This investigative study aims to study the mechanical and morphological properties of fly ash (FA)-based geopolymer paste as a repair material when applied on ordinary Portland cement (OPC) overlay concrete. The first part of this study investigates the optimal mix design of FA-based geopolymer paste with various NaOH concentrations of 8, 10, 12, and 14 M, which were used later as a repair material. The second part studies the bonding strength using a slant shear test between the geopolymer repair material and OPC substrate concrete. The results showed that a shorter setting time corresponds to the higher NaOH molarity, within the range of 53 and 30 min at 8 and 14 M, respectively. The compressive strength of FA-based geopolymer paste was found to reach 92.5 MPa at 60 days. Also, from the slant shear test results, prism specimens with 125 mm length and 50 mm wide have a large bond strength of 11 MPa at 12 M. The scanning electron microscopy/energy-dispersive X-ray (SEM/EDX) analysis showed that the OPC substrate has a significant effect on slant shear bond strength, where the presence of free cations of Ca²⁺ on the OPC substrate surface contributed to the formation of calcium alumina-silicate hydrate gel (C-A-S-H) by building various cross-links of Ca-O-Si.

Geopolymers produced by synthesizing aluminosilicate source materials with an alkaline activator solution promised an excellent properties akin to the existing construction material. This study focused on the effect of various binder to sand ratio on geopolymer mortar properties. Mix design of geopolymer mortar was produced using NaOH concentration of 12 molars, ratio of fly ash/alkaline activator and ratio Na 2 SiO 3 /NaOH of 2.0 and 2.5 respectively. Samples subsequently ware cured at ambient temperature. The properties of geopolymer mortar were analysed in term of compressive strength and density at different period which are on the 3 rd and 7 th day of curing. Experimental results revealed that the addition of sand slightly increase the compressive strength of geopolymer. The optimum compressive strength obtained was up to 31.39 MPa on the 7 th day. The density of geopolymer mortar was in the range between 2.0 g/cm 3 to 2.23 g/cm 3. Based on this findings, the special properties promoted by geopolymer mortar display high potential to be implemented in the field of concrete patch repair. 1.

In recent years, research and development of geopolymers has gained significant interest in the fields of repairs and restoration. This paper investigates the application of a geopolymer as a repair material by implementation of high-calcium fly ash (FA) as a main precursor, activated by a sodium hydroxide and sodium silicate solution. Three methods of concrete substrate surface preparation were cast and patched: as-cast against ordinary Portland cement concrete (OPCC), with drilled holes, wire-brushed, and left as-cast against the OPCC grade 30. This study indicated that FA-based geopolymer repair materials (GRMs) possessed very high bonding strength at early stages and that the behavior was not affected significantly by high surface treatment roughness. In addition, the investigations using scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) spectroscopy have revealed that the geopolymer repair material became chemically bonded to the OPC concrete substrate, due to the formation of a C–A–S–H gel. Fundamentally, the geopolymer network is composed of tetrahedral anions (SiO₄)⁴⁻ and (AlO₄)⁵⁻ sharing the oxygen, which requires positive ions such as Na⁺, K⁺, Li⁺, Ca²⁺, Na⁺, Ba²⁺, NH⁴⁺, and H₃O⁺. The availability of calcium hydroxide (Ca(OH)₂) at the surface of the OPCC substrate, which was rich in calcium ions (Ca²⁺), reacted with the geopolymer; this compensated the electron vacancies of the framework cavities at the bonding zone between the GRM and the OPCC substrate.

MATEC Web of Conferences, open access proceedings in Materials science, Engineering and Chemistry

Geopolymer possess many excellent properties such as high compressive and bond strength, long term durability, better acid resistance and also known as a "Sustainable Material" due to its low carbon emission and low energy consumption. Thus, it is a good opportunity to develop and explore not only for cement and concrete but also as geopolymeric repair materials. This reviews showed that good bonding properties between geopolymeric repair material and concrete substrate is important in order to acquire an enhanced resistance against penetration of harmful substances and avoiding respalling of the repair material by understanding the bonding behaviour. Bond strength depends to the properties of the repair materials itself and also the surface preparations of concrete substrate.