Experimental studies reveal that the simultaneous addition of zinc dialkyl dithiophosphates (ZDDPs) and multi-wall carbon nanotubes (MWCNTs) to a poly-alpha-olefin base oil strongly reduces wear. In this paper, it is shown that MWCNTs promote the formation of an anti-wear (AW) layer on the metal surface that is much thicker than what ZDDPs can create as a sole additive. More importantly, the nanotubes’ action is indirect, i.e., MWCNTs neither mechanically nor structurally strengthen the AW film. A new mechanism for this effect is also proposed, which is supported by detailed tribometer results, friction track 3D-topography measurements, electron diffraction spectroscopy (EDS), and Raman spectroscopy. In this mechanism, MWCNTs mediate the transfer of both thermal and electric energy released on the metal surface in the friction process. As a result, this energy penetrates more deeply into the oil volume, thus extending the spatial range of tribochemical reactions involving ZDDPs.

If a lubricant contains structures capable of conducting energy, reactions involving zinc dialkyldithiophosphate (ZDDP) may take place both very close to and away from the solid surfaces, with this indicating that ZDDP can be a highly effective anti-wear (AW) additive. The central thesis of this article is that the tribocatalytic effect is observed only when the energy emitted by the solids is transmitted by ordered molecular structures present in the lubricant, e.g., graphene. The friction tests were carried out for 100Cr6 steel balls in a sliding contact with uncoated or W-DLC-coated HS6-5-2C steel discs in the presence of polyalphaolefin 8 (PAO 8) as the lubricant, which was enhanced with graphene and/or ZDDP. There is sufficient evidence of the interactions occurring between ZDDP and graphene and their effects on the tribological performance of the system. It was also found that the higher the concentration of zinc in the wear area, the lower the wear. This was probably due to the energy transfer resulting from the catalytic decomposition of ZDDP molecules. Graphene, playing the role of the catalyst, contributed to that energy transfer.

The data from the authors’ earlier investigations show that molecules of zinc dithiophosphate (ZDDP) added to a lubricant can absorb energy emitted by a solid surface, which is where triboreactions occur. If the lubricant contains structures able to conduct energy, the ZDDP reactions can occur even at a relatively large distance from the solid surface, which should increase the effectiveness of ZDDP as an antiwear additive. The purpose of this paper was to verify the thesis that the tribocatalytic effect depends on the ability of the solid surface to emit electrons/energy and the ability of ordered molecular structures, such as carbon nanotubes (CNTs), to conduct energy and, most likely, to enhance the energy transfer. The tribological tests were performed using a TRB³ tribotester for 100Cr6 steel balls and uncoated or a-C:H coated HS6-5-2C steel discs. Polyalphaolefin 8 (PAO8) and PAO8 mixed with ZDDP and CNTs were used as lubricants. The results of the tribological tests suggested that: (a) the effect of the interactions between ZDDP and CNTs was clearly visible; (b) the structure and properties of the solid surface layer had a significant influence on the antiwear action of the ZDDP additive.

This article concerns the issue of thermal degradation process of fuels, important from the perspective of the operation of turbine engines, especially in the context of new fuels/bio-fuels and their implementation. The studies of the kerosene-based jet fuel (Jet A-1) and its blends with synthetic components manufactured according to HEFA and ATJ technology, were presented. Both technologies are currently approved by ASTM D7566 to produce components to be added to turbine fuels. Test rig investigations were carried out according to specific methodology which reflects the phenomena taking place in fuel systems of turbine engines. The mechanism of thermal degradation process was assessed on the basis of test results for selected properties, IR spectroscopy and calculation of activation energy. The results show that with the increase of the applied temperature there is an increment of the content of solid contaminants, water and acid for all tested fuels. Thermal degradation process is different for conventional jet fuel when compared to blends, but also semi-synthetic fuels distinguished by different thermal stability depending on a given manufacturing technology.