of recycled glass waste in concrete as a partial or complete replacement for aggregates has been reviewed by focusing on the effect of recycled glass waste on the fresh and mechanical properties of concrete.

Geopolymer (GP) concrete is a novel construction material that can be used in place of traditional Portland cement (PC) concrete to reduce greenhouse gas emissions and effectively manage industrial waste. Fly ash (FA) has long been utilized as a key constituent in GPs, and GP technology provides an environmentally benign alternative to FA utilization. As a result, a thorough examination of GP concrete manufactured using FA as a precursor (FA-GP concrete) and employed as a replacement for conventional concrete has become crucial. According to the findings of current investigations, FA-GP concrete has equal or superior mechanical and physical characteristics compared to PC concrete. This article reviews the clean production, mix design, compressive strength (CS), and microstructure (Ms) analyses of the FA-GP concrete to collect and publish the most recent information and data on FA-GP concrete. In addition, this paper shall attempt to develop a comprehensive database based on the previous research study that expounds on the impact of substantial aspects such as physio-chemical characteristics of precursors, mixes, curing, additives, and chemical activation on the CS of FA-GP concrete. The purpose of this work is to give viewers a greater knowledge of the consequences and uses of using FA as a precursor to making effective GP concrete.

Lightweight foamed concrete is a type of concrete characterized by light in self-weight, self-compaction, self-leveling, thermal isolation, and a high ratio of weight to strength. The advantages of GFRP bars include lightweight, high longitudinal tensile strength, non-conductivity, and resistance to corrosion. This study investigated the behavior of LWFC beams reinforced with GFRP bars under flexural loading. A total of four reinforced concrete beams were cast, where it consisted of two LWFC beams and two normal weight concrete beam which acted as control specimen. One of the lightweight foamed concrete beams and the normal concrete beams is reinforced with two GFRP bars and the other reinforced with two steel bars. All beams were designed with singly reinforced of two bars of diameter 12mm. The LWFC beams were with cement to sand ratio (1:1) and average dried density of 1800± kg/m^3. The main variables considered in this study was type of concrete and type of reinforcement. The flexural parameters investigated are ultimate load, crack width, ductility, deflection and stiffness. The lightweight foamed concrete beam reinforced with GFRP bars showed deflection and crack width greater than in beam reinforced with steel bars due to the low modulus of elasticity of GFRP bars.

Textile reinforced concrete (TRC) has gained attention from the construction industry due to several characteristics such as its lightweight, high tensile strength, design flexibility, corrosion resistance and remarkably long service life. Some structural applications that utilize TRC components include precast panels, structural repairs, waterproofing elements and façades. TRC is produced by incorporating textile fabrics into thin cementitious concrete panels. However, in order to use this strengthening method in construction practice, a design model is required. Investigating the combined effect of conventional steel and textile reinforcement on the ductility behavior of composite TRC/RC one-way slab is vitally important. Therefore, the current study describes the proper methods of calculating the ductility of the composite concrete reinforced by a direct combination of conventional steel and textile reinforcement. Four methods are presented to calculate the ductility of the three considered one-way slab specimens. The three slabs having dimensions 1500 mm × 500 mm × 50 mm were reinforced by steel bars (SRC), by steel with one layer of carbon fabric (SRC + 1T), and by steel with two layers of carbon fabric (SRC + 2T). The three slab specimens were cast by the hand lay-up method, removed from the molds, cured, and then tested in flexure after 28 days using the four-point bending method. The obtained results and calculations revealed the non-reasonability of using the conventional method based on yielding of steel reinforcement as the only criterion in the ductility determination. The results also confirmed the suitability of using the energy-based method over other discussed methods in the calculation of the ductility for the hybrid reinforced members.