This work presents results in the field of synthesis of new metal matrix composites with matrix NiTi and particles TiB₂, and their use as additives to fabricate metal matrix composites based on the Inconel 625 alloy. NiTi-TB₂ powders were obtained using self-propagating high-temperature synthesis. Composite NiTi-TiB₂ particles were spheroidized on a high-frequency induction plasmatron. Composite NiTi-TB₂ particles were mixed with metallic Inconel 625 powder with particle sizes of 50–150 µm. We used direct laser deposition by means of mixture of powders to grow samples with different contents of ceramics in the metal matrix. The process of direct laser deposition during the experiment was investigated. We have determined the peculiarities of the formation of the structure in metal matrix composites with different contents of titanium diboride. We have demonstrated the possibility of using Direct Laser Deposition (DLD) for fabricating items from ceramic metal materials. We have determined promising fields of further research for the purpose of obtaining efficient metal matrix composites using additive manufacturing technologies.

The urgency of heat treatment of samples of maraging steel obtained by direct laser deposition from steel powder 06Cr15Ni4CuMo is considered. The structural features and properties of 06Cr15Ni4CuMo steel samples after direct laser deposition and heat treatment are studied. The work is devoted to research into the influence of thermal processing on the formation of structure and the mechanical properties of deposit samples. Features of formation of microstructural components by means of optical microscopy are investigated. Tests for tension and impact toughness are conducted. As a result, it was established that the material obtained by the direct laser deposition method in its initial state significantly exceeds the strength characteristics of heat treatment castings of similar chemical composition, but is inferior to it in terms of impact toughness and relative elongation. The increase in relative elongation and impact toughness up to the level of cast material in the deposit samples is achieved at the subsequent heat treatment, which leads to the formation of the structure of tempered martensite and reduction in its content at two-stage tempering in the structure of the metal. The strength of the material is also reduced to the level of cast metal.

Currently, metal–matrix composite materials are some of the most promising types of materials, and they combine the advantages of a metal matrix and reinforcing particles/fibres. Within the framework of this article, the high-temperature synthesis of metal–matrix composite materials based on the (Ni-Ti)-TiB2 system was studied. The selected approaches make it possible to obtain composite materials of various compositions without contamination and with a high degree of energy efficiency during production processes. Combustion processes in the samples of a 63.5 wt.% NiB + 36.5 wt.% Ti mixture and the phase composition and structure of the synthesis products were researched. It has been established that the synthesis process in the samples proceeds via the spin combustion mechanism. It has been shown that self-propagating high-temperature synthesis (SHS) powder particles have a composite structure and consist of a Ni-Ti matrix and TiB2 reinforcement inclusions that are uniformly distributed inside it. The inclusion size lies in the range between 0.1 and 4 µm, and the average particle size is 0.57 µm. The obtained metal-matrix composite materials can be used in additive manufacturing technologies as ligatures for heat-resistant alloys, as well as for the synthesis of composites using traditional methods of powder metallurgy.

This research work studies the structural phase parameters and physicomechanical properties of metal-matrix composite materials based on a Ni–TiB₂ system obtained by additive manufacturing (specifically, direct laser deposition). The properties of the composites obtained were investigated at high temperatures (up to 1000 °C). The feasibility of the fabrication of a composite nanostructure of alloy with advanced physicomechanical properties was shown. The introduction of reinforcing TiB₂ particles into an Inconel 625 matrix was confirmed to increase the microhardness and tensile strength of the material obtained. Apparently, the composite structure of the samples facilitates the realisation of several strengthening mechanisms: (1) a grain boundary mechanism that causes strengthening and dislocation movement; (2) a mechanism based on the grain structure breakdown and Hall–Petch relationship realisation.

The novelty of this work consists of obtaining original fundamental data on the laws of synthesis of new metal matrix composite materials for additive technologies. CrN + TiNi composites were obtained using the method of self-propagating high-temperature synthesis. In this work, analysis of the parameters of the synthesis of composite materials as well as their structure and phase composition were carried out. A scheme for the formation of a composite structure is established; it is shown that the phase composition is represented by 54.6 wt.% CrN and 45.4 wt.% TiNi. It was shown that composites based on the system are suitable for machines that make use of direct laser deposition to grow layers of materials. Sample structure and phase parameters were studied. It is shown that titanium nitride particles are uniformly distributed in the CrNi intermetallic matrix, the TiN particle size ranges from 0.3 to 9 μm and the average particle size is 2.8 μm. The results obtained indicate the possibility of synthesizing promising metal matrix composite materials for additive technologies. Such materials may have increased hardness, operating temperature and strength.

This paper presents the results of measurements of the spall strength and elastic-plastic proper-ties, under dynamic and static loads, of the high-strength heat-resistant nickel-chromium alloy Inconel 625, obtained by the direct laser deposition method. The structural parameters of the obtained samples and the mechanical properties during static tests were studied. According to our information, anisotropy in the structural parameters operates primarily at the level of plastic deformation of alloys. Shock compression of the additive alloy Inconel 625 samples in the range of 6–18 GPa was carried out using a light-gas gun, both along and perpendicular to the direction of the deposition. The strength characteristics were determined from the analysis of the shock wave profiles, which were recorded using the VISAR laser velocimeter during the loading of samples. It was found that the value of the spall strength of additive samples does not depend on the direction of deposition, and the Hugoniot elastic limit of samples loaded perpendicular to the deposition direction is about ~10% higher. With an increase in the maximum compression stress, the material’s spall strength increases slightly, but for both types of samples, a slight decrease in the Hugoniot elastic limit was observed as the compression stresses increase. On the basis of the measured wave profiles, shock Hugoniots of the samples of the alloy Inconel 625, loaded both along and perpendicular to the direction of deposition, are constructed in this pressure range.