In the case of workpieces made of difficult-to-cut materials, the small-diameter holes (1 mm diameter below) can be obtained by means of various nonconventional machining methods, one of these being the hybrid electrochemical discharge machining (ECDM). In the literature they researched, the authors could not find enough information that would allow them to establish adequate work conditions for the ECDM of small diameter holes by using an electrolyte. The use of a spring in order to obtain the work motion required to drill thin workpieces, and the need to remove the insulating film appearing on the workpiece, including in the last stage of the machining, were considered. The experimental research ended in the development of a power type function, which emphasizes the influence of the electrode tool diameter, of the voltage applied to the electrodes, of the capacity of the electric circuit involved in obtaining the electrical discharges, and of the density of the electrolyte upon the absolute axial wear of the electrode tool.

Wire electrical discharge machining has appeared mainly in response to the need for detachment with sufficiently high accuracy of parts of plate-type workpieces. The improvements introduced later allowed the extension of this machining technology to obtain more complex ruled surfaces with increasingly high requirements regarding the quality of the machined surfaces and the productivity of the wire electrical discharge machining process. Therefore, it was normal for researchers to be interested in developing more and more in-depth investigations into the various aspects of wire electrical discharge machining. These studies focused first on improving the machining equipment, wire electrodes, and the devices used to position the clamping of a wire electrode and workpiece. A second objective pursued was determining the most suitable conditions for developing the machining process for certain proper situations. As output parameters, the machining productivity, the accuracy, and roughness of the machined surfaces, the wear of the wire electrode, and the changes generated in the surface layer obtained by machining were taken into account. There is a large number of scientific papers that have addressed issues related to wire electrical discharge machining. The authors aimed to reveal the aspects that characterize the process, phenomena, performances, and evolution trends specific to the wire electrical discharge machining processes, as they result from scientific works published mainly in the last two decades.

The thermal properties of parts obtained by 3D printing from polymeric materials may be interesting in certain practical situations. One of these thermal properties is the ability of a material to expand as the temperature rises or shrink when the temperature drops. A test experiment device was designed based on the thermal expansion or negative thermal expansion of spiral test samples, made by 3D printing of polymeric materials to investigate the behavior of some polymeric materials in terms of thermal expansion or contraction. A spiral test sample was placed on an aluminum alloy plate in a spiral groove. A finite element modeling highlighted the possibility that areas of the plate and the spiral test sample have different temperatures, which means thermal expansions or contractions have different values in the spiral areas. A global experimental evaluation of four spiral test samples was made by 3D printing four distinct polymeric materials: styrene-butadiene acrylonitrile, polyethylene terephthalate, thermoplastic polyurethane, and polylactic acid, has been proposed. The mathematical processing of the experimental results using specialized software led to establishing empirical mathematical models valid for heating the test samples from −9 °C to 13 °C and cooling the test samples in temperature ranges between 70 °C and 30 °C, respectively. It was found that the negative thermal expansion has the highest values in the case of polyethylene terephthalate and the lowest in the case of thermoplastic polyurethane.

The paper investigates the influence of some 3D printing conditions on some physical–mechanical and technological properties of polycaprolactone (PCL) wood-based biopolymer parts manufactured by FDM. Parts with 100% infill and the geometry according to ISO 527 Type 1B were printed on a semiprofessional desktop FDM printer. A full factorial design with three independent variables at three levels was considered. Some physical–mechanical properties (weight error, fracture temperature, ultimate tensile strength) and technological properties (top and lateral surface roughness, cutting machinability) were experimentally assessed. For the surface texture analysis, a white light interferometer was used. Regression equations for some of the investigated parameters were obtained and analysed. Higher printing speeds than those usually reported in the existing literature dealing with wood-based polymers’ 3D printing had been tested. Overall, the highest level chosen for the printing speed positively influenced the surface roughness and the ultimate tensile strength of the 3D-printed parts. The cutting machinability of the printed parts was investigated by means of cutting force criteria. The results showed that the PCL wood-based polymer analysed in this study had lower machinability than natural wood.