If a lubricant contains structures capable of conducting energy, reactions involving zinc dialkyldithiophosphate (ZDDP) may take place both very close to and away from the solid surfaces, with this indicating that ZDDP can be a highly effective anti-wear (AW) additive. The central thesis of this article is that the tribocatalytic effect is observed only when the energy emitted by the solids is transmitted by ordered molecular structures present in the lubricant, e.g., graphene. The friction tests were carried out for 100Cr6 steel balls in a sliding contact with uncoated or W-DLC-coated HS6-5-2C steel discs in the presence of polyalphaolefin 8 (PAO 8) as the lubricant, which was enhanced with graphene and/or ZDDP. There is sufficient evidence of the interactions occurring between ZDDP and graphene and their effects on the tribological performance of the system. It was also found that the higher the concentration of zinc in the wear area, the lower the wear. This was probably due to the energy transfer resulting from the catalytic decomposition of ZDDP molecules. Graphene, playing the role of the catalyst, contributed to that energy transfer.

This article explores the properties of composite materials employed in dental fillings. A traditional nano-hybrid composite containing nanofiller particles exceeding 82% by weight served as a benchmark. The remaining samples were fabricated from ormocer resin, maintaining an identical nanofiller content of 84%. In all specimens, the nanoparticles were dispersed randomly within the matrix. This study presents findings from investigations into surface geometry, hardness, wettability, and tribological behavior. The microscopic observations revealed that ormocer-based samples exhibited greater surface roughness than those composed of the traditional composite. Hardness testing indicated that both ceramic addition and sample preparation significantly influenced mechanical properties. Ceramic-enhanced samples demonstrated superior hardness, surpassing the reference composite by 30% and 43%, respectively. Contact angle measurements revealed hydrophilic characteristics in the classic composite, contrasting with the hydrophobic nature of ceramic-containing samples. Tribological evaluations revealed the superiority of the classic composite in terms of friction coefficients and volumetric wear compared to ormocer-based materials.

The data from the authors’ earlier investigations show that molecules of zinc dithiophosphate (ZDDP) added to a lubricant can absorb energy emitted by a solid surface, which is where triboreactions occur. If the lubricant contains structures able to conduct energy, the ZDDP reactions can occur even at a relatively large distance from the solid surface, which should increase the effectiveness of ZDDP as an antiwear additive. The purpose of this paper was to verify the thesis that the tribocatalytic effect depends on the ability of the solid surface to emit electrons/energy and the ability of ordered molecular structures, such as carbon nanotubes (CNTs), to conduct energy and, most likely, to enhance the energy transfer. The tribological tests were performed using a TRB³ tribotester for 100Cr6 steel balls and uncoated or a-C:H coated HS6-5-2C steel discs. Polyalphaolefin 8 (PAO8) and PAO8 mixed with ZDDP and CNTs were used as lubricants. The results of the tribological tests suggested that: (a) the effect of the interactions between ZDDP and CNTs was clearly visible; (b) the structure and properties of the solid surface layer had a significant influence on the antiwear action of the ZDDP additive.

Clinical trials conducted in many centres worldwide indicate that, despite advances made in the use of biomaterials for medical applications, tribocorrosive wear remains a significant issue. The release of wear residue into body fluids can cause inflammation and, as a result, implant failure. Surface modification is one of the methods used to improve the mechanical, tribological, and fatigue properties of biomaterials. In this article, the authors investigated the impact of ion implantation on improving the functional properties of implant surfaces. This paper presents morphology, geometric surface structure, hardness, and tribological test results for layers obtained by ion implantation with nitrogen and oxygen ions on alloy 316L. The surface morphology and thickness of the implanted layer were examined using scanning microscopy. Atomic force microscopy was used to evaluate the geometric structure of the surface. Instrumented indentation was used to measure nanohardness. Model tribo tests were carried out for reciprocating motion under conditions of dry friction and lubricated friction with Ringer’s solution. The tribological tests showed that the implanted samples had a lower wear than the reference samples. Nitrogen ion implantation increased the hardness of 316L steel by about 45% and increased it by about 15% when oxygen ions were used.

In this paper, the authors investigated the impact of DLC coatings doped with tungsten (a-C:H:W) coatings obtained using plasma-assisted physical vapor deposition (PVD) on the properties of the 100Cr6 steel. The results of the 100Cr6 steel specimens with and without the coating were compared. Scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysis were used to observe the morphology of the coating surfaces and cross-sections and identify the elements in the coating composition. The contact angle of the investigated surfaces was measured with a tensiometer. Additionally, the effect of the coatings on the tribological properties of lubricated friction pairs was evaluated. Friction tests were performed on a ball-on-disc tribometer under lubrication with cutting fluid. The surface texture of the samples before and after the tribological tests was measured using a confocal profilometer. The results obtained from the tests and analysis allow for the conclusion that the use of DLC coatings a-C:H:W increases the hardness of 100Cr6 steel by three times. The values of the contact angles were indicative of surface hydrophilic characteristics. The tungsten-doped diamond-like coating under friction conditions reduced the coefficient of friction and wear. DLC coatings a-C:H:W lubricated with the cutting fluid improve the mechanical and tribological properties of 100Cr6 steel sliding surfaces under friction.