The estimation of the size and location of defects in multi-layered composite structures by ultrasonic non-destructive testing using guided waves has attracted the attention of researchers for the last few decades. Although extensive signal processing techniques are available, there are only a few studies available based on image processing of the ultrasonic B-scan image to extract the size and location of defects via the process of ultrasonic non-destructive testing. This work presents an image processing technique for ultrasonic B-scan images to improve the estimation of the location and size of disbond-type defects in glass fiber-reinforced plastic materials with 25-mm and 51-mm diameters. The sample is a segment of a wind turbine blade with a variable thickness ranging from 3 to 24 mm. The experiment is performed by using a low-frequency ultrasonic system and a pair of contact-type piezoceramic transducers kept apart by a 50-mm distance and embedded on a moving mechanical panel. The B-scan image acquired by the ultrasonic pitch-catch technique is denoised by utilizing features of two-dimensional discrete wavelet transform. Thereafter, the normalized pixel densities are compared along the scanned distance on the region of interest of the image, and a −3 dB threshold is applied to the locations and sizes the defects in the spatial domain.

The reliability of the wind turbine blade (WTB) evaluation using a new criterion is presented in the work. Variation of the ultrasonic guided waves (UGW) phase velocity is proposed to be used as a new criterion for defect detection. Based on an intermediate value between the maximum and minimum values, the calculation of the phase velocity threshold is used for defect detection, location and sizing. The operation of the proposed technique is verified using simulation and experimental studies. The artificially milled defect having a diameter of 81 mm on the segment of WTB is used for verification of the proposed technique. After the application of the proposed evaluation technique for analysis of the simulated B-scan image, the coordinates of defect edges have been estimated with relative errors of 3.7% and 3%, respectively. The size of the defect was estimated with a relative error of 2.7%. In the case of an experimentally measured B-scan image, the coordinates of defect edges have been estimated with relative errors of 12.5% and 3.9%, respectively. The size of the defect was estimated with a relative error of 10%. The comparative results obtained by modelling and experiment show the suitability of the proposed new criterion to be used for the defect detection tasks solving.

This research utilizes Ultrasonic Guided Waves (UGW) to inspect corrosion-type defects in steel pipe walls, providing a solution for hard-to-reach areas typically inaccessible by traditional non-destructive testing (NDT) methods. Fundamental helical UGW modes are used, allowing the detection of defects anywhere on the pipe’s circumference using a limited number of transducers and measurements on the upper side of the pipe. Finite element (FE) modeling and experiments investigated generating and receiving UGW helical waves and their propagation through varying corrosion-type defects. Defect detection is based on phase delay differences in the helical wave’s signal amplitude peaks between defective and defect-free regions. Phase delay variations were noted for the different depths and spatial dimensions of the defects. These results highlight the phase delay method’s potential for NDT pipeline inspection.

In this study, a new method for determining the elastic constants of isotropic plates using Lamb wave fundamental modes is presented. This method solves the inverse problem, where the elastic constants (Young’s modulus and Poisson’s ratio) of the plate were estimated by measuring the phase velocities of the Lamb wave using the Rayleigh–Lamb equations to find the solution and determining the phase velocities of the A₀ and S₀ modes using a new method. The suitability of the proposed method for determining the elastic constants was evaluated using simulated and experimental signals propagating on an aluminum plate. The theoretical modeling on the aluminum 7075-T6 plate shows that the proposed method allows the determination of the Poisson ratio with a relative error not exceeding 2% and Young’s modulus with a relative error not exceeding 0.5%. The experimental measurements of an aluminum plate of known thickness (2 mm) and density (2685 kg/m³) confirmed the suitability of the proposed method for the measurements of elastic constants. In the proposed method, the processing of ultrasonic signals can be performed in real-time, and the values of the elastic constants can be obtained immediately after scanning the required distance.

Ultrasonic guided waves are already used for material characterization. The advantage of these waves is that they propagate in the plane of a plate and their propagation characteristics are sensitive to properties of the material. The objective of this research was to develop an ultrasonic method that could be used to measure the properties of thin plastic polyvinylchloride films (PVC). The proposed method exploits two fundamental Lamb wave modes, A₀ and S₀, for measurement of a thin film thickness and Young’s modulus. The Young’s modulus is found from the measured phased velocity of the S₀ mode and the film thickness from the velocities of both A₀ and S₀ modes. By using the proposed semi-contactless measurement algorithm, the Young’s modulus and thickness of different thickness (150 µm and 200 µm) PVC films were measured. The uncertainty of thickness measurements of the thinner 150 µm PVC film is 2% and the thicker 200 µm PVC film is 3.9%.

The ultrasonic testing technique using Lamb waves is widely used for the non-destructive testing and evaluation of various structures. For air-coupled excitation and the reception of A₀ mode Lamb waves, leaky guided waves are usually exploited. However, at low frequencies (<100 kHz), the velocity of this mode in plastic and composite materials can become slower than the ultrasound velocity in air, and its propagation in films is accompanied only by an evanescent wave in air. To date, the information about the attenuation of the slow A₀ mode is very contradictory. Therefore, the objective of this investigation was the measurement of the attenuation of the slow A₀ mode in thin plastic films. The measurement of the attenuation of normal displacements of the film caused by a propagating slow A₀ mode is discussed. The normal displacements of the film at different distances from the source were measured by a laser interferometer. In order to reduce diffraction errors, the measurement method based on the excitation of cylindrical but not plane waves was proposed. The slow A₀ mode was excited in the polyvinylchloride film by a dry contact type ultrasonic transducer made of high-efficiency PMN-32%PT strip-like piezoelectric crystal. It was found that that the attenuation of the slow A₀ mode in PVC film at the frequency of 44 kHz is 2 dB/cm. The obtained results can be useful for the development of quality control methods for plastic films.