Carbon fiber significantly enhances the mechanical, thermal and electrical properties of rubber composites, which are widely used in aerospace, military, national defense and other cutting-edge fields. The preparation of a high-performance carbon fiber rubber composite has been a research hotspot, because the surface of carbon fiber is smooth, reactive inert and has a poor adhesion with rubber. In this paper, a high-performance rubber composite is prepared by mixing dopamine-modified staple carbon fiber with natural latex, and the mechanisms of modified carbon fiber-reinforced natural latex composite are explored. The experimental results show that the surface-modified staple carbon fiber forms uniform and widely covered polydopamine coatings, which significantly improve the interface adhesion between the carbon fiber and the rubber matrix. Meanwhile, when the concentration of dopamine is 1.5 g/L and the staple carbon fiber is modified for 6h, the carbon fiber rubber composite shows excellent conductivity, thermal conductivity, and dynamic mechanical properties, and its tensile strength is 10.6% higher than that of the unmodified sample.

Short fiber reinforced rubber composites have been widely used in rubber products attributed to their excellent wear resistance. However, there are still some serious problems in the processing of short fiber reinforced rubber composites, such as Mooney viscosity increasing, temperature and extrusion pressure rising, and unstable extrusion quality. In particular, short fibers need to be extruded in a specific direction during the molding process, and the problems in this process are particularly prominent. In this manuscript, the influence of gear pump assisted extrusion on the properties of short fiber rubber composites is studied. The experimental results show that the application of a gear pump to assist extrusion could significantly increase the die pressure, reduce the extrusion temperature of the blend, and improve the extrusion efficiency and stability of the blend. Furthermore, it could improve the vulcanization efficiency, increase the tensile strength and tear strength of the compound, reduce wear, and guarantee the quality of extrusion products.

Spent Fluid Catalytic Cracking (FCC) Catalyst is a major waste in the field of the petroleum processing field, with a large output and serious pollution. The treatment cost of these waste catalysts is high, and how to achieve their efficient reuse has become a key topic of research at home and abroad. To this end, this paper conducted a mechanistic and experimental study on the replacement of some carbon blacks by spent FCC catalysts for the preparation of rubber products and explored the synergistic reinforcing effect of spent catalysts and carbon blacks, in order to extend the reuse methods of spent catalysts and reduce the pollution caused by them to the environment. The experimental results demonstrated that the filler dispersion and distribution in the compound are more uniform after replacing the carbon black with modified spent FCC catalysts. The crosslinking density of rubber increases, the Payne effect is decreased, and the dynamic mechanical properties and aging resistance are improved. When the number of replacement parts reached 15, the comprehensive performance of the rubber composites remained the same as that of the control group. In this paper, the spent FCC catalysts modified by the physical method instead of the carbon-black-filled SBR can not only improve the performance of rubber products, but also can provide basic technical and theoretical support to realize the recycling of spent FCC catalysts and reduce the environmental pressure. The feasibility of preparing rubber composites by spent catalysts is also verified.