Nowadays, the hybridization of natural and glass fiber has promised several advantages as a green composite. Nevertheless, their different characteristics lead to poor mechanical bonding. In this work, agel fiber and glass fiber was used as reinforcements, and activated carbon filler was added to the polymer matrix of a hybrid composite to modify its characteristics and mechanical properties. A tensile and bending test was conducted to evaluate the effect of three different weight percentages of activated carbon filler (1, 2, and 4 wt%). Vacuum-assisted resin infusion was used to manufacture the hybrid composite to obtain the high-quality composite. The results have revealed that adding 1 wt% filler yielded the most optimum result with the highest tensile strength, flexural strength, and elastic modulus, respectively: 112.90 MPa, 85.26 MPa, and 1.80 GPa. A higher weight percentage of activated carbon filler on the composite reduced its mechanical properties. The lowest test value was shown by the composite with 4 wt%. The micrograph observations have proven that the 4 wt% composite formed agglomeration filler that can induce stress concentration and reduce its mechanical performance. Adding 1 wt% filler offered the best dispersion in the matrix, which can enhance better load transfer capability.

This work presents results in the field of synthesis of new metal matrix composites with matrix NiTi and particles TiB₂, and their use as additives to fabricate metal matrix composites based on the Inconel 625 alloy. NiTi-TB₂ powders were obtained using self-propagating high-temperature synthesis. Composite NiTi-TiB₂ particles were spheroidized on a high-frequency induction plasmatron. Composite NiTi-TB₂ particles were mixed with metallic Inconel 625 powder with particle sizes of 50–150 µm. We used direct laser deposition by means of mixture of powders to grow samples with different contents of ceramics in the metal matrix. The process of direct laser deposition during the experiment was investigated. We have determined the peculiarities of the formation of the structure in metal matrix composites with different contents of titanium diboride. We have demonstrated the possibility of using Direct Laser Deposition (DLD) for fabricating items from ceramic metal materials. We have determined promising fields of further research for the purpose of obtaining efficient metal matrix composites using additive manufacturing technologies.

In this work, the critical fracture stresses during spalling of high-strength steel 09CrNi2MoCu samples obtained by direct laser deposition (DLD) were measured under shock compression of up to ~5.5 GPa. The microstructure and mechanical properties of DLD steel samples in the initial state and after heat treatment were studied and compared to traditional hot rolled one. The microstructural features of steel before and after heat treatment were revealed. The heat treatment modes of the deposit specimens on their strength properties under both static and dynamic loads have been investigated. The spall strength of the deposited specimens is somewhat lower than the strength of steel specimens after hot rolling regardless of their heat treatment. The minimum elastic limit of elasticity is exhibited by the deposit specimens. After heat treatment of the deposit samples, the elastic limit increases and approximately doubles. Subsequent heat treatment in the form of hardening and tempering allows obtaining strength properties under Hugoniot loads in traditional hot-rolled products.

There is the influence of high temperatures and internal stresses, defects accumulate, which lead to the formation of microcracks of various types, wear and subsequent destruction of the blade during their exploitation. In view of the complexity in the manufacture and high cost of new blades, after the development of their resource, the blades should be restored. This paper shows applying investigation which was directed to make a technological recommendations for restoration cladding of turbine blades. The influence of initial material characteristics and main technological parameters of cladding process on formation of geometry, structure and potential defects of deposited metal is considered. Based on obtained dependencies, criteria that allow producing a defect-free clad with controlled structure and a minimized allowance for further machining are determined. As result of investigation, laser powder cladding technology for restoration of heat-resistant nickel alloys turbine blades is developed.

Modern methods and technologies for the creation and processing of materials provide great opportunities for research. This work is devoted to the study of the causes of hot cracks, as well as the application of an analytical method for assessing the occurrence of hot cracks in high-temperature nickel alloys ZhS32, ZhS6U, ZhS6K, Rene 80, Rene 41, processed by laser powder cladding. In the course of the work, the process of the influence of a heat source on samples was modeled, an analysis of thermal fields and isotherms was performed, on the basis of which an analytical method was developed for finding the criterion for the pressure drop along the crystallization front in different modes and grades of alloys, to assess the tendency to form hot cracks in high-temperature nickel alloys.

In this paper, we present the results of a study on droplet transferring with arc space short circuits during wire-arc additive manufacturing (WAAM GMAW). Experiments were conducted on cladding of single beads with variable welding current and voltage parameters. The obtained oscillograms and video recordings were analyzed in order to compare the time parameters of short circuit and arc burning, the average process peak current, as well as the droplets size. Following the experiments conducted, 2.5D objects were built-up to determine the influence of electrode stickout and welding torch travel speed to identify the droplet transferring and formation features. Moreover, the current–voltage characteristics of the arc were investigated with varying WAAM parameters. Process parameters have been determined that make it possible to increase the stability of the formation of the built-up walls, without the use of specialized equipment for forced droplet transfer. In the course of the research, the following conclusions were established: the most stable drop transfer occurs at an arc length of 1.1–1.2 mm, reverse polarity provides the best drop formation result, the stickout of the electrode wire affects the drop transfer process and the quality of the deposited layers. The dependence of the formation of beads on the number of short circuits per unit length is noted.