In order to meet the requirements of industrial-scale fixed beds and develop an excellent adsorbent for asphalt VOCs. Zeolite ceramsite containing binder was prepared and successfully applied to the inhibition of asphalt VOCs. The results showed that prepared zeolite ceramsite possessed a high degree of crystallinity, and its main crystal phase is zeolite. The micropores with a pore size of 0.88 nm dominated the pore size distribution of the material. The adsorption experiment of asphalt VOCs showed a lower VOCs adsorption effect of 8.72% at a small dosage of 5%, while at a large dosage of 50%, the adsorption effect of VOCs exceeded 45%. This might be caused by the quite small external specific surface area, which occupied only 8.3% of the total specific surface area, and the low intraparticle diffusion coefficient due to the micropores. Meanwhile, the kinetics diameters of most aromatic hydrocarbons, which were comparable to the pore size of micropores, and the increase in the intraparticle diffusion resistance of aliphatic hydrocarbon molecules were the important factors in obtaining high adsorption of aromatic hydrocarbons in asphalt VOCs. Furthermore, the results indicated that the particulate adsorbent with a microporous structure should be mixed into the asphalt as a fine aggregate rather than an asphalt modifier for better asphalt VOCs adsorption effect.

The massive stockpiling of electrolytic manganese residue (EMR) has caused serious environmental pollution. In this study, EMR, coal gangue (CG), and fly ash (FA) were used as raw materials to obtain the optimal mix ratio based on Design-Expert mixture design. The effects of activator modulus, liquid–solid (L/S) ratio, and curing temperature on the mechanical properties of geopolymers were investigated. The results showed that the compressive strength of the prepared geopolymer was 12.0 MPa, and the 28d leaching of Mn was 0.123 mg/L under the conditions of EMR:CG:FA = 0.43:0.34:0.23, L/S = 0.9, a curing temperature of 60 °C, and a curing time of 24 h. This indicates that the geopolymer is an environmentally friendly material with high compressive strength. The mineral composition of the geopolymer is mainly hydrated calcium silicate and geopolymer gel. In addition, a more stable new mineral phase, MnSiO₃, was generated. The Fourier transform infrared (FTIR) spectrogram showed that the peak at 1100 m⁻¹ was shifted to 1112 cm⁻¹, which indicated that a geopolymerization reaction had occurred. Through scanning electron microscopy (SEM) and energy dispersive spectrum (EDS) analysis, it was identified that the geopolymerization produced a large amount of amorphous gelatinous substances with a relatively dense structure, the major elements being oxygen, silicon, aluminum, calcium, and sodium.

Realizing the utilization of reclaimed asphalt binder (RAB) and rice husk (RH) to reduce environmental pollution and expand the reutilization technique of reclaimed asphalt pavement (RAP), co-pyrolysis of RAB with RH has great potential. In this study, the co-pyrolysis behaviors, gaseous products, and kinetics were evaluated using thermogravimetric analysis and Fourier transform infrared spectroscopy (TG-FTIR). The results showed that incorporating RH into RAB improved its pyrolysis characteristics. The interactions between RAB and RH showed initial inhibition followed by subsequent promotion. The primary gaseous products formed during co-pyrolysis were aliphatic hydrocarbons, water, and carbon dioxide, along with smaller amounts of aldehydes and alcohols originating from RH pyrolysis. All average activation energy values for the blends, determined through iso-conversional methods, decreased with RH addition. The combined kinetic analysis revealed two distinct mechanisms: (1) at the lower conversion range, the pyrolysis of the blend followed a random nucleation and three-dimensional growth mechanism, while (2) at the higher conversion range, the control mechanism transitioned into three-dimensional diffusion.