The scientific literature regarding additive manufacturing, mainly the material extrusion method, suggests that the mechanical characteristics of the parts obtained by this technology depend on a number of the input factors specific to the printing process, such as printing temperature, printing trajectory, layer height, etc., and also on the post-process operations for parts, which, unfortunately, requires supplementary setups, equipment, and multiple steps that raise the overall costs. Therefore, this paper aims to investigate the influence of the printing direction, the thickness of the deposited material layer, and the temperature of the previously deposited material layer on the part tensile strength, hardness by means of Shore D and Martens hardness, and surface finish by using an in-process annealing method. A Taguchi L9 DOE plan was developed for this purpose, where the test specimens, with dimensions according to ISO 527-2 type B, were analysed. The results showed that the presented in-process treatment method is possible and could lead to sustainable and cost-effective manufacturing processes. The varied input factors influenced all the studied parameters. Tensile strength tended to increase, up to 12.5%, when the in-process heat treatment was applied, showed a positive linear variation with nozzle diameter, and presented considerable variations with the printing direction. Shore D and Martens hardness had similar variations, and it could be observed that by applying the mentioned in-process heat treatment, the overall values tended to decrease. Printing direction had a negligible impact on the additively manufactured parts’ hardness. At the same time, the nozzle diameter presented considerable variations, up to 36% for Martens hardness and 4% for Shore D, when higher diameter nozzles were used. The ANOVA analysis highlighted that the statistically significant factors were the nozzle diameter for the part’s hardness and the printing direction for the tensile strength.

The paper investigates the influence of some 3D printing conditions on some physical–mechanical and technological properties of polycaprolactone (PCL) wood-based biopolymer parts manufactured by FDM. Parts with 100% infill and the geometry according to ISO 527 Type 1B were printed on a semiprofessional desktop FDM printer. A full factorial design with three independent variables at three levels was considered. Some physical–mechanical properties (weight error, fracture temperature, ultimate tensile strength) and technological properties (top and lateral surface roughness, cutting machinability) were experimentally assessed. For the surface texture analysis, a white light interferometer was used. Regression equations for some of the investigated parameters were obtained and analysed. Higher printing speeds than those usually reported in the existing literature dealing with wood-based polymers’ 3D printing had been tested. Overall, the highest level chosen for the printing speed positively influenced the surface roughness and the ultimate tensile strength of the 3D-printed parts. The cutting machinability of the printed parts was investigated by means of cutting force criteria. The results showed that the PCL wood-based polymer analysed in this study had lower machinability than natural wood.

The present paper aims to contribute to the methodology of 3D printing in-process colouring and study its implications and impact on the tensile strength and surface quality of the obtained parts. The proposed study was based on a Taguchi L27 DOE plan using standardised EN ISO 527-2 type 1B-shaped specimens, in which four factors on three levels were considered. The obtained results highlight the possibility of using the presented in-process colouring method. Different materials (PLA, PLA+, and PETG) with varying infill densities (15%, 30%, and 50%), colour distribution (33%, 66%, and 99%), and colour pigments (blue, green, and red) were studied and the results highlighted that the most influential parameter on the tensile strength of the parts was infill density, followed by the tested material, colour pigment, and colouring percentage; regarding surface roughness, the most influential parameter was infill density, followed by colouring percentage, colour pigment, and material. Moreover, the values resulting from the Taguchi DOE were compared to uncoloured parts, from which it could be concluded that the colouring of the parts had direct implications (negative for tensile strength and positive for surface roughness).

Continuous research in the field of metal additive manufacturing has led to the need for constant improvement of manufacturing parameters especially in the case of FDM (Fused Deposition Modeling) manufacturing. In recent years, the main directions outlined for productivity and quality improvement were related to higher printing speed and the use of ironing-type processes. This article aims to study the manufacturing parameters of the dimensional accuracy and surface quality of FDM-manufactured 316L stainless steel. The degree of novelty is given by the application of the ironing process for the green part. A full factorial 3³ experimental design was designed for this study, in which the factors studied were ironing angle, ironing speed, and layer spacing during ironing. The dimensional accuracy and surface roughness were analyzed by means of deviation measurement from CAD to the green part and final part after the sintering process. Using the design of experiments offers the possibility of applying the analysis of variance (ANOVA) which provides information about the degree of influence of each of the studied factors. The results obtained for the dimensional accuracy showed that the ironing direction had the biggest influence on the Z-axis shrinkage. Overall, approximately 6% shrinkage in the Z and Y directions was obtained while in the X directions, the shrinkage percentage was around 20%. Surface roughness showed an improvement with higher ironing speeds for the green part while for the sintered part the most significant factor was ironing spacing.

The study investigates some 3D printing output parameters of a polycaprolactone (PCL) wood‐based biopolymer, a category of materials obtained by embedding wood‐derived components within polymeric matrices. These wood‐based biopolymers have garnered significant focus in recent years due to their environmental friendliness and vast potential across many different fields. A full factorial design with three independent variables (layer height, printing speed, and heat treatment exposure time) at three levels was considered. The research explores printing speeds higher than the speed ranges typically investigated in the existing scientific literature on FDM 3D printing of wood‐based polymers. Additionally, in this study, heat treatment is proposed as a post‐processing operation to enhance certain crucial proprieties such as surface quality, hardness, mechanical strength, and accuracy. The findings reveal that heat treatment has a positive influence on the investigated output parameters. Notably, 3D printed samples subjected to heat treatment exhibit an average decrease of 112.1% in surface roughness for a 5‐min exposure time and 121.73% for a 10‐min exposure time. The surface hardness of the samples also improved after applying the heat treatment. The part hardness improved with an average of 0.65%. Furthermore, significant correlations were observed between layer height and surface quality, hardness, printing speed, and tensile strength. Notably, printing speed contributed significantly to the variation in tensile strength, accounting for 52.77% of the parameter’s variation. These insights shed light on the optimization of 3D printing processes for wood‐based biopolymers, paving the way for enhanced performance and applicability across diverse fields.