The effect of electroslag remelting (ESR) with CaF₂-based synthetic slag on the microstructure and mechanical properties of three as-quenched martensitic/martensitic-bainitic ultrahigh-strength steels with tensile strengths in the range of 1250–2000 MPa was investigated. Ingots were produced both without ESR, using induction furnace melting and casting, and with subsequent ESR. The cast ingots were forged at temperatures between 1100 and 950 °C and air cooled. Final microstructures were investigated using laser scanning confocal microscopy, field emission scanning electron microscopy, electron backscatter diffraction, electron probe microanalysis, X-ray diffraction, color etching, and micro-hardness measurements. Mechanical properties were investigated through measurement of hardness, tensile properties and Charpy-V impact toughness. The microstructures of the investigated steels were mainly auto-tempered martensite in addition to small fractions of retained austenite and bainite. Due to the consequences of subtle modifications in chemical composition, ESR had a considerable impact on the final microstructural features: Prior austenite grain, effective martensite grain, and lath sizes were refined by up to 52%, 38%, and 28%, respectively. Moreover, the 95th percentiles in the cumulative size distribution of the precipitates decreased by up to 18%. However, ESR had little, if any, the effect on microsegregation. The variable effects of ESR on mechanical properties and how they depend on the initial steel composition are discussed.

This study provides a thorough analysis of the fatigue resistance of two low-alloy ultrahigh-strength steels (UHSSs): Steel A (fully martensitic) and Steel B (martensitic–bainitic). The investigation focused on the fatigue behaviour, damage mechanisms, and failure modes across different microstructures. Fatigue strength was determined through fully reversed tension–compression stress-controlled fatigue tests. Microstructural evolution, fracture surface characteristics, and crack-initiation mechanisms were investigated using laser scanning confocal microscopy and scanning electron microscopy. Microindentation hardness (H_IT) tests were conducted to examine the cyclic hardening and softening of the steels. The experimental results revealed that Steel A exhibited superior fatigue resistance compared to Steel B, with fatigue limits of 550 and 500 MPa, respectively. Fracture surface analysis identified non-metallic inclusions (NMIs) comprising the complex MnO-SiO₂ as critical sites for crack initiation during cyclic loading in both steels. The H_IT results after fatigue indicated significant cyclic softening for Steel A, with H_IT values decreasing from 7.7 ± 0.36 to 5.66 ± 0.26 GPa. In contrast, Steel B exhibited slight cyclic hardening, with H_IT values increasing from 5.24 ± 0.23 to 5.41 ± 0.31 GPa. Furthermore, the martensitic steel demonstrated superior yield and tensile strengths of 1145 and 1870 MPa, respectively. Analysis of the fatigue behaviour revealed the superior fatigue resistance of martensitic steel. The complex morphology and shape of the NMIs, examined using the 3D microstructure characterisation technique, demonstrated their role as stress concentrators, leading to localised plastic deformation and crack initiation.