The influence of cooling rate on the microstructure and mechanical properties of two new ultrahigh-strength steels (UHSSs) with different levels of C, Cr and Ni has been evaluated for the as-cooled and untempered condition. One UHSS had higher contents of C and Cr, while the other one had a higher Ni content. On the basis of dilatation curves, microstructures, macrohardness and microhardness, continuous cooling transformation diagrams were constructed as a guide to heat treatment possibilities. Cooling rates (CRs) of 60, 1 and 0.01 °C/s were selected for more detailed investigations. Microstructural characterization was made by laser scanning confocal microscopy, field emission scanning electron microscopy combined with electron backscatter diffraction, electron probe microanalysis and X-ray diffraction. Mechanical properties were characterized using macrohardness, tensile and Charpy V-notch impact tests. UHSS with the higher C and Cr contents showed lower transformation temperatures and slower bainite formation kinetics than that with the higher Ni content. Higher cooling rates led to lower volume fractions and carbon contents of retained austenite together with finer prior austenite grain size, as well as effective final grain size and lath size. These changes were accompanied by higher yield and tensile strengths. The best combinations of strength and toughness were obtained with martensitic microstructures and by avoiding the formation of granular bainite accompanied by proeutectoid carbides at low CR. For the cooling rates studied, UHSS with the higher C and Cr contents showed the higher hardness and strength but at the cost of toughness.

The effect of chromium content in the range of 1 wt.%–4 wt.% on the microstructure and mechanical properties of controlled-rolled and direct-quenched 12 mm thick low-carbon (0.04 wt.%) steel plates containing 0.06 wt.% Nb has been studied. In these microalloyed 700 MPa grade steels, the aim was to achieve a robust bainitic microstructure with a yield strength of 700 MPa combined with good tensile ductility and impact toughness. Continuous cooling transformation diagrams of deformed and non-deformed austenite were recorded to study the effect of Cr and hot deformation on the transformation behavior of the investigated steels. Depending on the cooling rate, the microstructures consist of one or more of the following microstructural constituents: bainitic ferrite, granular bainite, polygonal ferrite, and pearlite. The fraction of bainitic ferrite decreases with decreasing cooling rate, giving an increasing fraction of granular bainite and polygonal ferrite and a reduction in the hardness of the transformation products. Polygonal ferrite formation depends mainly on the Cr content and the cooling rate. In both deformed and non-deformed austenite, increasing the Cr content enhances the hardenability and refines the final microstructure, shifting the ferrite start curve to lower cooling rates. Preceding austenite deformation promotes the formation of polygonal ferrite at lower cooling rates, which leads to a decrease in hardness. In hot-rolled and direct-quenched plates, decreasing the Cr content promotes the formation of polygonal ferrite leading to an increase in the impact toughness and elongation but also a loss of yield strength.

In this study, ultra-high-strength steels, namely, cold-hardened austenitic stainless steel AISI 301 and martensitic abrasion-resistant steel AR600, as base metals (BMs) were butt-welded using a disk laser to evaluate the microstructure, mechanical properties, and effect of post-weld heat treatment (PWHT) at 250 °C of the dissimilar joints. The welding processes were conducted at different energy inputs (EIs; 50–320 J/mm). The microstructural evolution of the fusion zones (FZ) in the welded joints was examined using electron backscattering diffraction (EBSD) and laser scanning confocal microscopy. The hardness profiles across the weldments and tensile properties of the as-welded joints and the corresponding PWHT joints were measured using a microhardness tester and universal material testing equipment. The EBSD results showed that the microstructures of the welded joints were relatively similar since the microstructure of the FZ was composed of a lath martensite matrix with a small fraction of austenite. The welded structure exhibited significantly higher microhardness at the lower EIs of 50 and 100 J/mm (640 HV). However, tempered martensite was promoted at the high EI of 320 J/mm, significantly reducing the hardness of the FZ to 520 HV. The mechanical tensile properties were considerably affected by the EI of the as-welded joints. Moreover, the PWHT enhanced the tensile properties by increasing the deformation capacity due to promoting the tempered martensite in the FZ.

In this work, 2 mm thick medium-Mn austenitic stainless steel (MMn–SS) plates were joined with austenitic NiCr stainless steel (NiCr–SS) and low-carbon steel (LCS) using the gas tungsten arc welding technique. A precise adjustment of the welding process parameters was conducted to achieve high-quality dissimilar joints of MMn–SS with NiCr–SS and LCS. The microstructural evolution was studied using laser scanning confocal and electron microscopes. Secondary electron imaging and electron backscatter diffraction (EBSD) techniques were intensively employed to analyze the fine features of the weld structures. The mechanical properties of the joints were evaluated by uniaxial tensile tests and micro-indentation hardness (H_IT). The microstructure of the fusion zone (FZ) in the MMn–SS joints exhibited an austenitic matrix with a small fraction of δ-ferrite, ~6%. The tensile strength (TS) of the MMn–SS/NiCr–SS joint is significantly higher than that of the MMn–SS/LCS joint. For instance, the TSs of MMn–SS joints with NiCr–SS and LCS are 610 and 340 MPa, respectively. The tensile properties of MMn–SS/LCS joints are similar to those of BM LCS, since the deformation behavior and shape of the tensile flow curve for that joint are comparable with the flow curve of LCS. The H_IT measurements show that the MMn–SS/NiCr–SS joint is significantly stronger than the MMn–SS/LCS joint since the H_IT values are 2.18 and 1.85 GPa, respectively.