Aggregates can be categorized into natural and artificial aggregates. Preserving natural resources is crucial to ensuring the constant supply of natural aggregates. In order to preserve these natural resources, the production of artificial aggregates is beginning to gain the attention of researchers worldwide. One of the methods involves using geopolymer technology. On this basis, this current research focuses on the inter-particle effect on the properties of fly ash geopolymer aggregates with different molarities of sodium hydroxide (NaOH). The effects of synthesis parameters (6, 8, 10, 12, and 14 M) on the mechanical and microstructural properties of the fly ash geopolymer aggregate were studied. The fly ash geopolymer aggregate was palletized manually by using a hand to form a sphere-shaped aggregate where the ratio of NaOH/Na₂SiO₃ used was constant at 2.5. The results indicated that the NaOH molarity has a significant effect on the impact strength of a fly ash geopolymer aggregate. The highest aggregate impact value (AIV) was obtained for samples with 6 M NaOH molarity (26.95%), indicating the lowest strength among other molarities studied and the lowest density of 2150 kg/m³. The low concentration of sodium hydroxide in the alkali activator solution resulted in the dissolution of fly ash being limited; thus, the inter-particle volume cannot be fully filled by the precipitated gels.

As the demand for nonrenewable natural resources, such as aggregate, is increasing worldwide, new production of artificial aggregate should be developed. Artificial lightweight aggregate can bring advantages to the construction field due to its lower density, thus reducing the dead load applied to the structural elements. In addition, application of artificial lightweight aggregate in lightweight concrete will produce lower thermal conductivity. However, the production of artificial lightweight aggregate is still limited. Production of artificial lightweight aggregate incorporating waste materials or pozzolanic materials is advantageous and beneficial in terms of being environmentally friendly, as well as lowering carbon dioxide emissions. Moreover, additives, such as geopolymer, have been introduced as one of the alternative construction materials that have been proven to have excellent properties. Thus, this paper will review the production of artificial lightweight aggregate through various methods, including sintering, cold bonding, and autoclaving. The significant properties of artificial lightweight aggregate, including physical and mechanical properties, such as water absorption, crushing strength, and impact value, are reviewed. The properties of concrete, including thermal properties, that utilized artificial lightweight aggregate were also briefly reviewed to highlight the advantages of artificial lightweight aggregate.

This investigative study aims to study the mechanical and morphological properties of fly ash (FA)-based geopolymer paste as a repair material when applied on ordinary Portland cement (OPC) overlay concrete. The first part of this study investigates the optimal mix design of FA-based geopolymer paste with various NaOH concentrations of 8, 10, 12, and 14 M, which were used later as a repair material. The second part studies the bonding strength using a slant shear test between the geopolymer repair material and OPC substrate concrete. The results showed that a shorter setting time corresponds to the higher NaOH molarity, within the range of 53 and 30 min at 8 and 14 M, respectively. The compressive strength of FA-based geopolymer paste was found to reach 92.5 MPa at 60 days. Also, from the slant shear test results, prism specimens with 125 mm length and 50 mm wide have a large bond strength of 11 MPa at 12 M. The scanning electron microscopy/energy-dispersive X-ray (SEM/EDX) analysis showed that the OPC substrate has a significant effect on slant shear bond strength, where the presence of free cations of Ca²⁺ on the OPC substrate surface contributed to the formation of calcium alumina-silicate hydrate gel (C-A-S-H) by building various cross-links of Ca-O-Si.