In the current research, a porous silicon/zinc oxide (PSi/ZnO) nanocomposite produced by a combination of metal-assisted chemical etching (MACE) and atomic layer deposition (ALD) methods is presented. The applicability of the composite for biophotonics (optical biosensing) was investigated. To characterize the structural and optical properties of the produced PSi/ZnO nanocomposites, several studies were performed: scanning and transmission electron microscopy (SEM/TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), diffuse reflectance, and photoluminescence (PL). It was found that the ALD ZnO layer fully covers the PSi, and it possesses a polycrystalline wurtzite structure. The effect of the number of ALD cycles and the type of Si doping on the optical properties of nanocomposites was determined. PL measurements showed a “shoulder-shape” emission in the visible range. The mechanisms of the observed PL were discussed. It was demonstrated that the improved PL performance of the PSi/ZnO nanocomposites could be used for implementation in optical biosensor applications. Furthermore, the produced PSi/ZnO nanocomposite was tested for optical/PL biosensing towards mycotoxins (Aflatoxin B1) detection, confirming the applicability of the nanocomposites.

The unique combination of optical, chemical, and structural properties of one-dimensional zinc oxide (1D ZnO) makes it one of the most attractive materials in a wide range of research and applications. In the present study, 1D ZnO nanomaterials were fabricated using a combination of two independent methods: electrospinning and atomic layer deposition (ALD). The electrospinning technique was used to produce 1D electrospun fibers consisting of four types of polymers: polylactic acid (PLLA), polyvinylidene fluoride (PVDF), polyvinyl alcohol (PVA), and polyamide 6 (PA6). The ALD technology, in turn, was selected as an excellent candidate for the synthesis of a ZnO thin layer over polymer fibers for the production of 1D ZnO/polymer nanofiber composites (PLLA/ZnO, PVDF/ZnO, PVA/ZnO, PA6/ZnO). Structural and optical properties of the produced nanofibers were studied by means of scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), diffuse reflectance, and photoluminescence (PL) spectroscopy. It was found that only PVDF/ZnO nanofibers exhibit stable room temperature PL that may be the result of a higher ZnO content in the sample. In addition, PL measurements were conducted as a function of excitation power and temperature in order to establish the main PL mechanisms and parameters for the PVDF/ZnO sample, as a most promising candidate for the biophotonic application.

¹H and ¹⁹F spin-lattice relaxation experiments have been performed for a series of ionic liquids sharing the same anion: bis(trifluoromethanesulfonyl)imide but including cations of different alkyl chain lengths: butyltriethylammonium, triethyloctylammonium, dodecyltriethylammo-nium and hexadecyltriethylammonium. The studies have been carried out in the temperature range from 383 to 108 K at the resonance frequency of 200 MHz (for ¹H). A quantitative analysis of the relaxation data has revealed two dynamical processes for both kinds of ions. The dynamics have been successfully modeled in terms of the Arrhenius law. The timescales of the dynamical processes and their temperature evolution have been discussed in detail, depending on the structure of the cation.

Traditional consolidants commonly used for waterlogged wood conservation often present long-term drawbacks, prompting research into new and reliable alternatives. Reducing reliance on fossil-based chemicals that are harmful to people, the environment, and the climate is a growing trend, and sustainable materials are now being explored as alternative consolidants for conserving waterlogged archaeological wood. Among these bio-based products, sodium alginate, a natural polysaccharide, has shown promising potential. This study aimed to evaluate its effectiveness in stabilising dimensions of severely degraded archaeological elm wood during drying. Various treatments were tested, and dimensional stabilisation (ASE), weight percent gain (WPG), and volumetric shrinkage (Vs) were assessed. Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) were used to evaluate alginate penetration and interactions with residual wood components. Results indicated that the effectiveness of sodium alginate depends on the treatment method, with the soaking approach and slow drying providing the highest WPG and the best stabilisation without altering the natural wood colour. Although the best achieved anti-shrink efficiency of 40% is insufficient from the conservation perspective, sodium alginate has proven to be a promising consolidant for the conservation of waterlogged wood. Further studies will focus on enhancing its penetration and interactions with residual wood components.

The cobalt phthalocyanine (CoPc) thin films (300 nm thick) deposited on n-type silicon substrate have been studied using micro-Raman spectroscopy, atomic force spectroscopy (AFM) and I-V measurement. The CoPc thin layers have been deposited at room temperature by the quasi-molecular beam evaporation technique. The micro-Raman spectra of CoPc thin films have been recorded in the spectral range of 1000 cm-1 to 1900 cm-1 using 488 nm excitation wavelength. Moreover, using surface Raman mapping it was possible to obtain information about polymorphic forms distribution (before and after annealing) of metallophthalocyanine (α and β form) from polarized Raman spectra. The I-V characteristics of the Au/CoPc/n-Si/Al Schottky barrier were also investigated. The obtained results showed that influence of the annealing process plays a crucial role in the ordering and electrical conductivity of the molecular structure of CoPc thin films deposited on n-type silicon substrate