This work presents results in the field of synthesis of new metal matrix composites with matrix NiTi and particles TiB₂, and their use as additives to fabricate metal matrix composites based on the Inconel 625 alloy. NiTi-TB₂ powders were obtained using self-propagating high-temperature synthesis. Composite NiTi-TiB₂ particles were spheroidized on a high-frequency induction plasmatron. Composite NiTi-TB₂ particles were mixed with metallic Inconel 625 powder with particle sizes of 50–150 µm. We used direct laser deposition by means of mixture of powders to grow samples with different contents of ceramics in the metal matrix. The process of direct laser deposition during the experiment was investigated. We have determined the peculiarities of the formation of the structure in metal matrix composites with different contents of titanium diboride. We have demonstrated the possibility of using Direct Laser Deposition (DLD) for fabricating items from ceramic metal materials. We have determined promising fields of further research for the purpose of obtaining efficient metal matrix composites using additive manufacturing technologies.

The results disclosed that both the microstructure and mechanical properties of AA7075-T6 laser welds are considerably influenced by the heat input. In comparison with high heat input (arc welding), a smaller weld fusion zone with a finer dendrite arm spacing, limited loss of alloying elements, less intergranular segregation, and reduced residual tensile stress was obtained using low heat input. This resulted in a lower tendency of porosity and hot cracking, which improved the welded metal’s soundness. Subsequently, higher hardness as well as higher tensile strength for the welded joint was obtained with lower heat input. A welded joint with better mechanical properties and less mechanical discrepancy is important for better productivity. The implemented high-power fiber laser has enabled the production of a low heat input welded joint using a high welding speed, which is of considerable importance for minimizing not only the fusion zone size but also the deterioration of its properties. In other words, high-power fiber laser welding is a viable solution for recovering the mechanical properties of the high-strength AA 7075-T6 welds. These results are encouraging to build upon for further improvement of the mechanical properties to be comparable with the base metal.

Additive manufacturing of titanium alloys is one of the fastest growing areas of 3D metal printing. The use of AM methods for parts production in the aviation industry is especially promising. During the deposition of products with differently sized cross-sections, the thermal history changes, which leads to non-uniformity of the structure and properties. Such heterogeneity can lead to failure of the product during operation. The structure of deposited parts, depending on the thermal cycle, may consist of α’, α + α’ + β’, and α + β in different ratios. This problem can be solved by using heat treatment (HT). This paper presents research aimed towards the determination of optimal heat treatment parameters that allows the reception of the uniform formation of properties in the after-treatment state, regardless of the initial structure and properties, using the example of a deposited Ti-6Al-4V gas turbine blade.

In this work, the critical fracture stresses during spalling of high-strength steel 09CrNi2MoCu samples obtained by direct laser deposition (DLD) were measured under shock compression of up to ~5.5 GPa. The microstructure and mechanical properties of DLD steel samples in the initial state and after heat treatment were studied and compared to traditional hot rolled one. The microstructural features of steel before and after heat treatment were revealed. The heat treatment modes of the deposit specimens on their strength properties under both static and dynamic loads have been investigated. The spall strength of the deposited specimens is somewhat lower than the strength of steel specimens after hot rolling regardless of their heat treatment. The minimum elastic limit of elasticity is exhibited by the deposit specimens. After heat treatment of the deposit samples, the elastic limit increases and approximately doubles. Subsequent heat treatment in the form of hardening and tempering allows obtaining strength properties under Hugoniot loads in traditional hot-rolled products.

The work is devoted to the development of a model for calculating transient quasiperiodic temperature fields arising in the direct deposition process of thin walls with various configurations. The model allows calculating the temperature field, thermal cycles, temperature gradients, and the cooling rate in the wall during the direct deposition process at any time. The temperature field in the deposited wall is determined based on the analytical solution of the non-stationary heat conduction equation for a moving heat source, taking into account heat transfer to the environment. Heat accumulation and temperature change are calculated based on the superposition principle of transient temperature fields resulting from the heat source action at each pass. The proposed method for calculating temperature fields describes the heat-transfer process and heat accumulation in the wall with satisfactory accuracy. This was confirmed by comparisons with experimental thermocouple data. It takes into account the size of the wall and the substrate, the change in power from layer to layer, the pause time between passes, and the heat-source trajectory. In addition, this calculation method is easy to adapt to various additive manufacturing processes that use both laser and arc heat sources.

In test research, the technology of the blades growing on the disk part of the titanium compressor wheel by heterophase laser powder metallurgy was applied. The experiments were carried out to select the optimal modes of the process, ensuring the absence of defects in the form of pores, non-melting, cracks. The influence of granulometric composition on mechanical characteristics was also investigated. The optimal modes of the additive technological process, providing the formation of a defect-free structure and optimal mechanical properties of the blanks are found as a result of the experiments. The samples of titanium powder alloy Ti6Al4V and hybrid samples consisting of cast and powder materials were produced with the help of technology mention above. Tests of the grown and hybrid samples were carried out to determine the mechanical properties. Studies of micro and macrostructure of the samples were produced. Calculations of the stress-strain state and dynamic characteristics for the initial and hybrid glare using the found mechanical properties were carried out. Preparing testing hybrid titanium wheel carries out now. This technology also can be used for repairs of blisks blades.